On the effects of welding parameters on weld quality of plasma arc keyhole welding of structural steels

The possibility and the usefulness of applying plasma keyhole welding to structural steels with different compositions and material thicknesses, and in various welding positions has been examinated. Single pass butt welding with I groove in flat, horizontal vertical and vertical positions and root welding with V , Y and U grooves of thick plate material in flat position have been studied and the welds with high quality has been obtained. The technological conditions for successful welding are presented. The single and interactive effects of welding parameters on weld quality, especially on surface weld defects, geometrical form errors, internal defects and mechanical properties (strength, ductility, impact toughness, hardness and bendability) of weld joint, are presented. Welding parameter combinations providing the best quality welds are also presented.

The effects of real time control of welding parameters on weld quality in plasma arc keyhole welding

Joints intended for welding frequently show variations in geometry and position, for which it is unfortunately not possible to apply a single set of operating parameters to ensure constant quality. The cause of this difficulty lies in a number of factors, including inaccurate joint preparation and joint fit up, tack welds, as well as thermal distortion of the workpiece. In plasma arc keyhole welding of butt joints, deviations in the gap width may cause weld defects such as an incomplete weld bead, excessive penetration and burn through. Manual adjustment of welding parameters to compensate for variations in the gap width is very difficult, and unsatisfactory weld quality is often obtained. In this study a control system for plasma arc keyhole welding has been developed and used to study the effects of the real time control of welding parameters on gap tolerance during welding of austenitic stainless steel AISI 304L. The welding tests demonstrated the beneficial effect of real time control on weld quality. Compared with welding using constant parameters, the maximum tolerable gap width with an acceptable weld quality was 47% higher when using the real time controlled parameters for a plate thickness of 5 mm. In addition, burn through occurred with significantly larger gap widths when parameters were controlled in real time. Increased gap tolerance enables joints to be prepared and fit up less accurately, saving time and preparation costs for welding. In addition to the control system, a novel technique for back face monitoring is described in this study. The test results showed that the technique could be successfully applied for penetration monitoring when welding non magnetic materials. The results also imply that it is possible to measure the dimensions of the plasma efflux or weld root, and use this information in a feedback control system and, thus, maintain the required weld quality.

Influence of plasma modification on surface properties and offset printability of coated paper

The properties of the paper surface play a crucial role in ensuring suitable quality and runnability in various converting and finishing operations, such as printing. Plasma surface modification makes it possible to modify the surface chemistry of paper without altering the bulk material properties. This also makes it possible to investigate the role of the surface chemistry alone on printability without influencing the porous structure of the pigment-coated paper. Since the porous structure of a pigment coating controls both ink setting and optical properties, surface chemical changes created by a plasma modification have a potential to decouple these two effects and to permit a better optimization of them both. The aim of this work was to understand the effects of plasma surface modification on paper properties, and how it influences printability in the sheet-fed offset process. The objective was to broaden the fundamental understanding of the role of surface chemistry on offset printing. The effects of changing the hydrophilicity/ hydrophobicity and the surface chemical composition by plasma activation and plasma coatings on the properties of coated paper and on ink-paper interactions as well as on sheet-fed offset print quality were investigated. In addition, the durability of the plasma surface modification was studied. Nowadays, a typical sheet-fed offset press also contains units for surface finishing, for example UVvarnishing. The role of the surface chemistry on the UV-varnish absorption into highly permeable and porous pigment-coated paper was also investigated. With plasma activation it was possible to increase the surface energy and hydrophilicity of paper. Both polar and dispersion interactions were found to increase, although the change was greater in the polar interactions due to induced oxygen molecular groups. The results indicated that plasma activation takes place particularly in high molecular weight components such as the dispersion chemicals used to stabilize the pigment and latex particles. Surface composition, such as pigment and binder type, was found to influence the response to the plasma activation. The general trend was that pilot-scale treatment modified the surface chemistry without altering the physical coating structure, whereas excessive laboratory-scale treatment increased the surface roughness and reduced the surface strength, which led to micro-picking in printing. It was shown that pilot-scale plasma activation in combination with appropriate ink oils makes it possible to adjust the ink-setting rate. The ink-setting rate decreased with linseed-oil-based inks, probably due to increased acid-base interactions between the polar groups in the oil and the plasma-treated paper surface. With mineral-oil-based inks, the ink setting accelerated due to plasma activation. Hydrophobic plasma coatings were able to reduce or even prevent the absorption of dampening water into pigmentcoated paper, even when the dampening water was applied under the influence of nip pressure. A uniform hydrophobic plasma coating with sufficient chemical affinity with ink gave an improved print quality in terms of higher print density and lower print mottle. It was also shown that a fluorocarbon plasma coating reduced the free wetting of the UV-varnish into the highly permeable and porous pigment coating. However, when the UV-varnish was applied under the influence of nip pressure, which leads to forced wetting, the role of the surface chemical composition seems to be much less. A decay in surface energy and wettability occurred during the first weeks of storage after plasma activation, after which it leveled off. However, the oxygen/carbon elemental ratio did not decrease as a function of time, indicating that ageing could be caused by a re-orientation of polar groups or by a contamination of the surface. The plasma coatings appeared to be more stable when the hydrophobicity was higher, probably due to fewer interactions with oxygen and water vapor in the air.

Numerical simulation of two-chamber plasma sources using finite element method

Numerical simulation of plasma sources is very important. Such models allows to vary different plasma parameters with high degree of accuracy. Moreover, they allow to conduct measurements not disturbing system balance.Recently, the scientific and practical interest increased in so-called two-chamber plasma sources. In one of them (small or discharge chamber) an external power source is embedded. In that chamber plasma forms. In another (large or diffusion chamber) plasma exists due to the transport of particles and energy through the boundary between chambers.In this particular work two-chamber plasma sources with argon and oxygen as active mediums were onstructed. This models give interesting results in electric field profiles and, as a consequence, in density profiles of charged particles.

Laser- plasma- hybridihitsauksen käytettävyys teollisuudessa

Hybridihitsaukseksi nimitetään yleensä hitsausprosesseja, joissa yhdistetään kaari- ja laserhitsauksen vahvuudet. Laser- MIG/MAG- prosessit ovat näistä selvästi yleisimpiä, mutta muillekin prosesseille on sovelluksia. Tässä kandidaatintyössä on arvioitu laser- plasma- hybridihitsausprosessin käytettävyyttä teollisuuden prosesseissa. Arviointi on tehty vertailevana kirjallisuustutkimuksena laser- plasma- hybridiprosessin, laserhitsauksen, sekä muiden laser- hybridihitsausprosessien kesken. Prosessien vertailun lisäksi työssä on käsitelty hybridihitsausprosessien parametrien valintaa ja laser- plasma- hybridiprosessin erityispiirteitä.