Flash Memory Cells Reliability Parameters Investigation

The present work is a part of the large project with purpose to qualify the Flash memory for automotive application using a standardized test and measurement flow. High memory reliability and data retention are the most critical parameters in this application. The current work covers the functional tests and data retention test. The purpose of the data retention test is to obtain the data retention parameters of the designed memory, i.e. the maximum time of information storage at specified conditions without critical charge leakage. For this purpose the charge leakage from the cells, which results in decrease of cells threshold voltage, was measured after a long-time hightemperature treatment at several temperatures. The amount of lost charge for each temperature was used to calculate the Arrhenius constant and activation energy for the discharge process. With this data, the discharge of the cells at different temperatures during long time can be predicted and the probability of data loss after years can be calculated. The memory chips, investigated in this work, were 0.035 μm CMOS Flash memory testchips, designed for further use in the Systems-on-Chips for automotive electronics.

Methods to test gas tightness of packages

One of the primary goals for food packages is to protect food against harmful environment, especially oxygen and moisture. The gas transmission rate is the total gas transport through the package, both by permeation through the package material and by leakage through pinholes and cracks. The shelf life of a product can be extended, if the food is stored in a gas tight package. Thus there is a need to test gas tightness of packages. There are several tightness testing methods, and they can be broadly divided into destructive and nondestructive methods. One of the most sensitive methods to detect leaks is by using a non destructive tracer gas technique. Carbon dioxide, helium and hydrogen are the most commonly used tracer gases. Hydrogen is the lightest and the smallest of all gases, which allows it to escape rapidly from the leak areas. The low background concentration of H2 in air (0.5 ppm) enables sensitive leak detection. With a hydrogen leak detector it is also possible to locate leaks. That is not possible with many other tightness testing methods. The experimental work has been focused on investigating the factors which affect the measurement results with the H2leak detector. Also reasons for false results were searched to avoid them in upcoming measurements. From the results of these experiments, the appropriate measurement practice was created in order to have correct and repeatable results. The most important thing for good measurement results is to keep the probe of the detector tightly against the leak. Because of its high diffusion rate, the HZ concentration decreases quickly if holding the probe further away from the leak area and thus the measured H2 leaks would be incorrect and small leaks could be undetected. In the experimental part hydrogen, oxygen and water vapour transmissions through laser beam reference holes (diameters 1 100 μm) were also measured and compared. With the H2 leak detector it was possible to detect even a leakage through 1 μm (diameter) within a few seconds. Water vapour did not penetrate even the largest reference hole (100 μm), even at tropical conditions (38 °C, 90 % RH), whereas some O2 transmission occurred through the reference holes larger than 5 μm. Thus water vapour transmission does not have a significant effect on food deterioration, if the diameter of the leak is less than 100 μm, but small leaks (5 100 μm) are more harmful for the food products, which are sensitive to oxidation.

Simulation and material calibration of ultra high strength steel (UHSS) S960 welded joint under static tensile test utilizing finite element method (FEM)

The aim of this work was to calibrate the material properties including strength and strain values for different material zones of ultra-high strength steel (UHSS) welded joints under monotonic static loading. The UHSS is heat sensitive and softens by heat due to welding, the affected zone is heat affected zone (HAZ). In this regard, cylindrical specimens were cut out from welded joints of Strenx® 960 MC and Strenx® Tube 960 MH, were examined by tensile test. The hardness values of specimens’ cross section were measured. Using correlations between hardness and strength, initial material properties were obtained. The same size specimen with different zones of material same as real specimen were created and defined in finite element method (FEM) software with commercial brand Abaqus 6.14-1. The loading and boundary conditions were defined considering tensile test values. Using initial material properties made of hardness-strength correlations (true stress-strain values) as Abaqus main input, FEM is utilized to simulate the tensile test process. By comparing FEM Abaqus results with measured results of tensile test, initial material properties will be revised and reused as software input to be fully calibrated in such a way that FEM results and tensile test results deviate minimum. Two type of different S960 were used including 960 MC plates, and structural hollow section 960 MH X-joint. The joint is welded by BöhlerTM X96 filler material. In welded joints, typically the following zones appear: Weld (WEL), Heat affected zone (HAZ) coarse grained (HCG) and fine grained (HFG), annealed zone, and base material (BaM). Results showed that: The HAZ zone is softened due to heat input while welding. For all the specimens, the softened zone’s strength is decreased and makes it a weakest zone where fracture happens while loading. Stress concentration of a notched specimen can represent the properties of notched zone. The load-displacement diagram from FEM modeling matches with the experiments by the calibrated material properties by compromising two correlations of hardness and strength.