Fibre-reinforced composites as root canal posts

Fibre-reinforced composite (FRC) root canal posts are suggested to have biomechanical benefits over traditional metallic posts, but they lack good adhesion to resin composites. The aim of this series of studies was to evaluate the adhesion of individually formed fibre-reinforced composite material to composite resin and dentin, as well as some mechanical properties. Flexural properties were evaluated and compared between individually formed FRC post material and different prefabricated posts. The depth of polymerization of the individually formed FRC post material was evaluated with IR spectrophotometry and microhardness measurements, and compared to that of resin without fibres. Bonding properties of the individually formed FRC post to resin cements and dentin were tested using Pull-out- and Push-out-force tests, evaluated with scanning electron microscopy, and compared to those of prefabricated FRC and metal posts. Load-bearing capacity and microstrain were evaluated and failure mode assessment was made on incisors restored with individually formed FRC posts of different structures and prefabricated posts. The results of these studies show that the individually polymerized and formed FRC post material had higher flexural properties compared to the commercial prefabricated FRC posts. The individually polymerized FRC material showed almost the same degree of conversion after light polymerization as monomer resin without fibres. Moreover, it was found that the individually formed FRC post material with a semiinterpenetrating polymer network (IPN) polymer matrix bonded better to composite resin luting cement, than did the prefabricated posts with a cross-linked polymer matrix. Furthermore, it was found that, contrary to the other posts, there were no adhesive failures between the individually formed FRC posts and composite resin luting cement. This suggests better interfacial adhesion of cements to these posts. Although no differences in load-bearing capacity or microstrain could be seen, the incisors restored with individually formed FRC posts with a hollow structure showed more favourable failures compared to other prefabricated posts. These studies suggest that it is possible to use individually formed FRC material with semi-IPN polymer matrix as root canal post material. They also indicate that there are benefits especially regarding the bonding properties to composite resin and dentin with this material compared to prefabricated FRC post material with a cross-linked matrix. Furthermore, clinically more repairable failures were found with this material compared to those of prefabricated posts.

Arcus semi-diurni siderum, ad latitudinem Aboënsem

Arkit: A4 [B2].

Natural and synthetic fibres improving tensile strength and elongation of paper products

The theory part of the Master’s thesis introduces fibres with high tensile strength and elongation used in the production of paper or board. Strong speciality papers are made of bleached softwood long fibre pulp. The aim of the thesis is to find new fibres suitable for paper making to increase either tensile strength, elongation or both properties. The study introduces how fibres bond and what kind of fibres give the strongest bonds into fibre matrix. The fibres that are used the in manufacturing of non-wovens are long and elastic. They are longer than softwood cellulose fibres. The end applications of non-wovens and speciality papers are often the same, for instance, wet napkins or filter media. The study finds out which fibres are used in non-wovens and whether the same fibres could be added to cellulose pulp as armature fibres, what it would require for these fibres to be blended in cellulose, how they would bind with cellulose and whether some binding agents or thermal bonding, such as hot calendaring would be necessary. The following fibres are presented: viscose, polyester, nylon, polyethylene, polypropylene and bicomponent fibres. In the empiric part of the study the most suitable new fibres are selected for making hand sheets in laboratory. Test fibres are blended with long fibre cellulose. The test fibres are viscose (Tencel), polypropylene and polyethylene. Based on the technical values measured in the sheets, the study proposes how to continue trials on paper machine with viscose, polyester, bicomponent and polypropylene fibres.

Surface chemistry of fibres and vessel elements in chemical and recycled pulps

Den viktigaste råvaran i papperstillverkning är pappersmassa. Massan innehåller (ved)fibrer men också finmaterial och andra typers (ved)celler, så som kärlceller. Hur dessa komponenter beter sig under arkformationen i pappersmaskinen eller hur de bidrar till egenskaperna hos det färdiga pappret avgörs till stor del av massakomponenternas ytkemiska sammansättning, fysiska struktur och mängden joniserbara grupper på ytan. I denna avhandling studerades ytegenskaperna hos fraktionerade kemiska massor och returfibermassor med avancerade analystekniker. Rester av avfärgningskemikalier identifierades på både returfibrer och på kärlceller. Dessa kan påverka arkformationen och arkstyrkan på returfiberpapper. Kärlcellernas cellväggsstruktur visade sig skilja sig från fibrernas. Resultaten kan främja utvecklingen av returfiberprosessen och användningen av kärlcellsrika lövvedsmassor.