Epäpuhtausmetallien talteenotto sinkkiprosessissa

There are small amounts of valuable metals, such as indium, gallium and germanium, in zinc process solutions. Their solvent extraction was studied in this work in sulphate solutions containing zinc and other metals present in industrial solutions. It was discovered, that a commercial bis(2-ethylhexyl)phosphate (D2EHPA) extractant can be used to extract indium and gallium. Indium was extracted separately at a higher acid concentration than gallium. Zinc was co-extracted faster than gallium and almost as much as gallium at the same pH. However, the scrubbing of zinc was possible using a dilute sulphuric acid and a short contact time while gallium losses were small. Both indium and gallium were stripped with sulphuric acid. Germanium was extracted with 5,8-diethyl-7-hydroxydodecane-6-oxime with the commercial name of LIX 63. Unlike other metals in the solution the extraction of germanium increased with different extractants as the acidity increased. Germanium extraction isotherm was measured for a 125 g/L sulfuric acid solution. The loaded organic phase was washed with pure water. It removed the co-extracted acid and part of the germanium and extracted impurities such as iron and copper. Germanium was stripped using a NaOH solution. A process model utilizing own experimentally determined extraction, scrubbing and stripping isotherms was made with HSC Sim software developed by Outotec Oyj. The model based on McCabe–Thiele diagrams was used in sizing the necessary amount of stages and phase ratios in a recovery process. It was concluded, that indium, gallium and germanium can be recovered in the process from a feed where their concentrations are low (<300 ppm). In an example case the feed contained also more than 20 g/L zinc and 2–8 g/L iron, aluminium and copper. The recoveries of indium, gallium and germanium were more than 90 % when 1–3 stages were used in each extraction, scrubbing and stripping section. Since the number of stages is small mixer-settlers would be well suited for this purpose.

Kokoelma Jerusalemin kuningaskunnan vaiheista

Kirjallisuusarvostelu

Utilization of steelmaking waste materials for production of calcium carbonate (CaCO3)

The steel industry produces, besides steel, also solid mineral by-products or slags, while it emits large quantities of carbon dioxide (CO2). Slags consist of various silicates and oxides which are formed in chemical reactions between the iron ore and the fluxing agents during the high temperature processing at the steel plant. Currently, these materials are recycled in the ironmaking processes, used as aggregates in construction, or landfilled as waste. The utilization rate of the steel slags can be increased by selectively extracting components from the mineral matrix. As an example, aqueous solutions of ammonium salts such as ammonium acetate, chloride and nitrate extract calcium quite selectively already at ambient temperature and pressure conditions. After the residual solids have been separated from the solution, calcium carbonate can be precipitated by feeding a CO2 flow through the solution. Precipitated calcium carbonate (PCC) is used in different applications as a filler material. Its largest consumer is the papermaking industry, which utilizes PCC because it enhances the optical properties of paper at a relatively low cost. Traditionally, PCC is manufactured from limestone, which is first calcined to calcium oxide, then slaked with water to calcium hydroxide and finally carbonated to PCC. This process emits large amounts of CO2, mainly because of the energy-intensive calcination step. This thesis presents research work on the scale-up of the above-mentioned ammonium salt based calcium extraction and carbonation method, named Slag2PCC. Extending the scope of the earlier studies, it is now shown that the parameters which mainly affect the calcium utilization efficiency are the solid-to-liquid ratio of steel slag and the ammonium salt solvent solution during extraction, the mean diameter of the slag particles, and the slag composition, especially the fractions of total calcium, silicon, vanadium and iron as well as the fraction of free calcium oxide. Regarding extraction kinetics, slag particle size, solid-to-liquid ratio and molar concentration of the solvent solution have the largest effect on the reaction rate. Solvent solution concentrations above 1 mol/L NH4Cl cause leaching of other elements besides calcium. Some of these such as iron and manganese result in solution coloring, which can be disadvantageous for the quality of the PCC product. Based on chemical composition analysis of the produced PCC samples, however, the product quality is mainly similar as in commercial products. Increasing the novelty of the work, other important parameters related to assessment of the PCC quality, such as particle size distribution and crystal morphology are studied as well. As in traditional PCC precipitation process, the ratio of calcium and carbonate ions controls the particle shape; a higher value for [Ca2+]/[CO32-] prefers precipitation of calcite polymorph, while vaterite forms when carbon species are present in excess. The third main polymorph, aragonite, is only formed at elevated temperatures, above 40-50 °C. In general, longer precipitation times cause transformation of vaterite to calcite or aragonite, but also result in particle agglomeration. The chemical equilibrium of ammonium and calcium ions and dissolved ammonia controlling the solution pH affects the particle sizes, too. Initial pH of 12-13 during the carbonation favors nonagglomerated particles with a diameter of 1 μm and smaller, while pH values of 9-10 generate more agglomerates of 10-20 μm. As a part of the research work, these findings are implemented in demonstrationscale experimental process setups. For the first time, the Slag2PCC technology is tested in scale of ~70 liters instead of laboratory scale only. Additionally, design of a setup of several hundreds of liters is discussed. For these purposes various process units such as inclined settlers and filters for solids separation, pumps and stirrers for material transfer and mixing as well as gas feeding equipment are dimensioned and developed. Overall emissions reduction of the current industrial processes and good product quality as the main targets, based on the performed partial life cycle assessment (LCA), it is most beneficial to utilize low concentration ammonium salt solutions for the Slag2PCC process. In this manner the post-treatment of the products does not require extensive use of washing and drying equipment, otherwise increasing the CO2 emissions of the process. The low solvent concentration Slag2PCC process causes negative CO2 emissions; thus, it can be seen as a carbon capture and utilization (CCU) method, which actually reduces the anthropogenic CO2 emissions compared to the alternative of not using the technology. Even if the amount of steel slag is too small for any substantial mitigation of global warming, the process can have both financial and environmental significance for individual steel manufacturers as a means to reduce the amounts of emitted CO2 and landfilled steel slag. Alternatively, it is possible to introduce the carbon dioxide directly into the mixture of steel slag and ammonium salt solution. The process would generate a 60-75% pure calcium carbonate mixture, the remaining 25-40% consisting of the residual steel slag. This calcium-rich material could be re-used in ironmaking as a fluxing agent instead of natural limestone. Even though this process option would require less process equipment compared to the Slag2PCC process, it still needs further studies regarding the practical usefulness of the products. Nevertheless, compared to several other CO2 emission reduction methods studied around the world, the within this thesis developed and studied processes have the advantage of existing markets for the produced materials, thus giving also a financial incentive for applying the technology in practice.

Becoming Locals in a Borderland of Exiles. Sense of Place in the Stories of Lithuania Minor Dwellers

This thesis deals with sense of place, the relation that we construct with our dwelling and the surrounding environment. The topic belongs to the field of human geography. Sense of place is deeply intertwined with the ideas of feeling at home and having a place where to return. I argue that narratives of life experience help us relate to the places we inhabit, go through, leave. My analysis concerns Lithuania Minor, the Lithuanian region lying by the border with Kaliningrad, and focuses in particular on Vilkyškiai, a village in the municipality of Pagėgiai. Most of the area’s original population disappeared in the war. After 1945, people from all over the country and the USSR settled here. This raised the prickly question of who belongs to the borderland. Refugees, migrants and settlers allow us to observe closely the development of sense of place and its main constituents. Through this analysis, I challenge the idea of people’s natural rights to places and shows how time, engagement in local-based cultural activities and recollection help foreigners become locals. To grasp the locals’ sense of place, I collected open, light-structured interviews and applied some elements of semantic analysis to interpret the materials. From my research, it emerges that the cultivation of the region’s cultural heritage and the practice of storytelling were crucial in making the respondents feel at home. Leaving aside all legalistic claims concerning the issue, I suggest that people belong to the land they dwell. I believe that their sense of place deserves consideration from the State and the other actors seeing them as migrants.