Hemicellulose extracted Kraft pulp as a raw material of paper

The transformation of a traditional pulp mill into an integrated forest biorefinery utilizing wood-derived biomass presents a promising opportunity for enterprise revival of the pulp and paper industry by offering new sources of revenue and significantly improved industry profitability. One proposed next generation process step for an integrated forest biorefinery is the extraction of hemicelluloses, allowing the co-production of pulp and ethanol or chemicals. The extraction of hemicelluloses, however, will likely have downstream effects on pulp quality. In the literature survey an overview of the integrated forest biorefinery and possible next generation technologies implementable in such facility were reviewed. Moreover, some hemicellulose extraction methods suitable for the co-production of pulp and hemicellulose products were looked into in more detail. Also, an overview on the significance of pulp’s hemicellulose content on papermaking properties of pulp fibers was made. In the literature it is stated that the hemicellulose content of pulp affects on many papermaking properties of pulp fibers, hornification and paper strength properties in particular. In the experimental part the goal was to investigate what effects alkaline hemicellulose extraction after bleaching has on the papermaking properties of birch Kraft pulp. It was discovered that tested pulps, normal and hemi-poor birch Kraft pulp, were different in many ways regarding to pulp properties. Differences were observed in both physical and chemical characteristics. Furthermore, clear distinctions were seen in tested paper properties, especially in strength properties, between the handsheets made from hemi-poor or normal birch Kraft pulp. Hemi-poor and normal birch Kraft pulps were also compared as a raw material of laboratory made copy paper. Based on this comparison, usage of hemi-poor birch pulp as the raw material of copy paper does not drastically deteriorate its quality.

Green diesel synthesis by hydrodeoxygenation of lipids extracted from Chlorella algae in supercritical hexane

Lipids were extracted from Chlorella algae with supercritical hexane. The high lipids yield of approximately 10% was obtained at optimum conditions of 300 rpm stirring speed and 2 h duration compared to the total contents of lipids being 12%. Furthermore, an easiness of hexane recovery may be considered as economically and ecologically attractive. For the first time, in the current work catalytic hydrodeoxygenation (HDO) of Chlorella algal lipids was studied over 5 wt% Ni/H-Y-80 and 5 wt% Ni/SiO2 at 300 C and under 30 bar total pressure in H2. A comparative HDO of stearic acid was carried out under similar conditions. The conversion of lipids was about 35% over 5 wt% Ni/H-Y-80 after 6h, whereas, 5 wt% Ni/SiO2 was totally deactivated after 60 min. The selectivity to hydrocarbons (C15-C18) is 6%. As a comparison, complete conversion of stearic acid over 5 wt% Ni/H-Y-80 was achieved in 6 h. The transformation of lipids proceeded mostly via hydrogenation and hydrolysis with formation of free fatty acid (FFA). The lower activity might be attributed to deactivation of catalysts caused by chlorophylls and carotenoids. Even though the conversion is low, future studies in HDO of lipids extracted from other algae species having higher lipid content could be proposed. Coke resistant catalyst might be considered to improve catalytic activity.