Effect of Shielding Gases in Laser Welding of Aluminium Alloys

High reflectivity to laser light, alloying element evaporation during high power laser welding makes aluminium alloys highly susceptibility to weld defects such as porosity, cracking and undercutting. The dynamic behaviour of the keyhole, due to fluctuating plasma above the keyhole and the vaporization ofthe alloying elements with in the keyhole, is the key problem to be solved for the improvement of the weld quality and stabilization of the keyhole dynamics isperhaps the single most important development that can broaden the application of laser welding of aluminium alloys. In laser welding, the shielding gas is commonly used to stabilize the welding process, to improve the welded joint features and to protect the welded seam from oxidation. The chemicalcomposition of the shielding gas is a key factor in achieving the final qualityof the welded joints. Wide range of shielding gases varying from the pure gasesto complex mixtures based on helium, argon, nitrogen and carbon dioxide are commercially available. These gas mixtures should be considered in terms of their suitability during laser welding of aluminium alloys to produce quality welds. The main objective of the present work is to study the effect of the shielding gascomposition during laser welding of aluminium alloys. Aluminium alloy A15754 was welded using 3kW Nd-YAG laser (continuous wave mode). The alloy samples were butt welded with different shielding gases (pure and mixture of gases) so that high quality welds with high joint efficiencies could be produced. It was observed that the chemical composition of the gases influenced the final weld quality and properties. In general, the mixture gases, in correct proportions, enabled better utilisation of the properties of the mixing gases, stabilized the welding process and produced better weld quality compared to the pure shielding gases.

Visual measurement of laser-arc hybrid welding

Tässä työssä raportoidaan hybridihitsauksesta otettujen suurnopeuskuvasarjojen automaattisen analyysijärjestelmän kehittäminen.Järjestelmän tarkoitus oli tuottaa tietoa, joka avustaisi analysoijaa arvioimaan kuvatun hitsausprosessin laatua. Tutkimus keskittyi valokaaren taajuuden säännöllisyyden ja lisäainepisaroiden lentosuuntien mittaamiseen. Valokaaria havaittiin kuvasarjoista sumean c-means-klusterointimenetelmän avullaja perättäisten valokaarien välistä aikaväliä käytettiin valokaaren taajuuden säännöllisyyden mittarina. Pisaroita paikannettiin menetelmällä, jossa yhdistyi pääkomponenttianalyysi ja tukivektoriluokitin. Kalman-suodinta käytettiin tuottamaan arvioita pisaroiden lentosuunnista ja nopeuksista. Lentosuunnanmääritysmenetelmä luokitteli pisarat niiden arvioitujen lentosuuntien perusteella. Järjestelmän kehittämiseen käytettävissä olleet kuvasarjat poikkesivat merkittävästi toisistaan kuvanlaadun ja pisaroiden ulkomuodon osalta, johtuen eroista kuvaus- ja hitsausprosesseissa. Analyysijärjestelmä kehitettiin toimimaan pienellä osajoukolla kuvasarjoja, joissa oli tietynlainen kuvaus- ja hitsausprosessi ja joiden kuvanlaatu ja pisaroiden ulkomuoto olivat samankaltaisia, mutta järjestelmää testattiin myös osajoukon ulkopuolisilla kuvasarjoilla. Testitulokset osoittivat, että lentosuunnanmääritystarkkuus oli kohtuullisen suuri osajoukonsisällä ja pieni muissa kuvasarjoissa. Valokaaren taajuuden säännöllisyyden määritys oli tarkka useammassa kuvasarjassa.

Tuning the design procedures for laser processed microwave mechanics

This research has been focused at the development of a tuned systematic design methodology, which gives the best performance in a computer aided environment and utilises a cross-technological approach, specially tested with and for laser processed microwave mechanics. A tuned design process scheme is also presented. Because of the currently large production volumes of microwave and radio frequency mechanics even slight improvements of design methodologies or manufacturing technologies would give reasonable possibilities for cost reduction. The typical number of required iteration cycles could be reduced to one fifth of normal. The research area dealing with the methodologies is divided firstly into a function-oriented, a performance-oriented or a manufacturability-oriented product design. Alternatively various approaches can be developed for a customer-oriented, a quality-oriented, a cost-oriented or an organisation-oriented design. However, the real need for improvements is between these two extremes. This means that the effective methodology for the designers should not be too limited (like in the performance-oriented design) or too general (like in the organisation-oriented design), but it should, include the context of the design environment. This is the area where the current research is focused. To test the developed tuned design methodology for laser processing (TDMLP) and the tuned optimising algorithm for laser processing (TOLP), seven different industrial product applications for microwave mechanics have been designed, CAD-modelled and manufactured by using laser in small production series. To verify that the performance of these products meets the required level and to ensure the objectiveness ofthe results extensive laboratory tests were used for all designed prototypes. As an example a Ku-band horn antenna can be laser processed from steel in 2 minutes at the same time obtaining a comparable electrical performance of classical aluminium units or the residual resistance of a laser joint in steel could be limited to 72 milliohmia.

A Comparative Study of the Effectiveness of a Prefabricated Appliance and a Stabilization Appliance in the Treatment of Myofascial pain and Headache

The aim of this thesis was to evaluate the short- and long-term effectiveness of a prefabricated occlusal appliance (R) on patients with myofascial pain and headache by comparing it with the treatment of the stabilization appliance (S). Another aim was to evaluate the effect of appliance treatment on stress-related salivary parameters like cortisol and IgA, as well as on flow rate values in these patients. Sixty-five patients diagnosed with myofascial temporomandibular disorder (TMD) pain, of whom 94% suffered concomitantly from headache, at two centres for Stomatognathic Physiology, one in Sweden and one in Finland, were included in this randomized controlled trial using Research Diagnostic Criteria for TMD (RDC/TMD), with history questionnaires and clinical examinations performed at baseline and at 6- and 10-weeks, and 6- and 12-month follow-ups. Patients were randomly assigned either to the R or the S group. Treatment outcome was measured according to IMMPACT (Initiative on Methods, Measurements, and Pain Assessment in Clinical Trials), i.e. four chronic pain outcome domains: pain intensity, overall improvement, physical and emotional functioning. Changes in frequency and intensity of headache were recorded. Thirty-nine patients participated in the saliva study. Salivary analyses were performed at 6 and 10 weeks. The results revealed no differences between groups at baseline. At all follow-ups, all four outcome measures, as well as frequency and intensity of headache, showed statistically significant within-group improvement compared to baseline, without significant differences between groups. No treatment-induced changes in saliva parameters could be registered. In conclusion, the effectiveness of the prefabricated appliance seemed to be similar to that of the stabilization appliance in alleviating myofascial pain, and frequency and intensity of headache, in the short as well as the long term. However, no changes in salivary parameters were observed during treatment.

Surface transformation hardening of carbon steel with high power fiber laser

This study investigated the surface hardening of steels via experimental tests using a multi-kilowatt fiber laser as the laser source. The influence of laser power and laser power density on the hardening effect was investigated. The microhardness analysis of various laser hardened steels was done. A thermodynamic model was developed to evaluate the thermal process of the surface treatment of a wide thin steel plate with a Gaussian laser beam. The effect of laser linear oscillation hardening (LLOS) of steel was examined. An as-rolled ferritic-pearlitic steel and a tempered martensitic steel with 0.37 wt% C content were hardened under various laser power levels and laser power densities. The optimum power density that produced the maximum hardness was found to be dependent on the laser power. The effect of laser power density on the produced hardness was revealed. The surface hardness, hardened depth and required laser power density were compared between the samples. Fiber laser was briefly compared with high power diode laser in hardening medium-carbon steel. Microhardness (HV0.01) test was done on seven different laser hardened steels, including rolled steel, quenched and tempered steel, soft annealed alloyed steel and conventionally through-hardened steel consisting of different carbon and alloy contents. The surface hardness and hardened depth were compared among the samples. The effect of grain size on surface hardness of ferritic-pearlitic steel and pearlitic-cementite steel was evaluated. In-grain indentation was done to measure the hardness of pearlitic and cementite structures. The macrohardness of the base material was found to be related to the microhardness of the softer phase structure. The measured microhardness values were compared with the conventional macrohardness (HV5) results. A thermodynamic model was developed to calculate the temperature cycle, Ac1 and Ac3 boundaries, homogenization time and cooling rate. The equations were numerically solved with an error of less than 10-8. The temperature distributions for various thicknesses were compared under different laser traverse speed. The lag of the was verified by experiments done on six different steels. The calculated thermal cycle and hardened depth were compared with measured data. Correction coefficients were applied to the model for AISI 4340 steel. AISI 4340 steel was hardened by laser linear oscillation hardening (LLOS). Equations were derived to calculate the overlapped width of adjacent tracks and the number of overlapped scans in the center of the scanned track. The effect of oscillation frequency on the hardened depth was investigated by microscopic evaluation and hardness measurement. The homogeneity of hardness and hardened depth with different processing parameters were investigated. The hardness profiles were compared with the results obtained with conventional single-track hardening. LLOS was proved to be well suitable for surface hardening in a relatively large rectangular area with considerable depth of hardening. Compared with conventional single-track scanning, LLOS produced notably smaller hardened depths while at 40 and 100 Hz LLOS resulted in higher hardness within a depth of about 0.6 mm.

Laser cladding with scanning optics

Scanning optics create different types of phenomena and limitation to cladding process compared to cladding with static optics. This work concentrates on identifying and explaining the special features of laser cladding with scanning optics. Scanner optics changes cladding process energy input mechanics. Laser energy is introduced into the process through a relatively small laser spot which moves rapidly back and forth, distributing the energy to a relatively large area. The moving laser spot was noticed to cause dynamic movement in the melt pool. Due to different energy input mechanism scanner optic can make cladding process unstable if parameter selection is not done carefully. Especially laser beam intensity and scanning frequency have significant role in the process stability. The laser beam scanning frequency determines how long the laser beam affects with specific place local specific energy input. It was determined that if the scanning frequency in too low, under 40 Hz, scanned beam can start to vaporize material. The intensity in turn determines on how large package this energy is brought and if the intensity of the laser beam was too high, over 191 kW/cm2, laser beam started to vaporize material. If there was vapor formation noticed in the melt pool, the process starts to resample more laser alloying due to deep penetration of laser beam in to the substrate. Scanner optics enables more flexibility to the process than static optics. The numerical adjustment of scanning amplitude enables clad bead width adjustment. In turn scanner power modulation (where laser power is adjusted according to where the scanner is pointing) enables modification of clad bead cross-section geometry when laser power can be adjusted locally and thus affect how much laser beam melts material in each sector. Power modulation is also an important factor in terms of process stability. When a linear scanner is used, oscillating the scanning mirror causes a dwell time in scanning amplitude border area, where the scanning mirror changes the direction of movement. This can cause excessive energy input to this area which in turn can cause vaporization and process instability. This process instability can be avoided by decreasing energy in this region by power modulation. Powder feeding parameters have a significant role in terms of process stability. It was determined that with certain powder feeding parameter combinations powder cloud behavior became unstable, due to the vaporizing powder material in powder cloud. Mainly this was noticed, when either or both the scanning frequency or powder feeding gas flow was low or steep powder feeding angle was used. When powder material vaporization occurred, it created vapor flow, which prevented powder material to reach the melt pool and thus dilution increased. Also powder material vaporization was noticed to produce emission of light at wavelength range of visible light. This emission intensity was noticed to be correlated with the amount of vaporization in the powder cloud.