Weldability of high strength aluminium alloys

The need for reduced intrinsic weight of structures and vehicles in the transportation industry has made aluminium research of interest. Aluminium has properties that are favourable for structural engineering, including good strength-to-weight ratio, corrosion resistance and machinability. It can be easily recycled saving energy used in smelting as compared to steel. Its alloys can have ultimate tensile strength of up to 750 MPa, which is comparable to steel. Aluminium alloys are generally weldable, however welding of high strength alloys like the 7xxx series pose considerable challenges. This paper presents research on the weldability of high strength aluminium alloys, principally the 7xxx series. The weldability with various weld processes including MIG, TIG, and FSW, is discussed in addition to consideration of joint types, weld defects and recommendations for minimizing or preventing weld defects. Experimental research was carried out on 7025-T6 and AW-7020 alloys. Samples were welded, and weld cross sections utilized in weld metallurgy studies. Mechanical tests were carried out including hardness tests and tensile tests. In addition, testing was done for the presence of Al2O3 on exposed aluminium alloy. It was observed that at constant weld heat input using a pulsed MIG system, the welding speed had little or no effect on the weld hardness. However, the grain size increased as the filler wire feed rate, welding current and welding speed increased. High heat input resulted in lower hardness of the weld profile. Weld preheating was detrimental to AW- 7020 welds; however, artificial aging was beneficial. Acceptable welds were attained with pulsed MIG without the removal of the Al2O3 layer prior to welding. The Al2O3 oxide layer was found to have different compositions in different aluminium alloys. These findings contribute useful additional information to the knowledge base of aluminium welding. The application of the findings of this study in welding will help reduce weld cost and improve high strength aluminium structure productivity by removing the need for pre-weld cleaning. Better understanding of aluminium weld metallurgy equips weld engineers with information for better aluminium weld design.