The effect of microfibrillated cellulose addition on drying shrinkage and dimensional stability of wood-free paper

Microfibrillated cellulose (MFC) is known to enhance strength properties of paper. Improved strength usually means increased bonding which is strongly connected to dimensional instability of paper. Dimensional instability is due to changes in moisture content of paper; when paper is moistened it expands and when dried, it shrinks. Hygroexpansion is linked to end-use problems and excessive drying shrinkage consumes strength potential. Effective use of materials requires controlling of these phenomena. There isn’t yet data concerning dimensional stability of papers containing MFC which restricts wider use of MFC. Main objective of the work was to evaluate dimensional stability of wood-free paper containing different amounts of MFC. Sheets were dried with different methods to see how drying strains effected on drying shrinkage and hygroexpansion. Also tensile strength was measured to find out the effect of MFC. Results were compared to sheets containing kraft fines and in some test points cationic starch was used alongside with MFC. MFC increased the dimensional instability of freely dried sheets. As the amounts of MFC increased the effects on dimensional stability became more severe. However the fineness of MFC didn’t play any important role. Both hygroexpansion and drying shrinkage were decreased with cationic starch addition. Prevention of drying shrinkage over powered the effects of additives on hygroexpansion. Tensile strength improved up till 7 % addition amount which could be set as the upper limit of MFC addition when paper preparation and tensile strength are concerned.

Stability of Natural Colorants of Plant Origin

In recent years, there have been studies that show a correlation between the hyperactivity of children and use of artificial food additives, including colorants. This has, in part, led to preference of natural products over products with artificial additives. Consumers have also become more aware of health issues. Natural food colorants have many bioactive functions, mainly vitamin A activity of carotenoids and antioxidativity, and therefore they could be more easily accepted by the consumers. However, natural colorant compounds are usually unstable, which restricts their usage. Microencapsulation could be one way to enhance the stability of natural colorant compounds and thus enable better usage for them as food colorants. Microencapsulation is a term used for processes in which the active material is totally enveloped in a coating or capsule, and thus it is separated and protected from the surrounding environment. In addition to protection by the capsule, microencapsulation can also be used to modify solubility and other properties of the encapsulated material, for example, to incorporate fat-soluble compounds into aqueous matrices. The aim of this thesis work was to study the stability of two natural pigments, lutein (carotenoid) and betanin (betalain), and to determine possible ways to enhance their stability with different microencapsulation techniques. Another aim was the extraction of pigments without the use of organic solvents and the development of previously used extraction methods. Stability of pigments in microencapsulated pigment preparations and model foods containing these were studied by measuring the pigment content after storage in different conditions. Preliminary studies on the bioavailability of microencapsulated pigments and sensory evaluation for consumer acceptance of model foods containing microencapsulated pigments were also carried out. Enzyme-assisted oil extraction was used to extract lutein from marigold (Tagetes erecta) flower without organic solvents, and the yield was comparable to solvent extraction of lutein from the same flowers. The effects of temperature, extraction time, and beet:water ratio on extraction efficiency of betanin from red beet (Beta vulgaris) were studied and the optimal conditions for maximum yield and maximum betanin concentration were determined. In both cases, extraction at 40 °C was better than extraction at 80 °C and the extraction for five minutes was as efficient as 15 or 30 minutes. For maximum betanin yield, the beet:water ratio of 1:2 was better, with possibly repeated extraction, but for maximum betanin concentration, a ratio of 1:1 was better. Lutein was incorporated into oil-in-water (o/w) emulsions with a polar oil fraction from oat (Avena sativa) as an emulsifier and mixtures of guar gum and xanthan gum or locust bean gum and xanthan gum as stabilizers to retard creaming. The stability of lutein in these emulsions was quite good, with 77 to 91 percent of lutein being left after storage in the dark at 20 to 22°C for 10 weeks whereas in spray dried emulsions the retention of lutein was 67 to 75 percent. The retention of lutein in oil was also good at 85 percent. Betanin was incorporated into the inner w1 water phase of a water1-in-oil-inwater2 (w1/o/w2) double emulsion with primary w1/o emulsion droplet size of 0.34 μm and secondary w1/o/w2 emulsion droplet size of 5.5 μm and encapsulation efficiency of betanin of 89 percent. In vitro intestinal lipid digestion was performed on the double emulsion, and during the first two hours, coalescence of the inner water phase droplets was observed, and the sizes of the double emulsion droplets increased quickly because of aggregation. This period also corresponded to gradual release of betanin, with a final release of 35 percent. The double emulsion structure was retained throughout the three-hour experiment. Betanin was also spray dried and incorporated into model juices with different pH and dry matter content. Model juices were stored in the dark at -20, 4, 20–24 or 60 °C (accelerated test) for several months. Betanin degraded quite rapidly in all of the samples and higher temperature and a lower pH accelerated degradation. Stability of betanin was much better in the spray dried powder, with practically no degradation during six months of storage in the dark at 20 to 24 °C and good stability also for six months in the dark at 60 °C with 60 percent retention. Consumer acceptance of model juices colored with spray dried betanin was compared with similar model juices colored with anthocyanins or beet extract. Consumers preferred beet extract and anthocyanin colored model juices over juices colored with spray dried betanin. However, spray dried betanin did not impart any off-odors or off-flavors into the model juices contrary to the beet extract. In conclusion, this thesis describes novel solvent-free extraction and encapsulation processes for lutein and betanin from plant sources. Lutein showed good stability in oil and in o/w emulsions, but slightly inferior in spray dried emulsions. In vitro intestinal lipid digestion showed a good stability of w1/o/w2 double emulsion and quite high retention of betanin during digestion. Consumer acceptance of model juices colored with spray dried betanin was not as good as model juices colored with anthocyanins, but addition of betanin to real berry juice could produce better results with mixture of added betanin and natural berry anthocyanins could produce a more acceptable color. Overall, further studies are needed to obtain natural colorants with good stability for the use in food products.

Effect of ambient conditions on dimensional stability and stiffness of commercial paperboard and paperboard trays

The objective of this study was to develop laboratory test methods for characterizing the effects of changed moisture content on paperboard trays produced by press-forming process. Influence of moisture on the properties of unconverted paperboard such as bending stiffness, bursting strength, and curling was studied. Paperboard and tray samples were tested after storing in different relative humidity conditions (35, 50, 65, 80 and 95% RH). The effect of PE and PET extrusion coatings on these properties was also studied. It was found that increase in moisture content of paperboard decreases bending and bursting strength, dimensional stability and stiffness of paperboard trays. Such physical and mechanical properties as bending stiffness and curling of paperboard seem to define the stiffness of ready-made trays and their dimensional stability. Paperboards and trays with extruded PE and PET one sided coatings demonstrated higher strength properties but at the same time had lower dimensional stability comparing to uncoated paperboards. Samples with smaller polymer coat weight had better dimensional stability than respective samples with higher coat weight. It was also found that preconditioning of paperboard in lower humidity environment before press-forming could improve dimensional stability and stiffness of ready-made tray.