Developing of AC magnetometer and investigation of magnetic properties of LSMO

In this work AC magnetometer was developed and primary test measurements were performed for temperature range from 77 K up to 350 K in frequency range from 1 kHz up to 20 kHz. In the course of the present work dependencies of magnetization on temperature for Lao7Sr03Mni _yFeyO3 with y = 0.15, 0.20, 0.25 were obtained in DC magnetic field using SQUID magnetometer and in AC magnetic field using the developed AC magnetometer. Lai.XSrXMnO3 (LSMO) compounds belong to the class of Mn perovskites, which demonstrate very high degree of spin polarization. These materials are of great importance for nowadays applications in spintronics, where spin polarized electron transport is used. Spin glass like behavior was found as a characteristic feature of these solid solutions with the freezing temperature in the range 65 — 210 K.

Magnetic properties of ZnGeP2:Mn

In this work magnetic properties of ZnGeP2:Mn were investigated in DC magnetic field with SQUID magnetometer in the temperature range from 3 K up to 400 K and in AC magnetic field with AC magnetometer in the temperature range from 77 K up to 350 K in frequency range from 500 Hz up to 18 KHz. Three ZnGeP2:Mn samples were studied with Mn concentration c = 1.5 % mass, 3 % mass and 3.5 % mass.

Ferromagnetic properties of pyrolytic nanocarbon

The work reported in this thesis is dedicated to irreversible magnetic properties in pyrolytic nanocarbon samples. Based on atomic force microscope images, the samples consist of carbon clusters with radius 30..120 nm. These are treated as single-domain nanoparticles. Magnetic hysteresis, field cooled, zero field cooled and thermoremanent magnetization measurements were performed using an RF SQUID magnetometer and ferromagnetic behaviour was observed. Analysis suggests that the ferromagnetic ordering is associated with defects in a thin surface layer, whose thickness is independent of particle size. Critical radius for single-domain particles, critical radius for coherent rotation, magnetic layer thickness, distance between elementary magnetic moments, saturation magnetization, exchange stiffness constant and anisotropy energy density are also presented.

Magnetic properties of multi-walled nanotubes on polysterene substrate

Nanotubes are one of the most perspective materials in modern nanotechologies. It makes present investigation very actual. In this work magnetic properties of multi-walled nanotubes on polystyrene substrate are investigated by using quantum magnetometer SQUID. Main purpose was to obtain magnetic field and temperature dependences of magnetization and to compare them to existing theoretical models of magnetism in carbon-bases structures. During data analysis a mathematical algorithm for obtained data filtration was developed because measurement with quantum magnetometer assume big missives of number data, which contain accidental errors. Nature of errors is drift of SQUID signal, errors of different parts of measurement station. Nanotube samples on polystyrene substrate were studied with help of atomic force microscope. On the surface traces of nanotube were found contours, which were oriented in horizontal plane. This feature was caused by rolling method for samples. Detailed comparison of obtained dependences with information of other researches on this topic allows to obtain some conclusions about nature of magnetism in the samples. It emphasizes importance and actuality of this scientific work.

Hyperfine interactions in the new Fe-based superconducting structures and related magnetic phases

This thesis is devoted to the study of the hyperfine properties in iron-based superconductors and the synthesis of these compounds and related phases. During this work polycrystalline chalcogenide samples with stoichiometry 1:1 (FeTe1-χSχ, FeSe1-x) and pnictide samples with stoichiometry 1:2:2 (BaFe2(As1-χPχ)2, EuFe2(As1-x Px)2) were synthesized by solid-state reaction methods in vacuum and in a protecting Ar atmosphere. In several cases post-annealing in oxygen atmosphere was employed. The purity and superconducting properties of the obtained samples were checked with X-ray diffraction, SQUID and resistivity measurements. For studies of the magnetic properties of the investigated samples Mössbauer spectroscopy was used. Using low-temperature measurements around Tc and various values of the source velocity the hyperfine interactions were obtained and the magnetic and structural properties in the normal and superconducting states could be studied. Mössbauer measurements together with XRD characterization were also used for the detection of impurity phases. DFT calculations were used for the theoretical study of Mössbauer parameters for pnictide-based ᴻsamples BaFe2(As1-xPx)2 and EuFe2(As1-xPx)2.

Magnetization studies of polystyrene/multiwall carbon nanotube composite films

Lappeenranta University of Technology School of Technology Technical Physics Evgenii Zhukov MAGNETIZATION STUDIES OF POLYSTYRENE/MULTIWALL CARBON NANOTUBE COMPOSITE FILMS Master’s thesis 2015 55 pages, 41 pictures, 9 Tables. Examiners: Professor Erkki Lähderanta D.Sc. Ivan Zakharchuk Keywords: polystyrene, multi-walled carbon nanotubes, MWCNT, composite, magnetization, SQUID. In this thesis magnetic properties of polystyrene/multiwall carbon nanotube (MWCNT) composites are investigated with Quantum Design SQUID magnetometer (MPMS XL). The surface of the composite films is studied via BRUKER Multimode 8 Atomic Force Microscope, as well. The polystyrene/MWCNT composites have been prepared by the group of professor Okotrub (Physics Chemistry of Nanomaterials laboratory, Nikolaev Institute of Inorganic Chemistry, Russia). The composite films have been prepared by solution processing and stretching method. The approximate length and inner diameter of the MWCNTs used in fabrication are 260 μm and 10 nm, respectively. The content of MWCNTs is 1 and 2.5 contents percent (wt%) for studied samples. The stretching of the samples is 30% for samples with 1 and 2.5 wt% content, and one sample with 1 wt% loading of MWCNTs is 100% stretched. MWCNTs aligned perpendicular to a silicon substrate are used as a reference sample. The magnetization field dependencies of the samples exhibit hysteresis behavior. The values of saturation magnetization of composite films are much less compared to that of the reference sample. The saturation magnetization coercitivity field value drops with decrease of MWCNT content. At high magnetic fields strong presence of diamagnetism is observed. Measurements in magnetic field parallel and perpendicular to the composite plate display anisotropy with respect to the direction of stretching. Temperature dependences of magnetization for all samples display difference between zero-field cooled and field-cooled curves of magnetization. This divergence confirms the presence of magnetic interactions in the material. The atomic force microscopy study of the composites’ surfaces revealed that they are relatively smooth and the nanotubes are aligned with the axis of stretching to some extent. 

Magnetic properties of defective graphene

In this thesis, the influence of the functionalization of graphene and graphite on their magnetic properties was investigated. The functionalization was performed by covalent attaching of a phenyl groups with three different radicals (4-bromoaniline, 4-chloroaniline and 4-nitroaniline). Magnetic properties were measured by SQUID magnetometer. Both pristine graphite and graphene showed strong diamagnetic behavior. For good quality graphite, diamagnetism was found to be temperature-dependent. All samples demonstrated noticeable paramagnetic contribution below 50 K. According to fitting experimental results with Brillouin function and Curie law, it was shown that paramagnetism is provided by small clusters of spins (superparamagnetic behavior). Moreover, the clusters size and spin concentrations were calculated. For the samples functionalized with nitroaniline the antiferromagnetic transition around 120 K was observed. To explain this behavior, a simple model was proposed. Additional analysis of the graphene quality, structure and composition of the samples was carried out by HRTEM, EDS mapping, Raman spectroscopy and X-ray diffraction techniques.

The Role of Structural Imperfections in Sr2FeMoO6 Thin Films

In this work, Sr2FeMoO6 (SFMO) thin films were studied with the main focus on their magnetic and magneto-transport properties. The fabrication process of pulsed laser deposited SFMO films was first optimized. Then the effects of strain, film thickness and substrate were thoroughly investigated. In addition to these external factors, the effect of intrinsic defects on the magnetic properties of SFMO were also clarified. Secondly, the magnetoresistivity mechanims of SFMO films were studied and a semiempirical model of the temperature dependence of resistivity was introduced. The films were grown on single crystal substrates using a ceramic target made with sol-gel method. The structural characterization of the films were carried out with X-ray diffraction, atomic force microscopy, transmission electron microscopy and high kinetic energy photoelectron spectroscopy. The magnetic properties were measured with SQUID magnetometer and the magneto-transport properties by magnetometer with a resistivity option. SFMO films with the best combination of structural and magnetic properties were grown in Ar atmosphere at 1050 °C . Their magnetic properties could not be improved by the ex situ post-annealing treatments aside from the treatments in ultra-high vacuum conditions. The optimal film thickness was found to be around 150 nm and only small improvement in the magnetic properties with decreasing strain was observed. Instead, the magnetic properties were observed to be highly dependent on the choice of the substrate due to the lattice mismatch induced defects, which are best avoided by using the SrTiO3 substrate. The large difference in the Curie temperature and the saturation magnetization between the SFMO thin film and polycrystalline bulk samples was connected to the antisite disorder and oxygen vacancies. Thus, the Curie temperature of SFMO thin films could be improved by increasing the amount of oxygen vacancies for example with ultra-high vacuum treatments or improving the B-site ordering by further optimization of the deposition parameters. The magneto-transport properties of SFMO thin films do not follow any conventional models, but the temperature dependence of resistivity was succesfully described with a model of two spin channel system. Also, evidences that the resistivity-temperature behaviour of SFMO thin films is dominated by the structural defects, which reduce the band gap in the majority spin band were found. Moreover, the magnetic field response of the resistivity in SFMO thin films were found to be superposition of different mechanisms that seems to be related to the structural changes in the film.