Non-resorbable glass fibre-reinforced composite with porous surface as bone substitute material: Experimental studies in vitro and in vivo focused on bone-implant interface

The development of load-bearing osseous implant with desired mechanical and surface properties in order to promote incorporation with bone and to eliminate risk of bone resorption and implant failure is a very challenging task. Bone formation and resoption processes depend on the mechanical environment. Certain stress/strain conditions are required to promote new bone growth and to prevent bone mass loss. Conventional metallic implants with high stiffness carry most of the load and the surrounding bone becomes virtually unloaded and inactive. Fibre-reinforced composites offer an interesting alternative to metallic implants, because their mechanical properties can be tailored to be equal to those of bone, by the careful selection of matrix polymer, type of fibres, fibre volume fraction, orientation and length. Successful load transfer at bone-implant interface requires proper fixation between the bone and implant. One promising method to promote fixation is to prepare implants with porous surface. Bone ingrowth into porous surface structure stabilises the system and improves clinical success of the implant. The experimental part of this work was focused on polymethyl methacrylate (PMMA) -based composites with dense load-bearing core and porous surface. Three-dimensionally randomly orientated chopped glass fibres were used to reinforce the composite. A method to fabricate those composites was developed by a solvent treatment technique and some characterisations concerning the functionality of the surface structure were made in vitro and in vivo. Scanning electron microscope observations revealed that the pore size and interconnective porous architecture of the surface layer of the fibre-reinforced composite (FRC) could be optimal for bone ingrowth. Microhardness measurements showed that the solvent treatment did not have an effect on the mechanical properties of the load-bearing core. A push-out test, using dental stone as a bone model material, revealed that short glass fibre-reinforced porous surface layer is strong enough to carry load. Unreacted monomers can cause the chemical necrosis of the tissue, but the levels of leachable resisidual monomers were considerably lower than those found in chemically cured fibre-reinforced dentures and in modified acrylic bone cements. Animal experiments proved that surface porous FRC implant can enhance fixation between bone and FRC. New bone ingrowth into the pores was detected and strong interlocking between bone and the implant was achieved.

Development of porous glass-fiber reinforced composite for bone implants. Evaluation of antimicrobial effect and implant fixation

Cranial bone reconstructions are necessary for correcting large skull bone defects due to trauma, tumors, infections and craniotomies. Traditional synthetic implant materials include solid or mesh titanium, various plastics and ceramics. Recently, biostable glass-fiber reinforced composites (FRC), which are based on bifunctional methacrylate resin, were introduced as novel implant solution. FRCs were originally developed and clinically used in dental applications. As a result of further in vitro and in vivo testing, these composites were also approved for clinical use in cranial surgery. To date, reconstructions of large bone defects were performed in 35 patients. This thesis is dedicated to the development of a novel FRC-based implant for cranial reconstructions. The proposed multi-component implant consists of three main parts: (i) porous FRC structure; (ii) bioactive glass granules embedded between FRC layers and (iii) a silver-polysaccharide nanocomposite coating. The porosity of the FRC structure should allow bone ingrowth. Bioactive glass as an osteopromotive material is expected to stimulate the formation of new bone. The polysaccharide coating is expected to prevent bacterial colonization of the implant. The FRC implants developed in this study are based on the porous network of randomly-oriented E-glass fibers bound together by non-resorbable photopolymerizable methacrylate resin. These structures had a total porosity of 10–70 volume %, of which > 70% were open pores. The pore sizes > 100 μm were in the biologically-relevant range (50-400 μm), which is essential for vascularization and bone ingrowth. Bone ingrowth into these structures was simulated by imbedding of porous FRC specimens in gypsum. Results of push-out tests indicated the increase in the shear strength and fracture toughness of the interface with the increase in the total porosity of FRC specimens. The osteopromotive effect of bioactive glass is based on its dissolution in the physiological environment. Here, calcium and phosphate ions, released from the glass, precipitated on the glass surface and its proximity (the FRC) and formed bone-like apatite. The biomineralization of the FRC structure, due to the bioactive glass reactions, was studied in Simulated Body Fluid (SBF) in static and dynamic conditions. An antimicrobial, non-cytotoxic polysaccharide coating, containing silver nanoparticles, was obtained through strong electrostatic interactions with the surface of FRC. In in vitro conditions the lactose-modified chitosan (chitlac) coating showed no signs of degradation within seven days of exposure to lysozyme or one day to hydrogen peroxide (H2O2). The antimicrobial efficacy of the coating was tested against Staphylococcus aureus and Pseudomonas aeruginosa. The contact-active coating had an excellent short time antimicrobial effect. The coating neither affected the initial adhesion of microorganisms to the implant surface nor the biofilm formation after 24 h and 72 h of incubation. Silver ions released to the aqueous environment led to a reduction of bacterial growth in the culture medium.

Use of fiber-reinforced composite framework and thermochromic pigment in maxillofacial prostheses

The purpose of this investigation was to evaluate the possibility to enhance certain qualities of facial prostheses. Polymethyl methacrylate is still being used as base mate¬rial or clip carrier material, but it is hard and heavy, and debonding of the silicone from the acrylic base material is a frequent problem. This thesis aims to evaluate the use of fiber-reinforced composite (FRC) as framework material for maxillofacial silicone prostheses. FRC has been used as reinforcement in removable and fixed partial dentures since the 1990s. This material is lightweight and can be fabricated to compress the margins of the prosthesis slightly, to keep it tightly against the skin during jaw movements and facial expressions. Additionally, the use of a thermochromic pigment, colorless in room temperature and red in a cold environment, was studied in order to evaluate the possibility of using this color changing pigment in facial prostheses to mimic the color change of facial skin in cold weather. The tensile bond strength between pre-impregnated, unidirectional FRC and maxillofacial silicone elastomer was studied. Three different bonding agents or primers were compared. Bond strength was improved by one of the primers and by roughening the surface. The effect of a skin compressing glass fiber-reinforced composite framework on facial skin blood flow was studied by using a face mask, constructed with a compression pad corresponding to the outer margin of a glass fiber-reinforced framework beam of a facial prosthesis. The skin blood flow of ten healthy volunteers, aged 23-25 years, was measured during touch, light, and moderate compression of the skin, by using laser Doppler imaging technique. None of the compressions showed any marked effects on local skin blood flow. There were no significant differences between blood flow during compression and at baseline. Maxillofacial silicone elastomer was colored intrinsically with conventional color pigments: a control group containing only conventional pigments was compared to two test groups with 0.2 wt% and 0.6 wt% thermochromic pigment added. The color of the material was measured with a spectrophotometer in room temperature and after storage in a freezer. The color stability of the maxillofacial silicone elastomer colored with thermo¬chromic pigment was evaluated by artificial aging. The color dif¬ference of the L* (lightness) and a* values (redness), comparing color after the samples were stored at room temperature and in a freezer (-19°C), was statistically significant for both 0.2 wt% and 0.6 wt% thermo¬chromic pigment groups. The differences in the b* values (yellowness) were statistically significant for the 0.6 wt% group. Exposure to ultraviolet (UV) radiation led to visually noticeable and statistically signifi¬cant color changes (ΔE) in all color values in both test groups. The specimens containing thermochromic pigment were very sensitive to UV radiation. In conclusion, a framework of fiber-reinforced composite can successfully be bonded to maxillofacial silicone elastomer, and a framework beam, compressing the facial skin, did not remarkably alter the skin blood flow on healthy, young adults. The thermochromic pigment showed color change in maxillofacial silicone elastomer. However, artificial aging showed that it was too sensitive to UV radiation to be used, as such, in maxillofacial prostheses.