Effect of loading type on the fatigue strength of symmetric and asymmetric welded joints made of ultra high strength steel

In this study, finite element analyses and experimental tests are carried out in order to investigate the effect of loading type and symmetry on the fatigue strength of three different non-load carrying welded joints. The current codes and recommendations do not give explicit instructions how to consider degree of bending in loading and the effect of symmetry in the fatigue assessment of welded joints. The fatigue assessment is done by using effective notch stress method and linear elastic fracture mechanics. Transverse attachment and cover plate joints are analyzed by using 2D plane strain element models in FEMAP/NxNastran and Franc2D software and longitudinal gusset case is analyzed by using solid element models in Abaqus and Abaqus/XFEM software. By means of the evaluated effective notch stress range and stress intensity factor range, the nominal fatigue strength is assessed. Experimental tests consist of the fatigue tests of transverse attachment joints with total amount of 12 specimens. In the tests, the effect of both loading type and symmetry on the fatigue strength is studied. Finite element analyses showed that the fatigue strength of asymmetric joint is higher in tensile loading and the fatigue strength of symmetric joint is higher in bending loading in terms of nominal and hot spot stress methods. Linear elastic fracture mechanics indicated that bending reduces stress intensity factors when the crack size is relatively large since the normal stress decreases at the crack tip due to the stress gradient. Under tensile loading, experimental tests corresponded with finite element analyzes. Still, the fatigue tested joints subjected to bending showed the bending increased the fatigue strength of non-load carrying welded joints and the fatigue test results did not fully agree with the fatigue assessment. According to the results, it can be concluded that in tensile loading, the symmetry of joint distinctly affects on the fatigue strength. The fatigue life assessment of bending loaded joints is challenging since it depends on whether the crack initiation or propagation is predominant.

Ventricular rate during acute atrial fibrillation and outcome of electrical cardioversion: The FinCV Study

The impact of ventricular rate (VR) on the outcome of electrical cardioversion (ECV) of acute atrial fibrillation (AF) is currently unknown. We aimed to determine the effect of VR during acute AF on the success of ECV, recurrence of AF and occurrence of post-cardioversion complications in 30 days follow-up. All ECVs performed in patients with acute atrial fibrillation lasting <48 hours in 2 Finnish university hospitals during 2003-2010 and 1 central hospital during 2010 were retrospectively identified. A total of 6,624 ECVs were performed in 2,821 consecutive patients. VR≤60 BPM was defined low and VR≥160 BPM high. The median VR before ECV was 109 BPM. The success rate of ECV was 94.2%. Bradycardia occurred in 62 (0.9%) and thromboembolic complications in 39 (0.6%) ECVs. Low VR was observed before 75 (1.1%) ECVs and male sex was its only independent predictor. High VR was observed in 165 (2.5%) ECVs. The independent predictors of high VR were younger age, <12 h episode duration, no previous history of AF and alcohol abuse. Low or high VR were not related to the success of ECV, incidence of thromboembolic or bradycardic complications, or recurrence of AF, although VR was significantly (p<0.001) lower in the patients in whom AF recurred. In conclusion, ECV of acute AF is an effective procedure and VR during AF does not affect its efficacy, the maintenance of sinus rhythm or the incidence of bradycardic, thromboembolic or other complications during 30 days follow-up after ECV. Low VR is predominately observed in male patients, while high VR was a feature related to a shorter history of AF and high alcohol-intake.