Continuous hydride generation in the presence of L- cysteine for the determination of arsenic, bismuth, antimony and tin in steels by inductively coupled plasma atomic emission spectrometry

Arsenic, bismuth, germanium, antimony and tin were simultaneously determined by continuous hydride generation and inductively coupled plasma-atomic emission spectrometry . I Hydrides were introduced into four different types of gas-liquid separators. Two of the gas-liquid separators were available in-house. A third was developed for this project and a fourth was based on a design used by CET AC. The best signal intensity was achieved by the type II frit-based gas-liquid separator, but the modified Cetac design gave promise for the future, due to low relative standard deviation. A method was developed for the determination of arsenic, bismuth, antimony and tin in low-alloy steels. Four standard reference materials from NIST were dissolved in 10 mL aqua regia without heat. Good agreement was obtained between experimental values and certified values for arsenic, bismuth, antimony and tin. The method was developed to provide the analyst with the opportunity to determine the analytes by using simple aqueous standards to prepare calibration lines. Within the limits of the samples analyzed, the method developed is independent of matrix.

Set-up and evaluation of a mid-infrared reflectometer and investigation of the optical properties of doped tin telluride

A system comprised of a Bomem interferometer and a LT3-110 Heli-Tran cryostat was set up to measure the reflectance of materials in the mid-infrared spectral region. Several tests were conducted to ensure the consistency and reliability of the system. Silicon and Chromium, two materials with well known optical properties were measured to test the accuracy of the system, and the results were found to be in good agreement with the literature. Reflectance measurements on pure SnTe and several Pb and Mn-doped alloys were carried out. These materials were chosen because they exhibit a strong plasma edge in the mid infrared region. The optical conductivity and several related optical parameters were calculated from the measured reflectance. Very low temperature measurements were carried out in the far-infrared on Sn9SMn2Te, and the results are indicative of a spin glass phase at 0.8 K. Resistivity measurements were made at room temperature. The resistivity values were found, as expected, to decrease with increasing carrier concentration and to increase with increasing manganese concentration.

Far infrared optical properties of V and Cr doped Sb2Te3 /

The far infrared reflectance of Sb2Te3 , Sbi.97Vo.o3Te3 and Sbi.94Cr .o6Te3 was measured near normal incidence at different temperatures (between 45K and 300K). The direct current resistivities of the above samples were also measured between the temperatures of 4K and 300K. Also Kramers Kronig (KK) analyses were performed on the reflectance spectra to obtain the optical conductivities. In the doped samples, it was observed that a phonon at 62cm-1 softens to about 55cm-1 on decreasing the temperature from 295K to 45K. Also, it was observed that the plasma frequency of the doped samples is independent of doping. The scattering rate for the vanadium doped sample was seen to be greater than that for the chromium doped sample despite the fact that vanadium impurity density is less than that of chromium. The Drude-Lorentz model fits to the KK optical conductivity show that the samples used in this work are conventional metals. Definitive measurements of the temperature dependence of the scattering rate across the ferromagnetic transition await equipment changes allowing measurements at low temperature using the mercury cadmium telluride (MCT) detector.