Effect of Mechanical and Geometric Mismatching on Fatigue and Damage of Welded Joints

The future of high technology welded constructions will be characterised by higher strength materials and improved weld quality with respect to fatigue resistance. The expected implementation of high quality high strength steel welds will require that more attention be given to the issues of crack initiation and mechanical mismatching. Experiments and finite element analyses were performed within the framework of continuum damage mechanics to investigate the effect of mismatching of welded joints on void nucleation and coalescence during monotonic loading. It was found that the damage of undermatched joints mainly occurred in the sandwich layer and the damageresistance of the joints decreases with the decrease of the sandwich layer width. The damage of over-matched joints mainly occurred in the base metal adjacent to the sandwich layer and the damage resistance of the joints increases with thedecrease of the sandwich layer width. The mechanisms of the initiation of the micro voids/cracks were found to be cracking of the inclusions or the embrittled second phase, and the debonding of the inclusions from the matrix. Experimental fatigue crack growth rate testing showed that the fatigue life of under-matched central crack panel specimens is longer than that of over-matched and even-matched specimens. Further investigation by the elastic-plastic finite element analysis indicated that fatigue crack closure, which originated from the inhomogeneousyielding adjacent to the crack tip, played an important role in the fatigue crack propagation. The applicability of the J integral concept to the mismatched specimens with crack extension under cyclic loading was assessed. The concept of fatigue class used by the International Institute of Welding was introduced in the parametric numerical analysis of several welded joints. The effect of weld geometry and load condition on fatigue strength of ferrite-pearlite steel joints was systematically evaluated based on linear elastic fracture mechanics. Joint types included lap joints, angle joints and butt joints. Various combinations of the tensile and bending loads were considered during the evaluation with the emphasis focused on the existence of both root and toe cracks. For a lap joint with asmall lack-of-penetration, a reasonably large weld leg and smaller flank angle were recommended for engineering practice in order to achieve higher fatigue strength. It was found that the fatigue strength of the angle joint depended strongly on the location and orientation of the preexisting crack-like welding defects, even if the joint was welded with full penetration. It is commonly believed that the double sided butt welds can have significantly higher fatigue strength than that of a single sided welds, but fatigue crack initiation and propagation can originate from the weld root if the welding procedure results in a partial penetration. It is clearly shown that the fatigue strength of the butt joint could be improved remarkably by ensuring full penetration. Nevertheless, increasing the fatigue strength of a butt joint by increasing the size of the weld is an uneconomical alternative.

Utilizing social media in software documentation and knowledge management

This Master’s thesis studies the possibilities that social media tools can bring to help knowledge management in software development companies. It will introduce the most popular tools of social media and their usage possibilities in companies, not forgetting the possible downsides. One relevant aspect in this study is to investigate the possibilities of social media to help converting existing tacit knowledge into explicit. The purpose of the work is to create a proposal of social media utilization for a mid-sized software company, which has not utilized social media tools before. To be able to create the proposal, employees of the company are interviewed and a survey is executed to analyze the current situation. In addition a pilot project for trying out new social media tools is executed. The final result of this thesis introduces a tailored solution for the target company to start utilizing social media in its documentation and knowledge sharing processes. This new solution consists of multiple individual suggestions that are categorized and prioritized based on the significance and benefit that they bring to the company.

Health-related quality of life in school children: validation of instrument, child self assessment, parent-proxy assessment and school nursing documentation of health check-ups

The aims of this study were to validate an international Health-Related Quality of Life (HRQL) instrument, to describe child self and parent-proxy assessed HRQL at child age 10 to 12 and to compare child self assessments with parent-proxy assessments and school nursing documentation. The study is part of the Schools on the Move –research project. In phase one, a cross-cultural translation and validation process was performed to develop a Finnish version of Pediatric Quality of Life Inventory™ 4.0 (PedsQL™ 4.0). The process included a two-way translation, cognitive interviews (children n=7, parents n=5) and a survey (children n=1097, parents n=999). In phase two, baseline and follow-up surveys (children n=986, parents n=710) were conducted to describe and compare the child self and parent-proxy assessed HRQL in school children between the ages 10 and 12. Phase three included two separate data, school nurse documented patient records (children n=270) and a survey (children n=986). The relation between child self assessed HRQL and school nursing documentation was evaluated. Validity and reliability of the Finnish version of PedsQL™ 4.0 was good (Child Self Report α=0.91, Parent-Proxy Report α=0.88). Children reported lower HRQL scores at the emotional (mean 76/80) than the physical (mean 85/89) health domains and significantly lower scores at the age of 10 than 12 (dMean=4, p=<0.001). Agreement between child self and parent-proxy assessment was fragile (r=0,4, p=<0.001) but increased as the child grew from age 10 to 12 years. At health check-ups, school nurses documented frequently children’s physical health, such as growth (97%) and posture (98/99%) but seldom emotional issues, such as mood (2/7%). The PedsQLTM 4.0 is a valid instrument to assess HRQL in Finnish school children although future research is recommended. Children’s emotional wellbeing needs future attention. HRQL scores increase during ages between childhood and adolescence. Concordance between child self and parent-proxy assessed HRQL is low. School nursing documentation, related to child health check-ups, is not in line with child self assessed HRQL and emotional issues need more attention.

Transfer pricing documentation differences in Finland and China - Case company study

This Master’s Thesis deals with the topic of transfer pricing documentation in Finland and China. The goal of the research is to find what kind of differences exist in a single case company’s transfer pricing documentation when following Chinese or Finnish transfer pricing regulations. The study is carried out as a case study research. The theoretical framework consists of information from different transfer pricing topics and transfer pricing documentation regulations in China and Finland. The main research material was the case company’s transfer pricing documents with the support of open discus-sion with one of the case company’s employees. The study compared the 2009 and 2010 documents. The 2009 document was done based on the Finnish method while the 2010 document was based on the Chinese documentation principles. The conclusion made is that the content of the documents was heavily similar, while the main differences come in the way the content is presented and the level of detail used in the documents.