Laser Cutting of Austenitic Stainless Steel with a High Quality Laser Beam

The thin disk and fiber lasers are new solid-state laser technologies that offer a combinationof high beam quality and a wavelength that is easily absorbed by metal surfacesand are expected to challenge the CO2 and Nd:YAG lasers in cutting of metals ofthick sections (thickness greater than 2mm). This thesis studied the potential of the disk and fiber lasers for cutting applications and the benefits of their better beam quality. The literature review covered the principles of the disk laser, high power fiber laser, CO2 laser and Nd:YAG laser as well as the principle of laser cutting. The cutting experiments were made with thedisk, fiber and CO2 lasers using nitrogen as an assist gas. The test material was austenitic stainless steel of sheet thickness 1.3mm, 2.3mm, 4.3mm and 6.2mm for the disk and fiber laser cutting experiments and sheet thickness of 1.3mm, 1.85mm, 4.4mm and 6.4mm for the CO2 laser cutting experiments. The experiments focused on the maximum cutting speeds with appropriate cut quality. Kerf width, cutedge perpendicularity and surface roughness were the cut characteristics used to analyze the cut quality. Attempts were made to draw conclusions on the influence of high beam quality on the cutting speed and cut quality. The cutting speeds were enormous for the disk and fiber laser cutting experiments with the 1.3mm and 2.3mm sheet thickness and the cut quality was good. The disk and fiber laser cutting speeds were lower at 4.3mm and 6.2mm sheet thickness but there was still a considerable percentage increase in cutting speeds compared to the CO2 laser cutting speeds at similar sheet thickness. However, the cut quality for 6.2mm thickness was not very good for the disk and fiber laser cutting experiments but could probably be improved by proper selection of cutting parameters.

Characterisation of Laser Beam and Paper Material Interaction

It is known already from 1970´s that laser beam is suitable for processing paper materials. In this thesis, term paper materials mean all wood-fibre based materials, like dried pulp, copy paper, newspaper, cardboard, corrugated board, tissue paper etc. Accordingly, laser processing in this thesis means all laser treatments resulting material removal, like cutting, partial cutting, marking, creasing, perforation etc. that can be used to process paper materials. Laser technology provides many advantages for processing of paper materials: non-contact method, freedom of processing geometry, reliable technology for non-stop production etc. Especially packaging industry is very promising area for laser processing applications. However, there are only few industrial laser processing applications worldwide even in beginning of 2010´s. One reason for small-scale use of lasers in paper material manufacturing is that there is a shortage of published research and scientific articles. Another problem, restraining the use of laser for processing of paper materials, is colouration of paper material i.e. the yellowish and/or greyish colour of cut edge appearing during cutting or after cutting. These are the main reasons for selecting the topic of this thesis to concern characterization of interaction of laser beam and paper materials. This study was carried out in Laboratory of Laser Processing at Lappeenranta University of Technology (Finland). Laser equipment used in this study was TRUMPF TLF 2700 carbon dioxide laser that produces a beam with wavelength of 10.6 μm with power range of 190-2500 W (laser power on work piece). Study of laser beam and paper material interaction was carried out by treating dried kraft pulp (grammage of 67 g m-2) with different laser power levels, focal plane postion settings and interaction times. Interaction between laser beam and dried kraft pulp was detected with different monitoring devices, i.e. spectrometer, pyrometer and active illumination imaging system. This way it was possible to create an input and output parameter diagram and to study the effects of input and output parameters in this thesis. When interaction phenomena are understood also process development can be carried out and even new innovations developed. Fulfilling the lack of information on interaction phenomena can assist in the way of lasers for wider use of technology in paper making and converting industry. It was concluded in this thesis that interaction of laser beam and paper material has two mechanisms that are dependent on focal plane position range. Assumed interaction mechanism B appears in range of average focal plane position of 3.4 mm and 2.4 mm and assumed interaction mechanism A in range of average focal plane position of 0.4 mm and -0.6 mm both in used experimental set up. Focal plane position 1.4 mm represents midzone of these two mechanisms. Holes during laser beam and paper material interaction are formed gradually: first small hole is formed to interaction area in the centre of laser beam cross-section and after that, as function of interaction time, hole expands, until interaction between laser beam and dried kraft pulp is ended. By the image analysis it can be seen that in beginning of laser beam and dried kraft pulp material interaction small holes off very good quality are formed. It is obvious that black colour and heat affected zone appear as function of interaction time. This reveals that there still are different interaction phases within interaction mechanisms A and B. These interaction phases appear as function of time and also as function of peak intensity of laser beam. Limit peak intensity is the value that divides interaction mechanism A and B from one-phase interaction into dual-phase interaction. So all peak intensity values under limit peak intensity belong to MAOM (interaction mechanism A one-phase mode) or to MBOM (interaction mechanism B onephase mode) and values over that belong to MADM (interaction mechanism A dual-phase mode) or to MBDM (interaction mechanism B dual-phase mode). Decomposition process of cellulose is evolution of hydrocarbons when temperature is between 380- 500°C. This means that long cellulose molecule is split into smaller volatile hydrocarbons in this temperature range. As temperature increases, decomposition process of cellulose molecule changes. In range of 700-900°C, cellulose molecule is mainly decomposed into H2 gas; this is why this range is called evolution of hydrogen. Interaction in this range starts (as in range of MAOM and MBOM), when a small good quality hole is formed. This is due to “direct evaporation” of pulp via decomposition process of evolution of hydrogen. And this can be seen can be seen in spectrometer as high intensity peak of yellow light (in range of 588-589 nm) which refers to temperature of ~1750ºC. Pyrometer does not detect this high intensity peak since it is not able to detect physical phase change from solid kraft pulp to gaseous compounds. As interaction time between laser beam and dried kraft pulp continues, hypothesis is that three auto ignition processes occurs. Auto ignition of substance is the lowest temperature in which it will spontaneously ignite in a normal atmosphere without an external source of ignition, such as a flame or spark. Three auto ignition processes appears in range of MADM and MBDM, namely: 1. temperature of auto ignition of hydrogen atom (H2) is 500ºC, 2. temperature of auto ignition of carbon monoxide molecule (CO) is 609ºC and 3. temperature of auto ignition of carbon atom (C) is 700ºC. These three auto ignition processes leads to formation of plasma plume which has strong emission of radiation in range of visible light. Formation of this plasma plume can be seen as increase of intensity in wavelength range of ~475-652 nm. Pyrometer shows maximum temperature just after this ignition. This plasma plume is assumed to scatter laser beam so that it interacts with larger area of dried kraft pulp than what is actual area of beam cross-section. This assumed scattering reduces also peak intensity. So result shows that assumably scattered light with low peak intensity is interacting with large area of hole edges and due to low peak intensity this interaction happens in low temperature. So interaction between laser beam and dried kraft pulp turns from evolution of hydrogen to evolution of hydrocarbons. This leads to black colour of hole edges.

Thick Section Laser Beam Welding of Structural Steels: Methods for Improving Welding Efficiency

Laser beam welding (LBW) is applicable for a wide range of industrial sectors and has a history of fifty years. However, it is considered an unusual method with applications typically limited to welding of thin sheet metal. With a new generation of high power lasers there has been a renewed interest in thick section LBW (also known as keyhole laser welding). There was a growing body of publications during 2001-2011 that indicates an increasing interest in laser welding for many industrial applications, and in last ten years, an increasing number of studies have examined the ways to increase the efficiency of the process. Expanding the thickness range and efficiency of LBW makes the process a possibility for industrial applications dealing with thick metal welding: shipbuilding, offshore structures, pipelines, power plants and other industries. The advantages provided by LBW, such as high process speed, high productivity, and low heat input, may revolutionize these industries and significantly reduce the process costs. The research to date has focused on either increasing the efficiency via optimizing process parameters, or on the process fundamentals, rather than on process and workpiece modifications. The argument of this thesis is that the efficiency of the laser beam process can be increased in a straightforward way in the workshop conditions. Throughout this dissertation, the term “efficiency” is used to refer to welding process efficiency, specifically, an increase in efficiency refers an increase in weld’s penetration depth without increasing laser power level or decreasing welding speed. These methods are: modifications of the workpiece – edge surface roughness and air gap between the joining plates; modification of the ambient conditions – local reduction of the pressure in the welding zone; modification of the welding process – preheating of the welding zone. Approaches to improve the efficiency are analyzed and compared both separately and combined. These experimentally proven methods confirm previous findings and contribute additional evidence which expand the opportunities for laser beam welding applications. The focus of this research was primarily on the effects of edge surface roughness preparation and pre-set air gap between the plates on weld quality and penetration depth. To date, there has been no reliable evidence that such modifications of the workpiece give a positive effect on the welding efficiency. Other methods were tested in combination with the two methods mentioned above. The most promising - combining with reduced pressure method - resulted in at least 100% increase in efficiency. The results of this thesis support the idea that joining those methods in one modified process will provide the modern engineering with a sufficient tool for many novel applications with potential benefits to a range of industries.

Suojakaasuseoksen koostumuksen vaikutus CO2-laser-MAG-hybridihitsauksessa

Hitsaavassa teollisuudessa kilpailukyvyn säilyttäminen edellyttää hitsauksen tehokkuuden nostoa. Niinpä metalliteollisuus etsii kuumeisesti uusia yhä tehokkaampia hitsausmenetelmiä. CO2-laserin ja MAG:in yhdistelmän muodostamalla hybridihitsauksella saadaan aikaan syvä tunkeuma kuten laserhitsauksessa, mutta sallitaan laserhitsausta väljemmät railotoleranssit. Samalla muodonmuutokset vähenevät huomattavasti verrattuna perinteiseen kaarihitsaukseen. Kaariavusteisessa laserhitsauksessa yhdistetään laserhitsaukseen perinteinen kaarihitsaus eli MIG/MAG-, TIG- tai plasmahitsaus. Menetelmää voidaan kutsua myös hybridihitsaukseksi ja sillä hyödynnetään molempien prosessien edut välttyen yksittäisten prosessien haitoilta. Prosessin haittapuolena on parametrien suuri määrä, joka on rajoittanut menetelmän käyttöönottoa. Diplomityössä tutkittiin suojakaasuseoksen koostumuksen vaikutusta rakenneteräksen CO2-laser-MAG-hybridihitsauksessa. Laserhitsauksen ja MAG-hitsauksen suojakaasuvirtaukset yhdistettiin siten, että heliumseosteinen suojakaasu tuotiin MAG-polttimen kaasukuvun kautta. Suojakaasun heliumpitoisuus nostettiin niin korkeaksi, että estettiin laserhitsauksen muodostaman plasman syntyminen. Samalla hitsauskokeissa opittiin paremmin ymmärtämään prosessia ja sen parametrien riippuvuutta toisiinsa. Tutkitut suojakaasuseokset koostuivat heliumista, argonista ja hiilidioksidista. Hitsauskokeiden perusteella havaittiin, että suojakaasuseoksen optimaalinen heliumpitoisuus on 40-50 %. Tällöin laserin tunkeumaa häiritsevää plasmapilveä ei synny ja prosessi on stabiili. Päittäisliitosten hitsauksessa suojakaasuseoksen 2 %:n CO2-pitoisuudella saadaan aikaan hyvin vähän huokosia sisältävä hitsi, jonka tunkeumaprofiilin muoto ja liittymä perusaineeseen on juoheva. Pienaliitoksilla 7 %:n CO2-pitoisuudella prosessi pysyy stabiilina ja vähäroiskeisena. Tunkeuma hieman levenee hitsin keskeltä ja hitsin liittyminen perusaineeseen on juoheva.CO2-laser-MAG-hybridihitsauksella aikaansaadaan laadukkaita hitsejä taloudellisesti, mikäli käytetyt parametrit ovat oikein valittuja. Parametrit on sovitettava jokaiseen hitsaustapaukseen erikseen, eikä niitä välttämättä voida suoraan käyttää toisessa tapauksessa.

The effects of some variables on CO2 laser-MAG hybrid welding

The CO2-laser-MAG hybrid welding process has been shown to be a productive choice for the welding industry, being used in e.g. the shipbuilding, pipe and beam manufacturing, and automotive industries. It provides an opportunity to increase the productivity of welding of joints containing air gaps compared with autogenous laser beam welding, with associated reductions in distortion and marked increases in welding speeds and penetration in comparison with both arc and autogenous laser welding. The literature study indicated that the phenomena of laser hybrid welding are mostly being studied using bead-on-plate welding or zero air gap configurations. This study shows it very clearly that the CO2 laser-MAG hybrid welding process is completely different, when there is a groove with an air gap. As in case of industrial use it is excepted that welding is performed for non-zero grooves, this study is of great importance for industrial applications. The results of this study indicate that by using a 6 kW CO2 laser-MAG hybrid welding process, the welding speed may also be increased if an air gap is present in the joint. Experimental trials indicated that the welding speed may be increased by 30-82% when compared with bead-on-plate welding, or welding of a joint with no air gap i.e. a joint prepared as optimum for autogenous laser welding. This study demonstrates very clearly, that the separation of the different processes, as well as the relative configurations of the processes (arc leading or trailing) affect welding performance significantly. These matters influence the droplet size and therefore the metal transfer mode, which in turn determined the resulting weld quality and the ability to bridge air gaps. Welding in bead-onplate mode, or of an I butt joint containing no air gap joint is facilitated by using a leading torch. This is due to the preheating effect of the arc, which increases the absorptivity of the work piece to the laser beam, enabling greater penetration and the use of higher welding speeds. With an air gap present, air gap bridging is more effectively achieved by using a trailing torch because of the lower arc power needed, the wider arc, and the movement of droplets predominantly towards the joint edges. The experiments showed, that the mode of metal transfer has a marked effect on gap bridgeability. Transfer of a single droplet per arc pulse may not be desirable if an air gap is present, because most of the droplets are directed towards the middle of the joint where no base material is present. In such cases, undercut is observed. Pulsed globular and rotational metal transfer modes enable molten metal to also be transferred to the joint edges, and are therefore superior metal transfer modes when bridging air gaps. It was also found very obvious, that process separation is an important factor in gap bridgeability. If process separation is too large, the resulting weld often exhibits sagging, or no weld may be formed at all as a result of the reduced interaction between the component processes. In contrast, if the processes are too close to one another, the processing region contains excess molten metal that may create difficulties for the keyhole to remain open. When the distance is optimised - i.e. a separation of 0-4 mm in this study, depending on the welding speed and beam-arc configuration - the processes act together, creating beneficial synergistic effects. The optimum process separation when using a trailing torch was found to be shorter (0-2 mm) than when a leading torch is used (2-4 mm); a result of the facilitation of weld pool motion when the latter configuration is adopted. This study demonstrates, that the MAG process used has a strong effect on the CO2-laser-MAG hybrid welding process. The laser beam welding component is relatively stable and easy to manage, with only two principal processing parameters (power and welding speed) needing to be adjusted. In contrast, the MAG process has a large number of processing parameters to optimise, all of which play an important role in the interaction between the laser beam and the arc. The parameters used for traditional MAG welding are often not optimal in achieving the most appropriate mode of metal transfer, and weld quality in laser hybrid welding, and must be optimised if the full range of benefits provided by hybrid welding are to be realised.

Performance of high power fibre laser cutting of thick-section steel and mediumsection aluminium

Cutting of thick section stainless steel and mild steel, and medium section aluminium using the high power ytterbium fibre laser has been experimentally investigated in this study. Theoretical models of the laser power requirement for cutting of a metal workpiece and the melt removal rate were also developed. The calculated laser power requirement was correlated to the laser power used for the cutting of 10 mm stainless steel workpiece and 15 mm mild steel workpiece using the ytterbium fibre laser and the CO2 laser. Nitrogen assist gas was used for cutting of stainless steel and oxygen was used for mild steel cutting. It was found that the incident laser power required for cutting at a given cutting speed was lower for fibre laser cutting than for CO2 laser cutting indicating a higher absorptivity of the fibre laser beam by the workpiece and higher melting efficiency for the fibre laser beam than for the CO2 laser beam. The difficulty in achieving an efficient melt removal during high speed cutting of the 15 mmmild steel workpiece with oxygen assist gas using the ytterbium fibre laser can be attributed to the high melting efficiency of the ytterbium fibre laser. The calculated melt flow velocity and melt film thickness correlated well with the location of the boundary layer separation point on the 10 mm stainless steel cut edges. An increase in the melt film thickness caused by deceleration of the melt particles in the boundary layer by the viscous shear forces results in the flow separation. The melt flow velocity increases with an increase in assist gas pressure and cut kerf width resulting in a reduction in the melt film thickness and the boundary layer separation point moves closer to the bottom cut edge. The cut edge quality was examined by visual inspection of the cut samples and measurement of the cut kerf width, boundary layer separation point, cut edge squareness (perpendicularity) deviation, and cut edge surface roughness as output quality factors. Different regions of cut edge quality in 10 mm stainless steel and 4 mm aluminium workpieces were defined for different combinations of cutting speed and laserpower.Optimization of processing parameters for a high cut edge quality in 10 mmstainless steel was demonstrated

Spectrometrical Monitoring of Laser Sintering Process of Ceramic Material

This thesis is done as a part of project called FuncMama that is a project between Technical Research Centre of Finland (VTT), Oulu University (OY), Lappeenranta University of Technology (LUT) and Finnish industrial partners. Main goal of the project is to manufacture electric and mechanical components from mixed materials using laser sintering. Aim of this study was to create laser sintered pieces from ceramic material and monitor the sintering event by using spectrometer. Spectrometer is a device which is capable to record intensity of different wavelengths in relation with time. In this study the monitoring of laser sintering was captured with the equipment which consists of Ocean Optics spectrometer, optical fiber and optical lens (detector head). Light from the sintering process hit first to the lens system which guides the light in to the optical fibre. Optical fibre transmits the light from the sintering process to the spectrometer where wavelengths intensity level information is detected. The optical lens of the spectrometer was rigidly set and did not move along with the laser beam. Data which was collected with spectrometer from the laser sintering process was converted with Excel spreadsheet program for result’s evaluation. Laser equipment used was IPG Photonics pulse fibre laser. Laser parameters were kept mainly constant during experimental part and only sintering speed was changed. That way it was possible to find differences in the monitoring results without fear of too many parameters mixing together and affecting to the conclusions. Parts which were sintered had one layer and size of 5 x 5 mm. Material was CT2000 – tape manufactured by Heraeus which was later on post processed to powder. Monitoring of different sintering speeds was tested by using CT2000 reference powder. Moreover tests how different materials effect to the process monitoring were done by adding foreign powder Du Pont 951 which had suffered in re-grinding and which was more reactive than CT2000. By adding foreign material it simulates situation where two materials are accidently mixed together and it was studied if that can be seen with the spectrometer. It was concluded in this study that with the spectrometer it is possible to detect changes between different laser sintering speeds. When the sintering speed is lowered the intensity level of light is higher from the process. This is a result of higher temperature at the sintering spot and that can be noticed with the spectrometer. That indicates it could be possible to use spectrometer as a tool for process observation and support the idea of having system that can help setting up the process parameter window. Also important conclusion was how well the adding of foreign material could be seen with the spectrometer. When second material was added a significant intensity level raise could be noticed in that part where foreign material was mixed. That indicates it is possible to see if there are any variations in the material or if there are more materials mixed together. Spectrometric monitoring of laser sintering could be useful tool for process window observation and temperature controlling of the sintering process. For example if the process window for specific material is experimentally determined to get wanted properties and satisfying sintering speed. It is possible if the data is constantly recorded that the results can show faults in the part texture between layers. Changes between the monitoring data and the experimentally determined values can then indicate changes in the material being generated by material faults or by wrong process parameters. The results of this study show that spectrometer could be one possible tool for monitoring. But to get in that point where this all can be made possible much more researching is needed.

Surface transformation hardening of carbon steel with high power fiber laser

This study investigated the surface hardening of steels via experimental tests using a multi-kilowatt fiber laser as the laser source. The influence of laser power and laser power density on the hardening effect was investigated. The microhardness analysis of various laser hardened steels was done. A thermodynamic model was developed to evaluate the thermal process of the surface treatment of a wide thin steel plate with a Gaussian laser beam. The effect of laser linear oscillation hardening (LLOS) of steel was examined. An as-rolled ferritic-pearlitic steel and a tempered martensitic steel with 0.37 wt% C content were hardened under various laser power levels and laser power densities. The optimum power density that produced the maximum hardness was found to be dependent on the laser power. The effect of laser power density on the produced hardness was revealed. The surface hardness, hardened depth and required laser power density were compared between the samples. Fiber laser was briefly compared with high power diode laser in hardening medium-carbon steel. Microhardness (HV0.01) test was done on seven different laser hardened steels, including rolled steel, quenched and tempered steel, soft annealed alloyed steel and conventionally through-hardened steel consisting of different carbon and alloy contents. The surface hardness and hardened depth were compared among the samples. The effect of grain size on surface hardness of ferritic-pearlitic steel and pearlitic-cementite steel was evaluated. In-grain indentation was done to measure the hardness of pearlitic and cementite structures. The macrohardness of the base material was found to be related to the microhardness of the softer phase structure. The measured microhardness values were compared with the conventional macrohardness (HV5) results. A thermodynamic model was developed to calculate the temperature cycle, Ac1 and Ac3 boundaries, homogenization time and cooling rate. The equations were numerically solved with an error of less than 10-8. The temperature distributions for various thicknesses were compared under different laser traverse speed. The lag of the was verified by experiments done on six different steels. The calculated thermal cycle and hardened depth were compared with measured data. Correction coefficients were applied to the model for AISI 4340 steel. AISI 4340 steel was hardened by laser linear oscillation hardening (LLOS). Equations were derived to calculate the overlapped width of adjacent tracks and the number of overlapped scans in the center of the scanned track. The effect of oscillation frequency on the hardened depth was investigated by microscopic evaluation and hardness measurement. The homogeneity of hardness and hardened depth with different processing parameters were investigated. The hardness profiles were compared with the results obtained with conventional single-track hardening. LLOS was proved to be well suitable for surface hardening in a relatively large rectangular area with considerable depth of hardening. Compared with conventional single-track scanning, LLOS produced notably smaller hardened depths while at 40 and 100 Hz LLOS resulted in higher hardness within a depth of about 0.6 mm.

Laser-TIG–hybridihitsauksen soveltuvuustutkimus

Tässä tutkimuksessa selvitetään ilman hitsauslisäainetta tapahtuvan laser–TIG–hybridihitsausprosessin soveltuvuus 6 mm ja 8 mm paksujen päittäisliitettyjen S355 K2 ja Laser 355 MC rakenneterästen hitsaukseen. Hitsien tarkastelussa huomio kiinnitetään hitsausnopeuteen, hitsien tunkeumaan, liittämistehokkuuteen, hitsien kovuuteen ja hitsausliitoksen ulkonäköön. Muita tutkittavia asioita ovat laser-TIG-hybridihitsattujen levyjen muodonmuutokset ja suuresta hitsausnopeudesta sekä pienestä t8/5 jäähtymisajasta johtuvat mahdolliset kylmähalkeamat. Laser-TIG-hybridihitsejä verrataan robotti-MAG- ja käsin MAG-hitseihin sekä kaarihitsausstandardin SFS-EN ISO 5817 hitsiluokkien mukaisiin raja-arvoihin. Laser-TIG-hybridihitsausprosessissa TIG-valokaari mahdollistaa tasaisen ja lähes roiskeettoman hitsin ja lasersäde aikaansaa syvän tunkeuman sekä tasalaatuisen juurihitsin. Laser-TIG-hybridihitsausprosessilla 6 mm paksut S355 K2 rakenneteräslevyt on mahdollista hitsata levyn yhdeltä puolelta kerralla valmiiksi. Paksummat 8 mm levyt voidaan hitsata levyn yhdeltä tai molemmilta puolilta suoritettavalla laser-TIG-hybridihitsauksella. Laser-TIG-hybridihitsausprosessilla hitsatut hitsit ovat hyvin siistejä ja lähes roiskeettomia. Verrattaessa laser-TIG-hybridihitsausprosessia muihin hitsausprosesseihin sen voidaan todeta olevan erittäin kilpailukykyinen 6 mm paksujen päittäisliitettyjen rakenneterästen hitsaamisessa, mutta se soveltuu myös 8 mm paksujen rakenneterästen hitsaamiseen. Tutkitut hitsit täyttävät kaarihitsausstandardin SFS-EN ISO 5817 B- ja D-hitsiluokkien mukaiset raja-arvot. Vertailukokeet 6 mm paksulla S355 rakenneteräksellä osoittavat, että yhdeltä puolelta suoritettavan laser-TIG-hybridihitsauksen hitsausnopeus on robotti-MAG-hitsaukseen verrattuna yli nelinkertainen ja MAG-käsinhitsaukseen verrattuna yli viisinkertainen. Laser-TIG-hybridihitsauksessa liittämistehokkuus on noin viisinkertainen robotti-MAGhitsaukseen verrattuna. Molemmilta puolilta suoritettavalla laser-TIG-hybridihitsauksella voidaan 8 mm paksulla S355 rakenneteräksellä saavuttaa noin kolminkertainen hitsausnopeus ja liittämistehokkuus robotti-MAG-hitsaukseen verrattuna. Laser-TIG-hybridihitsauksessa TIG-kaaren tuoman lisälämmön ansiosta suurillakin hitsausnopeuksilla (1 m/min) voidaan saavuttaa edulliset kovuusarvot. Kovuusmittausten tulosten perusteella 6 mm ja 8 mm paksujen S355 K2 ja Laser 355 MC rakenneterästen hitsit eivät ylittäneet kaarihitsausstandardin määrittelemää 350 HV kovuuden enimmäisrajaa. Laser-TIG-hybridihitsauksen edullisesta lämmöntuonnista johtuen levyjen pituus- ja poikittaissuuntaiset muodonmuutokset ovat noin 80 prosenttia pienemmät kuin käsin suoritettavassa MAG-hitsauksessa. Laser-TIG-hybridihitsausprosessilla käytetään I-railoa, mutta robotti-MAG- ja käsin MAG-hitsausprosesseilla joudutaan käyttämään V-railoa, jolloin lämmöntuonti ja siitä johtuvat muodonmuutokset ovat suuremmat. Korkea liittämistehokkuus ja edullinen lämmöntuonti merkitsevät vähäisempiä muodonmuutoksia ja siten merkittäviä säästöjä työ-, materiaali- ja energiakustannuksissa. 8 mm ja sitä paksummilla S355 rakenneteräksillä levyn yhdeltä puolelta suoritettava päittäisliitoksen hitsaaminen on laser-TIG hybridihitsauksella haastavaa, koska yli 200 A:n TIG-kaarivirralla suuri metallisula aiheuttaa avaimenreiän sulkeutumisen ja avaimenreiän alaosaan muodostuu kaasukuplia. Tästä voidaan tehdä sellainen johtopäätös, että päittäisliitettävien levyjen ilmarakoa pitäisi kasvattaa niin suureksi, että avaimenreiän sulavirtaus ei pääse estymään. Yli 0,25 mm:n ilmarako edellyttää lasersäteen vaaputusta tai säteen halkaisijan kasvattamista. Ilmaraon kasvattaminen edellyttää myös lisäaineen käyttöä. Tutkimustulosten perusteella laser-TIG-hybridihitsausprosessilla voidaan saavuttaa merkittäviä etuja ja kustannussäästöjä, joten sen hyödyntämistä kannattaa harkita 8 mm ja sitä ohuempien päittäisliitettävien tuotteiden konepaja- ja tehdastuotannossa. Laser-TIGhybridihitsausprosessi soveltuu esimerkiksi seuraavien tuotteiden hitsaamiseen: päittäisliitettävät levyt, palkit, koneenosat, putket, säiliöt ja erilaiset pyörähdyskappaleet.

Characterization Of Process Efficiency Improvement In Laser Additive Manufacturing

Laser additive manufacturing (LAM), known also as 3D printing, has gained a lot of interest in past recent years within various industries, such as medical and aerospace industries. LAM enables fabrication of complex 3D geometries by melting metal powder layer by layer with laser beam. Research in laser additive manufacturing has been focused in development of new materials and new applications in past 10 years. Since this technology is on cutting edge, efficiency of manufacturing process is in center role of research of this industry. Aim of this thesis is to characterize methods for process efficiency improvements in laser additive manufacturing. The aim is also to clarify the effect of process parameters to the stability of the process and in microstructure of manufactured pieces. Experimental tests of this thesis were made with various process parameters and their effect on build pieces has been studied, when additive manufacturing was performed with a modified research machine representing EOSINT M-series and with EOS EOSINT M280. Material used was stainless steel 17-4 PH. Also, some of the methods for process efficiency improvements were tested. Literature review of this thesis presents basics of laser additive manufacturing, methods for improve the process efficiency and laser beam – material- interaction. It was observed that there are only few public studies about process efficiency of laser additive manufacturing of stainless steel. According to literature, it is possible to improve process efficiency with higher power lasers and thicker layer thicknesses. The process efficiency improvement is possible if the effect of process parameter changes in manufactured pieces is known. According to experiments carried out in this thesis, it was concluded that process parameters have major role in single track formation in laser additive manufacturing. Rough estimation equations were created to describe the effect of input parameters to output parameters. The experimental results showed that the WDA (width-depth-area of cross-sections of single track) is correlating exponentially with energy density input. The energy density input is combination of the input parameters of laser power, laser beam spot diameter and scan speed. The use of skin-core technique enables improvement of process efficiency as the core of the part is manufactured with higher laser power and thicker layer thickness and the skin with lower laser power and thinner layer thickness in order to maintain high resolution. In this technique the interface between skin and core must have overlapping in order to achieve full dense parts. It was also noticed in this thesis that keyhole can be formed in LAM process. It was noticed that the threshold intensity value of 106 W/cm2 was exceeded during the tests. This means that in these tests the keyhole formation was possible.

Laser cladding with scanning optics

Scanning optics create different types of phenomena and limitation to cladding process compared to cladding with static optics. This work concentrates on identifying and explaining the special features of laser cladding with scanning optics. Scanner optics changes cladding process energy input mechanics. Laser energy is introduced into the process through a relatively small laser spot which moves rapidly back and forth, distributing the energy to a relatively large area. The moving laser spot was noticed to cause dynamic movement in the melt pool. Due to different energy input mechanism scanner optic can make cladding process unstable if parameter selection is not done carefully. Especially laser beam intensity and scanning frequency have significant role in the process stability. The laser beam scanning frequency determines how long the laser beam affects with specific place local specific energy input. It was determined that if the scanning frequency in too low, under 40 Hz, scanned beam can start to vaporize material. The intensity in turn determines on how large package this energy is brought and if the intensity of the laser beam was too high, over 191 kW/cm2, laser beam started to vaporize material. If there was vapor formation noticed in the melt pool, the process starts to resample more laser alloying due to deep penetration of laser beam in to the substrate. Scanner optics enables more flexibility to the process than static optics. The numerical adjustment of scanning amplitude enables clad bead width adjustment. In turn scanner power modulation (where laser power is adjusted according to where the scanner is pointing) enables modification of clad bead cross-section geometry when laser power can be adjusted locally and thus affect how much laser beam melts material in each sector. Power modulation is also an important factor in terms of process stability. When a linear scanner is used, oscillating the scanning mirror causes a dwell time in scanning amplitude border area, where the scanning mirror changes the direction of movement. This can cause excessive energy input to this area which in turn can cause vaporization and process instability. This process instability can be avoided by decreasing energy in this region by power modulation. Powder feeding parameters have a significant role in terms of process stability. It was determined that with certain powder feeding parameter combinations powder cloud behavior became unstable, due to the vaporizing powder material in powder cloud. Mainly this was noticed, when either or both the scanning frequency or powder feeding gas flow was low or steep powder feeding angle was used. When powder material vaporization occurred, it created vapor flow, which prevented powder material to reach the melt pool and thus dilution increased. Also powder material vaporization was noticed to produce emission of light at wavelength range of visible light. This emission intensity was noticed to be correlated with the amount of vaporization in the powder cloud.

Defining the keyhole modes – the effects on the weld geometry and the molten pool behaviour in high power laser welding of stainless steels

Keyhole welding, meaning that the laser beam forms a vapour cavity inside the steel, is one of the two types of laser welding processes and currently it is used in few industrial applications. Modern high power solid state lasers are becoming more used generally, but not all process fundamentals and phenomena of the process are well known and understanding of these helps to improve quality of final products. This study concentrates on the process fundamentals and the behaviour of the keyhole welding process by the means of real time high speed x-ray videography. One of the problem areas in laser welding has been mixing of the filler wire into the weld; the phenomena are explained and also one possible solution for this problem is presented in this study. The argument of this thesis is that the keyhole laser welding process has three keyhole modes that behave differently. These modes are trap, cylinder and kaleidoscope. Two of these have sub-modes, in which the keyhole behaves similarly but the molten pool changes behaviour and geometry of the resulting weld is different. X-ray videography was used to visualize the actual keyhole side view profile during the welding process. Several methods were applied to analyse and compile high speed x-ray video data to achieve a clearer image of the keyhole side view. Averaging was used to measure the keyhole side view outline, which was used to reconstruct a 3D-model of the actual keyhole. This 3D-model was taken as basis for calculation of the vapour volume inside of the keyhole for each laser parameter combination and joint geometry. Four different joint geometries were tested, partial penetration bead on plate and I-butt joint and full penetration bead on plate and I-butt joint. The comparison was performed with selected pairs and also compared all combinations together.

Energy and raw material consumption analysis of powder bed fusion: case study: CNC machining and laser additive manufacturing

Laser additive manufacturing (LAM), known also as 3D printing, is a powder bed fusion (PBF) type of additive manufacturing (AM) technology used to manufacture metal parts layer by layer by assist of laser beam. The development of the technology from building just prototype parts to functional parts is due to design flexibility. And also possibility to manufacture tailored and optimised components in terms of performance and strength to weight ratio of final parts. The study of energy and raw material consumption in LAM is essential as it might facilitate the adoption and usage of the technique in manufacturing industries. The objective this thesis was find the impact of LAM on environmental and economic aspects and to conduct life cycle inventory of CNC machining and LAM in terms of energy and raw material consumption at production phases. Literature overview in this thesis include sustainability issues in manufacturing industries with focus on environmental and economic aspects. Also life cycle assessment and its applicability in manufacturing industry were studied. UPLCI-CO2PE! Initiative was identified as mostly applied exiting methodology to conduct LCI analysis in discrete manufacturing process like LAM. Many of the reviewed literature had focused to PBF of polymeric material and only few had considered metallic materials. The studies that had included metallic materials had only measured input and output energy or materials of the process and compared to different AM systems without comparing to any competitive process. Neither did any include effect of process variation when building metallic parts with LAM. Experimental testing were carried out to make dissimilar samples with CNC machining and LAM in this thesis. Test samples were designed to include part complexity and weight reductions. PUMA 2500Y lathe machine was used in the CNC machining whereas a modified research machine representing EOSINT M-series was used for the LAM. The raw material used for making the test pieces were stainless steel 316L bar (CNC machined parts) and stainless steel 316L powder (LAM built parts). An analysis of power, time, and the energy consumed in each of the manufacturing processes on production phase showed that LAM utilises more energy than CNC machining. The high energy consumption was as result of duration of production. Energy consumption profiles in CNC machining showed fluctuations with high and low power ranges. LAM energy usage within specific mode (standby, heating, process, sawing) remained relatively constant through the production. CNC machining was limited in terms of manufacturing freedom as it was not possible to manufacture all the designed sample by machining. And the one which was possible was aided with large amount of material removed as waste. Planning phase in LAM was shorter than in CNC machining as the latter required many preparation steps. Specific energy consumption (SEC) were estimated in LAM based on the practical results and assumed platform utilisation. The estimated platform utilisation showed SEC could reduce when more parts were placed in one build than it was in with the empirical results in this thesis (six parts).

CO2-laserin soveltaminen WFU-paperin reunan leikkaamiseen

Tämän diplomityön tarkoitus oli selvittää CO2-laserin soveltuvuutta paperin reunan leikkaamiseen ennen liimapuristinta nopealle modernilleWFU-paperikoneelle. Merkittävimmät leikkauskokeet tehtiin leikkaamalla paperirataa todenmukaisissa olosuhteissa koekoneella. Koeleikkauksissa tutkittiin myös päällystettyjen paperilajien CO2-laserleikkausta. Paperin reunan koeleikkauksia suoritettiin leikkauspöytää vasten sekä telaa vasten. Leikkauspöytänä käytettiin korkeapainevesileikkaimelle suunniteltua leikkauspöytää, jota paranneltiin tämän työn yhteydessä paremmin laserleikkaukselle sopivaksi. Telaa vasten suoritetuilla leikkauksilla lasertehon tarve oli suurempi verrattuna pöytää vasten leikkaukseen samalla leikkausnopeudella ja samalla paperilajilla. Laserlaitteiston mitoittaminen oikein pelkkien arkkileikkauskokeiden perusteella ei ollut mahdollista. Myös rullilla tapahtuvia leikkauskokeita tarvittiin. Pöytää vasten tapahtuvaan leikkaamiseen tarvitaan 1000 W laserlaite paperin molemmille reunoille. Tämän tehoiset laserlaitteet riittävät kaikille Changshun PK 1:n paperilajeille niiden lajikohtaiseen maksimiajonopeuteen. Testatuista kolmesta polttovälistä antoi 5" polttoväli parhaat leikkaustulokset. Polttopisteen paikka voi vaihdella ± 0.75 mm paperin pinnasta vaikuttamatta silti merkittävästi lasertehon tarpeeseen. Laserleikatun paperin reuna oli hyvälaatuinen, eikä laserleikkaus aiheuttanut paperille epätoivottuja asioita kuten mustumista.

Metallien laserporaus

Lasertarkkuusporauksella on tämän hetken teollisuudessa useita sovelluksia, kuten esimerkiksi mustesuihkukirjoittimet, dieselmoottoreiden polttoainesuuttimet, lääketieteen instrumentit, turbiinien lapojen jäähdytysreiät ja stensiilit. Tässä työssä on tutkittu laserporauksen mahdollisuuksia 99,9 % kupariin sekä EN 1.4301 ruostumattomaan teräkseen (vastaava AISI 304). Ainepaksuuksia oli käytettävissä kolmea: 0,1 mm, 0,5 mm ja 1,0 mm. Vertailun vuoksi valittiin tutkimukseen mukaan ainepaksuudeltaan 1,0 mm EN 1.4432 haponkestävää terästä (vastaava AISI 316L). Tutkimuksessa käytettiin kolmea eritehoista 1,064 µm aallonpituuden Nd:YAG – laseria ja yhtä CO2 – laseria. Poratut reiät kuvattiin elektronimikroskoopilla ja jokaisesta reiästä mitattiin halkaisija, ympyrämäisyys ja kartiokkuus. Lisäksi reiän laatua arvioitaessa tarkasteltiin purseen määrää reikien ympärillä. Tutkimus osoitti, että eri materiaaleihin voidaan porata, laserin säteen laadusta ja aallonpituudesta riippuen, hyvin erikokoisia reikiä. Kartiokkuuteen havaittiin voitavan vaikuttaa polttopisteen paikkaa siirtämällä.