Optical properties of organic superconductor K-(BETS)2FeBr4 /

/c-(BETS)2FeBr4 is the first antiferromagnetic organic superconductor with successive antiferromagnetic and superconducting transitions at Ta^=2.5K and Tc=l.lK respectively at ambient pressure. Polarized reflectance measurements were performed on three single crystalsamples of this material using a Briiker IFS66V/S Interferometer, and a Bolometer detector or an MCT detector, at seven temperatures between 4K and 300K, in both the far-infrared and mid-infrared frequency range. After the reflectance results were obtained, the Kramers-Kronig dispersion relation was apphed to determine the optical conductivity of /c-(BETS)2FeBr4 at these seven temperatures. Additionally, the optical conductivity spectra were fitted with a Drude/Lorentz Oscillator model in order to study the evolution of the optical conductivity with temperature along the a-axis and c-axis. The resistivities calculated from the Drude model parameters along the a-axis and c-axis agreed reasonably with previous transport measurements.

Far infrared optical properties of V and Cr doped Sb2Te3 /

The far infrared reflectance of Sb2Te3 , Sbi.97Vo.o3Te3 and Sbi.94Cr .o6Te3 was measured near normal incidence at different temperatures (between 45K and 300K). The direct current resistivities of the above samples were also measured between the temperatures of 4K and 300K. Also Kramers Kronig (KK) analyses were performed on the reflectance spectra to obtain the optical conductivities. In the doped samples, it was observed that a phonon at 62cm-1 softens to about 55cm-1 on decreasing the temperature from 295K to 45K. Also, it was observed that the plasma frequency of the doped samples is independent of doping. The scattering rate for the vanadium doped sample was seen to be greater than that for the chromium doped sample despite the fact that vanadium impurity density is less than that of chromium. The Drude-Lorentz model fits to the KK optical conductivity show that the samples used in this work are conventional metals. Definitive measurements of the temperature dependence of the scattering rate across the ferromagnetic transition await equipment changes allowing measurements at low temperature using the mercury cadmium telluride (MCT) detector.

Specific heat of UPdâ Siâ

The specific heat of single-crystal U Pd2 Si2 has been studied using both the step heating and continious heating methods for the temperature range 2 to 250 K. Successive phase transitions at Tl = 136I< and T2 = 108I< are reported, which are consistent with current publications. The transition at 40K, which was previously reported, has not been detected. Recent published elastic neutron scattering data, magnetic susceptibility and resistivity results suggest that U Pd2 Si2 may be a heavy fermion compound, however, the electronic specific heat coefficient I (= 18.97 ;~), obtained from the specific heat Cv measurements, is smaller than that of the conventional heavy fermion system. The Debye temperature of U Pd2Si2 is found to be 116.55K. The possibility is discussed that the maximum in CIT in the low-temperature range 2 to 4K corresponds to Schottky anomaly induced by localized magnetic impurities .