Magnesium hydroxide-based peroxide bleaching of high-brightness mechanical pulps

A high final brightness is desired in most paper and board products. This requires bleaching processes that are able to produce high-brightness pulps. Mechanical pulps are widely bleached for high brightness using alkaline hydrogen peroxide with traditional sodium hydroxide and sodium silicate as additives. With high doses however, peroxide bleaching causes high organic loads in the mill effluent and anionic trash carry-over to papermaking. To alleviate the problems that arise from the use of sodium-based additives in peroxide bleaching, interest in the use of alternative magnesium-based chemicals has increased. In this study, a new, technical high-purity magnesium hydroxide-based bleaching additive was evaluated on laboratory-scale, pilot-scale and mill-scale experiments and trials for its ability to produce a high brightness in peroxide bleaching without the known problems of sodium-based chemicals. The key findings of this study include: a high brightening potential of peroxide bleaching using the Mg(OH)2-based additive, significant reductions (40-70%) in all categories of environmental load, and cationic demand lowered by 60-70% in bleached pulp with no loss in strength properties or in sheet bulk. When used in TMP refiner bleaching, the Mg(OH)2-based additive resulted in savings in specific energy consumption and provided a good bleaching response.

Vaihtoehtoalkalit mekaanisen massan peroksidivalkaisussa

Tehokkain tapavalkaista mekaanisesti kuidutettua puumassaa on suorittaa se hapettavasti peroksidikemikaalilla vahvasti alkalisissa oloissa. Perinteisesti alkalisuus on aikaansaatu natriumhydroksidin ja -silikaatin avulla. Se kuitenkin liuottaa massasta merkittävästi ligniiniä, mikä huonontaa saantoa ja suurentaa valkaisun jätevesien orgaanisen hiilen määrää sekä kemiallista hapenkulutusta. Yhä kovenevien vaaleustavoitteiden ja tiukentuneen vedenkäytön seurauksena on syntynyt tarve etsiä parempia valkaisun alkaleja. Kirjallisuuden pohjalta valittiinkokeellisesti tutkittaviksi alkaleiksi magnesiumhydroksidi, magnesiumoksidi, kalsiumhydroksidi sekä kalsiumoksidi. Niiden toimivuutta hapettavan vetyperoksidivalkaisun alkaleina tutkittiin valkaisukokein natriumsilikaattilisäyksen kanssa sekä ilman. Näistä parhaiten toimivaksi osoittautui Mg(OH)2. Sen avulla suoritettiin jatkoksi laboratoriokoevalkaisuja korkeassa sakeudessa. Keski- ja korkeasakeusvalkaisukokeiden tulosten mukaan käytettäessä Mg(OH)2 -alkalia natriumydroksidin ja -silikaatin asemesta jää massan loppuvaaleus noin yhden ISO-prosentin verran heikommaksi. Tällöin valkaisusuodoksessa oli vain varsin vähäinen määrä massasta liuennutta orgaanista hiiliainesta, noin 45 % siitä, mitä natriumin yhdisteiden käyttö vertailukokeessa tuotti. Tulosta varmennettiin suorittamalla korkea-sakeusvalkaisukokeita hiokemassatehtaan olosuhteissa, massoilla ja kiertovesillä.Myös tehdaskokeiden mukaan valkaistun massan loppuvaaleus jää noin yhden ISO-prosentin alhaisemmaksi, mutta valkaisusuodoksen orgaanisen hiilen määrä (TOC) jääalle puoleen Na-kemikaalein suoritetusta vertailukokeesta.

Häiriöaineiden vaikutus käytettäessä magnesiumhydroksidialkalia mekaanisen massan peroksidivalkaisussa

Nykypäivänä ympäristön suojelu ja erityisesti jätevesipäästöjen pienentäminen vaikuttavat yhä enemmän metsäteollisuuden toimintatapoihin. Lisäksi veden käytön vähentyessä ja prosesseja suljettaessa silikaatteihin väistämättä liittyvät saostumat ovat kasvava ongelma. Magnesiumhydroksidin on havaittu olevan potentiaalinen natriumhydroksidin korvaava alkali mekaanisen massan peroksidivalkaisussa. Lisäksi magnesiumhydroksidilla voidaan saavuttaa lähes yhtä korkea vaaleus, jopa ilman silikaattia, kuin natriumhydroksidilla natriumsilikaatin kanssa. Magnesiumhydroksidin orgaanista ainesta liuottava vaikutus on myös noin puolet verrattuna natriumhydroksidiin. Työssä selvitettiin, miten häiriöaineet vaikuttavat mekaanisen massan peroksidivalkaisuun käytettäessä magnesiumhydroksidialkalia. Laboratoriokokeiden tulokset osoittivat, että magnesiumhydroksidi kesti paremmin valkaisussa käytettyjä häiriöaineita. Pienillä metallilisäyksillä ei ole vaikutusta massan vaaleuteen käytettäessä magnesiumhydroksidia. Korvattaessa laimennusvettä viirapuristimen suodoksella peroksidi kului lähes loppuun käytettäessä natriumhydroksidia, mikä näkyi myös vaaleuden heikkenemisenä. Valkaisukokeiden perusteella magnesiumhydroksidialkalilla jäädään jopa kolme prosenttiyksikköä natriumhydroksidin kanssa saadusta vaaleudesta, peroksidiannoksen olleessa kolme prosenttia. Mutta käytettäessä magnesiumhydroksidialkalia liuenneen orgaanisen hiilen kokonaismäärä (TOC) sekä biologinen (BOD7) että kemiallinen (CODcr) hapenkulutus pienenivät lähes puolella.

Magnesiumhydroksidialkalin käytön vaikutukset päällystämättömän aikakauslehtipaperin valmistukseen

Magnesiumhydroksidin on havaittu soveltuvan natriumhydroksidin korvaajaksi mekaanisen massan peroksidivalkaisun alkalina. Työssä selvitettiin, miten magnesiumhydroksidi vaikuttaa paperin valmistukseen ja valmiin paperin ominaisuuksiin. Laboratoriokokeet osoittivat magnesiumhydroksidin soveltuvan mekaanisen massan peroksidivalkaisun alkaliksi, sillä vaaleustavoite saavutettiin sen avulla. Valkaistun massan varaustila, johtokyky sekä ζ -potentiaali laskivat magnesiumhydroksidin vaikutuksesta. Nämä johtivat huomattavasti korkeampaan paperin täyteaineretentioon. Massan vedenpidätyskyky kasvoi korvattaessa natriumhydroksidi magnesiumhydroksidilla. Arkkien ominaisuuksista vetoindeksi, valonsirontakerroin ja taivutusjäykkyys kasvoivat. Kaikki edellä mainitut ominaisuudet viittaavat siihen, että magnesiumhydroksidin käyttö parantaa hienoaineen sitoutumista paperiin.

Influence of reactant absorption and dissolution in heterogeneous precipitation processes

In this research work, the aim was to investigate the volumetric mass transfer coefficient [kLa] of oxygen in stirred tank in the presence of solid particle experimentally. The kLa correlations as a function of propeller rotation speed and flow rate of gas feed were studied. The O2 and CO2 absorption in water and in solid-liquid suspensions and heterogeneous precipitation of MgCO3 were thoroughly examined. The absorption experiments of oxygen were conducted in various systems like pure water and in aqueous suspensions of quartz and calcium carbonate particles. Secondly, the precipitation kinetics of magnesium carbonate was also investigated. The experiments were performed to study the reactive crystallization with magnesium hydroxide slurry and carbon dioxide gas by varying the feed rates of carbon dioxide and rotation speeds of mixer. The results of absorption and precipitation are evaluated by titration, total carbon (TC analysis), and ionic chromatrography (IC). For calcium carbonate, the particle concentration was varied from 17.4 g to 2382 g with two size fractions: 5 µm and 45-63 µm sieves. The kLa and P/V values of 17.4 g CaCO3 with particle size of 5µm and 45-63 µm were 0.016 s-1 and 2400 W/m3. At 69.9 g concentration of CaCO3, the achieved kLa is 0.014 s-1 with particle size of 5 µm and 0.017 s-1 with particle size of 45 to 63 µm. Further increase in concentration of calcium carbonate, i.e. 870g and 2382g , does not affect volumetric mass transfer coeffienct of oxygen. It could be concluded from absorption results that maximum value of kLa is 0.016 s-1. Also particle size and concentration does affect the transfer rate to some extend. For precipitation experiments, the constant concentration of Mg(OH)2 was 100 g and the rotation speed varied from 560 to 750 rpm, whereas the used feed rates of CO2 were 1 and 9 L/min. At 560 rpm and feed rate of CO2 is 1 L/min, the maximum value of Mg ion and TC were 0.25 mol/litre and 0.12 mol/litre with the residence time of 40 min. When flow rate of CO2 increased to 9 L/min with same 560 rpm, the achieved value of Mg and TC were 0.3 mol/litre and 0.12 mol/L with shorter residence time of 30 min. It is concluded that feed rate of CO2 is dominant in precipitation experiments and it has a key role in dissociation and reaction of magnesium hydroxide in precipitation of magnesium carbonate.

Influence of multi-phase phenomena on semibatch crystallization processes of aqueous solutions

Crystal properties, product quality and particle size are determined by the operating conditions in the crystallization process. Thus, in order to obtain desired end-products, the crystallization process should be effectively controlled based on reliable kinetic information, which can be provided by powerful analytical tools such as Raman spectrometry and thermal analysis. The present research work studied various crystallization processes such as reactive crystallization, precipitation with anti-solvent and evaporation crystallization. The goal of the work was to understand more comprehensively the fundamentals, phenomena and utilizations of crystallization, and establish proper methods to control particle size distribution, especially for three phase gas-liquid-solid crystallization systems. As a part of the solid-liquid equilibrium studies in this work, prediction of KCl solubility in a MgCl2-KCl-H2O system was studied theoretically. Additionally, a solubility prediction model by Pitzer thermodynamic model was investigated based on solubility measurements of potassium dihydrogen phosphate with the presence of non-electronic organic substances in aqueous solutions. The prediction model helps to extend literature data and offers an easy and economical way to choose solvent for anti-solvent precipitation. Using experimental and modern analytical methods, precipitation kinetics and mass transfer in reactive crystallization of magnesium carbonate hydrates with magnesium hydroxide slurry and CO2 gas were systematically investigated. The obtained results gave deeper insight into gas-liquid-solid interactions and the mechanisms of this heterogeneous crystallization process. The research approach developed can provide theoretical guidance and act as a useful reference to promote development of gas-liquid reactive crystallization. Gas-liquid mass transfer of absorption in the presence of solid particles in a stirred tank was investigated in order to gain understanding of how different-sized particles interact with gas bubbles. Based on obtained volumetric mass transfer coefficient values, it was found that the influence of the presence of small particles on gas-liquid mass transfer cannot be ignored since there are interactions between bubbles and particles. Raman spectrometry was successfully applied for liquid and solids analysis in semi-batch anti-solvent precipitation and evaporation crystallization. Real-time information such as supersaturation, formation of precipitates and identification of crystal polymorphs could be obtained by Raman spectrometry. The solubility prediction models, monitoring methods for precipitation and empirical model for absorption developed in this study together with the methodologies used gives valuable information for aspects of industrial crystallization. Furthermore, Raman analysis was seen to be a potential controlling method for various crystallization processes.

Carponate precipitation with carbon dioxide gas

The aim of this thesis research work focused on the carbonate precipitation of magnesium using magnesium hydroxide Mg(OH)2 and carbon dioxide (CO2) gas at ambient temperature and pressure. The rate of dissolution of Mg(OH)2 and precipitation kinetics were investigated under different operating conditions. The conductivity and pH of the solution were inline monitored by a Consort meter and the solid samples gotten from the precipitation reaction were analysed by a laser diffraction analyzer Malvern Mastersizer to obtain particle size distributions (PSD) of crystal samples. Also the Mg2+ concentration profiles were determined from the liquid phase of the precipitate by ion chromatography (IC) analysis. Crystal morphology of the obtained precipitates were also investigated and discussed in this work. For the carbonation reaction of magnesium hydroxide in the present work, it was found that magnesium carbonate trihydrate (nesquehonite) was the main product and its formation occurred at a pH of around 7-8. The stirrer speed has a significant effect on the dissolution rate of Mg(OH)2. The highest obtained Mg2+ concentration level was 0.424 mol L-l for the 470 rpm and 0.387 mol L-1 for the 560 rpm which corresponded to the processing time of 45 mins and 40 mins respectively. The particle size distribution shows that the average particle size keeps increasing during the reaction as the CO2 is been fed to the system. The carbonation process is kinetically favored and simple as nesquehonite formation occurs in a very short time. It is a thermodynamically and chemically stable solid product, which allows for a long-term storage of CO2. Since the carbonation reaction is a complex system which includes dissolution of magnesium hydroxide particles, absorption of CO2, chemical reaction and crystallization, the dissolution of magnesium hydroxide was studied in hydrochloric acid (HCl) solvent with and without nitrogen (N2) inert gas. It was found on the dissolution part that the impeller speed had effect on the dissolution rate. The higher the impeller speed the higher the pH of the solution, although for the highest speed of 650rpm it was not the case. Therefore, it was concluded that the optimum speed of the stirrer was 560rpm. The influence of inert gas N2 on the dissolution rate of Mg(OH)2 particles could be seen based on measured pH, electric conductivity and Mg2+ concentration curves.

Production of magnesium carbonates from serpentinites for CO2 mineral sequestration : optimisation towards industrial application

Global warming is one of the most alarming problems of this century. Initial scepticism concerning its validity is currently dwarfed by the intensification of extreme weather events whilst the gradual arising level of anthropogenic CO2 is pointed out as its main driver. Most of the greenhouse gas (GHG) emissions come from large point sources (heat and power production and industrial processes) and the continued use of fossil fuels requires quick and effective measures to meet the world’s energy demand whilst (at least) stabilizing CO2 atmospheric levels. The framework known as Carbon Capture and Storage (CCS) – or Carbon Capture Utilization and Storage (CCUS) – comprises a portfolio of technologies applicable to large‐scale GHG sources for preventing CO2 from entering the atmosphere. Amongst them, CO2 capture and mineralisation (CCM) presents the highest potential for CO2 sequestration as the predicted carbon storage capacity (as mineral carbonates) far exceeds the estimated levels of the worldwide identified fossil fuel reserves. The work presented in this thesis aims at taking a step forward to the deployment of an energy/cost effective process for simultaneous capture and storage of CO2 in the form of thermodynamically stable and environmentally friendly solid carbonates. R&D work on the process considered here began in 2007 at Åbo Akademi University in Finland. It involves the processing of magnesium silicate minerals with recyclable ammonium salts for extraction of magnesium at ambient pressure and 400‐440⁰C, followed by aqueous precipitation of magnesium in the form of hydroxide, Mg(OH)2, and finally Mg(OH)2 carbonation in a pressurised fluidized bed reactor at ~510⁰C and ~20 bar PCO2 to produce high purity MgCO3. Rock material taken from the Hitura nickel mine, Finland, and serpentinite collected from Bragança, Portugal, were tested for magnesium extraction with both ammonium sulphate and bisulphate (AS and ABS) for determination of optimal operation parameters, primarily: reaction time, reactor type and presence of moisture. Typical efficiencies range from 50 to 80% of magnesium extraction at 350‐450⁰C. In general ABS performs better than AS showing comparable efficiencies at lower temperature and reaction times. The best experimental results so far obtained include 80% magnesium extraction with ABS at 450⁰C in a laboratory scale rotary kiln and 70% Mg(OH)2 carbonation in the PFB at 500⁰C, 20 bar CO2 pressure for 15 minutes. The extraction reaction with ammonium salts is not at all selective towards magnesium. Other elements like iron, nickel, chromium, copper, etc., are also co‐extracted. Their separation, recovery and valorisation are addressed as well and found to be of great importance. The assessment of the exergetic performance of the process was carried out using Aspen Plus® software and pinch analysis technology. The choice of fluxing agent and its recovery method have a decisive sway in the performance of the process: AS is recovered by crystallisation and in general the whole process requires more exergy (2.48–5.09 GJ/tCO2sequestered) than ABS (2.48–4.47 GJ/tCO2sequestered) when ABS is recovered by thermal decomposition. However, the corrosive nature of molten ABS and operational problems inherent to thermal regeneration of ABS prohibit this route. Regeneration of ABS through addition of H2SO4 to AS (followed by crystallisation) results in an overall negative exergy balance (mainly at the expense of low grade heat) but will flood the system with sulphates. Although the ÅA route is still energy intensive, its performance is comparable to conventional CO2 capture methods using alkanolamine solvents. An energy‐neutral process is dependent on the availability and quality of nearby waste heat and economic viability might be achieved with: magnesium extraction and carbonation levels ≥ 90%, the processing of CO2‐containing flue gases (eliminating the expensive capture step) and production of marketable products.

Effect of anionic salts in concentrate mixture and magnesium intake on some blood and urine minerals and acid-base balance of dry pregnant cows on grass silage based feeding

Selostus: Kationi-anionitasapaino ja magnesiumin saanti ummessaolevien lypsylehmien säilörehuruokinnassa

Calcination of aluminum hydroxide over pressure and residence time

This work investigates the possible effect of pressure and residence time to the reaction of aluminum hydroxide into aluminum oxide. Various pressurized conditions are used as well as the help of various residence times. The aim is to increase the conversion of the reaction with the use of different pressures and residence times. The tests were performed with a laboratory scale fluidized bed reactor at the Outotec R&D Center in Frankfurt. Additional test work such as particle size analysis and differential thermal analysis were also carried out. Some calcined samples were also characterized with X-ray diffraction at the University of Auckland to obtain a reaction pathway when using pressurized conditions. All of the results are then compared with previous results.

Adsorption of arsenic from ammonia containing waste water by ferrous hydroxide waste

Arsenic is a toxic substance. The amount of arsenic in waste water is a raising problem because of increasing mining industry. Arsenic is connected to cancers in areas where arsenic concentration in drinking water is higher than recommendations. The main object in this master’s thesis was to research how ferrous hydroxide waste material is adsorbed arsenic from ammonia containing waste water. In this master’s thesis there is two parts: theoretical and experimental part. In theoretical part harmful effects of arsenic, theory of adsorption, isotherms modeling of adsorption and analysis methods of arsenic are described. In experimental part adsorption capacity of ferrous hydroxide waste material and adsorption time with different concentrations of arsenic were studied. Waste material was modified with two modification methods. Based on experimental results the adsorption capacity of waste material was high. The problem with waste material was that at same time with arsenic adsorption sulfur was dissolving in solution. Waste material was purified from sulfur but purification methods were not efficient enough. Purification methods require more research.

Stability and properties of cellulose-sodium hydroxide solution systems

Since cellulose is a linear macromolecule it can be used as a material for regenerated cellulose fiber products e.g. in textile fibers or film manufacturing. Cellulose is not thermoformable, thus the manufacturing of these regenerated fibers is mainly possible through dissolution processes preceding the regeneration process. However, the dissolution of cellulose in common solvents is hindered due to inter- and intra-molecular hydrogen bonds in the cellulose chains, and relatively high crystallinity. Interestingly at subzero temperatures relatively dilute sodium hydroxide solutions can be used to dissolve cellulose to a certain extent. The objective of this work was to investigate the possible factors that govern the solubility of cellulose in aqueous NaOH and the solution stability. Cellulose-NaOH solutions have the tendency to form a gel over time and at elevated temperature, which creates challenges for further processing. The main target of this work was to achieve high solubility of cellulose in aqueous NaOH without excessively compromising the solution stability. In the literature survey an overview of the cellulose dissolution is given and possible factors contributing to the solubility and solution properties of cellulose in aqueous NaOH are reviewed. Furthermore, the concept of solution rheology is discussed. In the experimental part the focus was on the characterization of the used materials and properties of the prepared solutions mainly concentrating on cellulose solubility and solution stability.

Continuous Counter-current Solvent Extraction of Magnesium and Calcium from Lithium-rich Brine

Solvent extraction of calcium and magnesium impurities from a lithium-rich brine (Ca ~ 2,000 ppm, Mg ~ 50 ppm, Li ~ 30,000 ppm) was investigated using a continuous counter-current solvent extraction mixer-settler set-up. The literature review includes a general review about resources, demands and production methods of Li followed by basics of solvent extraction. Experimental section includes batch experiments for investigation of pH isotherms of three extractants; D2EHPA, Versatic 10 and LIX 984 with concentrations of 0.52, 0.53 and 0.50 M in kerosene respectively. Based on pH isotherms LIX 984 showed no affinity for solvent extraction of Mg and Ca at pH ≤ 8 while D2EHPA and Versatic 10 were effective in extraction of Ca and Mg. Based on constructed pH isotherms, loading isotherms of D2EHPA (at pH 3.5 and 3.9) and Versatic 10 (at pH 7 and 8) were further investigated. Furthermore based on McCabe-Thiele method, two extraction stages and one stripping stage (using HCl acid with concentration of 2 M for Versatic 10 and 3 M for D2EHPA) was practiced in continuous runs. Merits of Versatic 10 in comparison to D2EHPA are higher selectivity for Ca and Mg, faster phase disengagement, no detrimental change in viscosity due to shear amount of metal extraction and lower acidity in stripping. On the other hand D2EHPA has less aqueous solubility and is capable of removing Mg and Ca simultaneously even at higher Ca loading (A/O in continuous runs > 1). In general, shorter residence time (~ 2 min), lower temperature (~23 °C), lower pH values (6.5-7.0 for Versatic 10 and 3.5-3.7 for D2EHPA) and a moderately low A/O value (< 1:1) would cause removal of 100% of Ca and nearly 100% of Mg while keeping Li loss less than 4%, much lower than the conventional precipitation in which 20% of Li is lost.