2 resultados para Chromium alloys.
em Brock University, Canada
Resumo:
A system comprised of a Bomem interferometer and a LT3-110 Heli-Tran cryostat was set up to measure the reflectance of materials in the mid-infrared spectral region. Several tests were conducted to ensure the consistency and reliability of the system. Silicon and Chromium, two materials with well known optical properties were measured to test the accuracy of the system, and the results were found to be in good agreement with the literature. Reflectance measurements on pure SnTe and several Pb and Mn-doped alloys were carried out. These materials were chosen because they exhibit a strong plasma edge in the mid infrared region. The optical conductivity and several related optical parameters were calculated from the measured reflectance. Very low temperature measurements were carried out in the far-infrared on Sn9SMn2Te, and the results are indicative of a spin glass phase at 0.8 K. Resistivity measurements were made at room temperature. The resistivity values were found, as expected, to decrease with increasing carrier concentration and to increase with increasing manganese concentration.
Resumo:
Pressure variations of the superconducting transition temperature Ic of a series of amorphous NixZr 1 OO-x alloys have been studied under quasmydrostatic pressures upto 8 G Pa. For amorphous samples having Ni-concentration less than 40%, i)Tc/dP is positive in sign and it decreases non linearly with increase in I. whereasdTcldP is negative in sign for Ni concentration of 45%. Comparison with the Hall coefficient (I) and the thermoelectric power (2) results for the same amorphous alloys leads to the conclusion that s-d hybridization nature of the d-band (Nil plays a central role in the sign reversal behaviour. Application of pressures greater than 2 G Pa to Ni20ZrgO led to the formation of a new phase, w-Zr. which retains its form after the pressure is released.