Low frequency Raman scattering in amorphous materials: fused quartz, "pyrex" boro-silicate glass and soda-lime silicate glass

Raman scattering in the region 20 to 100 cm -1 for fused quartz, "pyrex" boro-silicate glass, and soft soda-lime silicate glass was investigated. The Raman spectra for the fused quartz and the pyrex glass were obtained at room temperature using the 488 nm exciting line of a Coherent Radiation argon-ion laser at powers up to 550 mW. For the soft soda-lime glass the 514.5 nm exciting line at powers up to 660 mW was used because of a weak fluorescence which masked the Stokes Raman spectrum. In addition it is demonstrated that the low-frequency Raman coupling constant can be described by a model proposed by Martin and Brenig (MB). By fitting the predicted spectra based on the model with a Gaussian, Poisson, and Lorentzian forms of the correlation function, the structural correlation radius (SCR) was determined for each glass. It was found that to achieve the best possible fit· from each of the three correlation functions a value of the SCR between 0.80 and 0.90 nm was required for both quartz and pyrex glass but for the soft soda-lime silicate glass the required value of the SCR. was between 0.50 and 0.60 nm .. Our results support the claim of Malinovsky and Sokolov (1986) that the MB model based on a Poisson correlation function provides a universal fit to the experimental VH (vertical and horizontal polarizations) spectrum for any glass regardless of its chemical composition. The only deficiency of the MB model is its failure to fit the experimental depolarization spectra.

Pressure dependence of superconductivity in amorphous Ni x Zr 100-x alloys

Pressure variations of the superconducting transition temperature Ic of a series of amorphous NixZr 1 OO-x alloys have been studied under quasmydrostatic pressures upto 8 G Pa. For amorphous samples having Ni-concentration less than 40%, i)Tc/dP is positive in sign and it decreases non linearly with increase in I. whereasdTcldP is negative in sign for Ni concentration of 45%. Comparison with the Hall coefficient (I) and the thermoelectric power (2) results for the same amorphous alloys leads to the conclusion that s-d hybridization nature of the d-band (Nil plays a central role in the sign reversal behaviour. Application of pressures greater than 2 G Pa to Ni20ZrgO led to the formation of a new phase, w-Zr. which retains its form after the pressure is released.

SYNTHESIS OF CYCLIC AZOBENZENE ANALOGUES FOR INCORPORATION INTO OLIGONUCLEOTIDES, PEPTIDES AND POLYMERS

(A) In recent years, considerable amount of effort has contributed towards enhancing our understanding of the new photoswitch, cyclic azobenzene, particularly from the theoretical point of view. However, the challenging part with this system was poor efficiency of its synthesis from 2,2’- dinitrodibenzyl and lack of effective methods for further modification which would be useful to incorporate this system into biomolecules as a photoswitch. We report the synthesis of cyclic azobenzene and analogues from 2,2’-dinitrodibenzyl, which would allow for further incorporation of this cyclic azobenzene into biomolecules. Reaction of 2,2’-dinitrodibenzyl with zinc metal powder in the presence of triethylammonium formate buffer (pH-9.5) gave a cyclic azoxybenzene, 11,12-dihydrodibenzo[c,g][1,2]diazocine-5-oxide. The latter compound was converted into cyclic azobenzene analogues (bromo-, chloro-, cyano-, and carboxyl) through subsequent transformations. The carboxylic acid analogue was reacted with D-threoninol to give the corresponding amide, which readily undergoes photo-isomerization upon illumination with light. Upon illumination with light at 400 nm, approximately 70% of cis- isomer of amide was isomerized to trans- isomer. It was observed that cis- to trans- isomerization reached the maximum steady state of light transmission after approximately 40 min, whereas the trans- to cis- isomerization approximately acquired in 2 h to regain full recovery of light transmission. Cyclic azobenzene phosphoramidite was synthesized from DMT-protected D-threoninol linked cyclic azobenzene. (B) In recent years, there has been considerable interest invested towards the synthesis of azobenzene analogues for incorporation into proteins. Among the many azobenzene analogues, the synthesis of bi-functional cyclic azobenzene analogues for the incorporation into proteins is relatively new. In this thesis, we report the synthesis of a cyclic azobenzene biscarboxylic acid from 4-(bromomethyl)benzonitrile. (C) Azobenzene has been widely used in the field of polymer science to study the surface morphology and surface properties of polymers. In this thesis, we report the incorporation of cyclic azobenzene into a commercial polymer 2- (hydroxyethyl)methacrylate. Samples collected after 24 h from the reaction solution showed approximately 9% of incorporation of cyclic azobenzene into polymer compared to samples collected after 10 h, which showed approximately 6% incorporation.

Lipase-Mediated Enzymatic Catalysis For The Synthesis of New Chiral Polymers

Immobilized lipase B from Candida antarctica (N435) was investigated as a potential biocatalyst to generate silicone-based chiral polymers from monomers derived from the enzymatic dihydroxylation of bromobenzene. Several conditions and parameters have been investigated for this purpose and lipase transesterification preference to each of the free secondary alcohols in the chiral monomers was documented. The N435 was challenged with a series of substrates where the free alcohol moieties were systematically protected in order to study the substrate preference(s) for the transesterification reactions.