Electronic and magnetic properties of LaV1-xO3 /

A series of LaVi^xOs compounds (x=0.00, 0.02, 0.04, 0.06, 0.08) were prepeired using the standard solid reaction. The samples were chareicterized by X-ray diffraction (XRD), fourprobe resistivity, smd magnetic susceptibility studies. Powder X-ray diffraction analysis indicated the formation of a single-phase sample with a orthorhombic structure which was first found in GdFeOs (space group Pnma) . The Unit Cell program was used for calculating lattice peirameters from XFID data. The XRD spectnim could be indexed on a cubic lattice with Og = 2ap ~ (7.8578 to 7.9414 A). The lattice parameter was observed to increase as the Vanadium vacancy increased. Four-probe resistivity measurements exhibited semiconductor behavior for all sajnples from room temperature down to 19K. The resistivity of samples increased with increasing Vanadium vacancy. The resistivity of samples demonstrated activated conduction with an activation energy of approximately 0.2 eV. The activation energy increased with increasing lattice parameter. Field cool magnetic susceptibility measurements were performed with field of 500 G from 300 K to 5 K. These measurements indicated the presence of an antiferromagnetic transition at about 140 K. The data was fitted above Neel temperature to Ciurie-Weiss law yielding a negative parameignetic Curie temperature. This implies that antiferromagnetic ordering is present.

Magnetic properties of the Biâ Srâ CaCuâ Oâ single crystal

The Bi2Sr2CaCu20g single crystal with a superconducting transition temperature equal to 90 ± 2 K was prepared. The irreversibility line of the single crystal for a mgnetic field direction along the c-axis and T* in the ab-plane was determined. The reduced temperature (l - T ) is proportional to H 1.1 for fields below 004 T and proportional to HO.09 for fields above 0.4 T. The zero temperature upper critical field Hc2(0) and coherence length ~ (0) were determined from the magnetization meaurements to be H-lC2=35.9T , H//C2=31.2T, ~c(0)=35.0 A, and ~ab(0)=32.5A,and from the magnetoresistance measurements to be H-lc2 = 134.6T , H//C2=55.5T '~c(0)=38.1 A, and ~ab(0)=2404 A for both directions of the applied magnetic field. The results obtained for Hc2(0) and ~(O) are not reliable due to the rounding that the single crystal exhibits in the magnetization and magnetoresistance curves. The magnetization relaxation of the single crystal was investigated, and was found to be logarithmic in time, and the relaxation rate increases with temperature up to 50 -60 K, then decreases at higher temperatures.