Weldability of powder bed fusion fabricated stainless steel 316L sheets to cold rolled sheet metal

Weldability of powder bed fusion (PBF) fabricated components has come to discussion in past two years due to resent developments in the PBF technology and limited size of the machines used in the fabrication process. This study concentrated on effects of energy input of welding on mechanical properties and microstructural features of welds between PBF fabricated stainless steel 316L sheets and cold rolled sheet metal of same composition by the means of destructive testing and microscopic analysis. Optical fiber diameter, laser power and welding speed were varied during the experiments that were executed following one variable at a time (OVAT) method. One of the problems of welded PBF fabricated components has been lower elongations at break comparing to conventionally manufactured components. Decreasing energy input of the laser keyhole welding decreased elongations at break of the welded specimens. Ultimate tensile strengths were not affected significantly by the energy input of the welding, but fracturing of the specimens welded using high energy input occurred from the weld metal. Fracturing of the lower energy input welds occurred from the PBF fabricated base metal. Energy input was found to be critical factor for mechanical properties of the welds. Multioriented grain growth and formation of neck at fusion zone boundary on the cold rolled side of the weld was detected and suspected to be result from weld pool flows caused by differences in molten weld pool behaviour between the PBF fabricated and cold rolled sides of the welds.

Feasibility of industrial implementation of laser cutting into paper making machine

Laser cutting implementation possibilities into paper making machine was studied as the main objective of the work. Laser cutting technology application was considered as a replacement tool for conventional cutting methods used in paper making machines for longitudinal cutting such as edge trimming at different paper making process and tambour roll slitting. Laser cutting of paper was tested in 70’s for the first time. Since then, laser cutting and processing has been applied for paper materials with different level of success in industry. Laser cutting can be employed for longitudinal cutting of paper web in machine direction. The most common conventional cutting methods include water jet cutting and rotating slitting blades applied in paper making machines. Cutting with CO2 laser fulfils basic requirements for cutting quality, applicability to material and cutting speeds in all locations where longitudinal cutting is needed. Literature review provided description of advantages, disadvantages and challenges of laser technology when it was applied for cutting of paper material with particular attention to cutting of moving paper web. Based on studied laser cutting capabilities and problem definition of conventional cutting technologies, preliminary selection of the most promising application area was carried out. Laser cutting (trimming) of paper web edges in wet end was estimated to be the most promising area where it can be implemented. This assumption was made on the basis of rate of web breaks occurrence. It was found that up to 64 % of total number of web breaks occurred in wet end, particularly in location of so called open draws where paper web was transferred unsupported by wire or felt. Distribution of web breaks in machine cross direction revealed that defects of paper web edge was the main reason of tearing initiation and consequent web break. The assumption was made that laser cutting was capable of improvement of laser cut edge tensile strength due to high cutting quality and sealing effect of the edge after laser cutting. Studies of laser ablation of cellulose supported this claim. Linear energy needed for cutting was calculated with regard to paper web properties in intended laser cutting location. Calculated linear cutting energy was verified with series of laser cutting. Practically obtained laser energy needed for cutting deviated from calculated values. This could be explained by difference in heat transfer via radiation in laser cutting and different absorption characteristics of dry and moist paper material. Laser cut samples (both dry and moist (dry matter content about 25-40%)) were tested for strength properties. It was shown that tensile strength and strain break of laser cut samples are similar to corresponding values of non-laser cut samples. Chosen method, however, did not address tensile strength of laser cut edge in particular. Thus, the assumption of improving strength properties with laser cutting was not fully proved. Laser cutting effect on possible pollution of mill broke (recycling of trimmed edge) was carried out. Laser cut samples (both dry and moist) were tested on the content of dirt particles. The tests revealed that accumulation of dust particles on the surface of moist samples can take place. This has to be taken into account to prevent contamination of pulp suspension when trim waste is recycled. Material loss due to evaporation during laser cutting and amount of solid residues after cutting were evaluated. Edge trimming with laser would result in 0.25 kg/h of solid residues and 2.5 kg/h of lost material due to evaporation. Schemes of laser cutting implementation and needed laser equipment were discussed. Generally, laser cutting system would require two laser sources (one laser source for each cutting zone), set of beam transfer and focusing optics and cutting heads. In order to increase reliability of system, it was suggested that each laser source would have double capacity. That would allow to perform cutting employing one laser source working at full capacity for both cutting zones. Laser technology is in required level at the moment and do not require additional development. Moreover, capacity of speed increase is high due to availability high power laser sources what can support the tendency of speed increase of paper making machines. Laser cutting system would require special roll to maintain cutting. The scheme of such roll was proposed as well as roll integration into paper making machine. Laser cutting can be done in location of central roll in press section, before so-called open draw where many web breaks occur, where it has potential to improve runability of a paper making machine. Economic performance of laser cutting was done as comparison of laser cutting system and water jet cutting working in the same conditions. It was revealed that laser cutting would still be about two times more expensive compared to water jet cutting. This is mainly due to high investment cost of laser equipment and poor energy efficiency of CO2 lasers. Another factor is that laser cutting causes material loss due to evaporation whereas water jet cutting almost does not cause material loss. Despite difficulties of laser cutting implementation in paper making machine, its implementation can be beneficial. The crucial role in that is possibility to improve cut edge strength properties and consequently reduce number of web breaks. Capacity of laser cutting to maintain cutting speeds which exceed current speeds of paper making machines what is another argument to consider laser cutting technology in design of new high speed paper making machines.

Simulation and material calibration of ultra high strength steel (UHSS) S960 welded joint under static tensile test utilizing finite element method (FEM)

The aim of this work was to calibrate the material properties including strength and strain values for different material zones of ultra-high strength steel (UHSS) welded joints under monotonic static loading. The UHSS is heat sensitive and softens by heat due to welding, the affected zone is heat affected zone (HAZ). In this regard, cylindrical specimens were cut out from welded joints of Strenx® 960 MC and Strenx® Tube 960 MH, were examined by tensile test. The hardness values of specimens’ cross section were measured. Using correlations between hardness and strength, initial material properties were obtained. The same size specimen with different zones of material same as real specimen were created and defined in finite element method (FEM) software with commercial brand Abaqus 6.14-1. The loading and boundary conditions were defined considering tensile test values. Using initial material properties made of hardness-strength correlations (true stress-strain values) as Abaqus main input, FEM is utilized to simulate the tensile test process. By comparing FEM Abaqus results with measured results of tensile test, initial material properties will be revised and reused as software input to be fully calibrated in such a way that FEM results and tensile test results deviate minimum. Two type of different S960 were used including 960 MC plates, and structural hollow section 960 MH X-joint. The joint is welded by BöhlerTM X96 filler material. In welded joints, typically the following zones appear: Weld (WEL), Heat affected zone (HAZ) coarse grained (HCG) and fine grained (HFG), annealed zone, and base material (BaM). Results showed that: The HAZ zone is softened due to heat input while welding. For all the specimens, the softened zone’s strength is decreased and makes it a weakest zone where fracture happens while loading. Stress concentration of a notched specimen can represent the properties of notched zone. The load-displacement diagram from FEM modeling matches with the experiments by the calibrated material properties by compromising two correlations of hardness and strength.

Statistical variation of weld profiles and their expected influence on fatigue strength

The general objective of this study was to conduct astatistical analysis on the variation of the weld profiles and their influence on the fatigue strength of the joint. Weld quality with respect to its fatigue strength is of importance which is the main concept behind this thesis. The intention of this study was to establish the influence of weld geometric parameters on the weld quality and fatigue strength. The effect of local geometrical variations of non-load carrying cruciform fillet welded joint under tensile loading wasstudied in this thesis work. Linear Elastic Fracture Mechanics was used to calculate fatigue strength of the cruciform fillet welded joints in as-welded condition and under cyclic tensile loading, for a range of weld geometries. With extreme value statistical analysis and LEFM, an attempt was made to relate the variation of the cruciform weld profiles such as weld angle and weld toe radius to respective FAT classes.

Mangaaniseosteisen duplex-teräksen hitsattavuus

Diplomityön tavoitteena oli selvittää mangaaniseosteisen LDX2101 duplex-teräksen ja LDX2101 hitsauslisäaineiden hitsausparametrit puikkohitsaus-, MAG-täytelankahitsaus- ja plasmahitsausprosessilla. Toisena tavoitteena oli selvittää lämmöntuonnin vaikutuksia hit-sausliitosten mekaanisiin ominaisuuksiin, iskusitkeyteen (-40 °C) ja ferriitti- / austeniittipitoi-suuksien jakaantumiseen. Tutkittavat hitsit olivat päittäishitsejä ja koelevyjen aineenpaksuus oli 6 mm. Koetulosten perusteella tehtiin hitsausohjeet kyseisille hitsausprosesseille. Työn kirjallisessa osassa on selvitetty yleisesti duplex-terästen käyttökohteita, mekaanisia ja kemiallisia ominaisuuksia sekä duplex-terästen korroosio-ominaisuuksia. Lisäksi on käsitelty eri hitsausprosesseja ja duplex-terästen hitsattavuutta, jossa selvitetään mm. terästen jähmet-tymistä, erkaumia ja faaseja, lämmöntuonnin vaikutuksia ja hitsausliitosten korroosionkestä-vyyttä. Teoriaosassa on kerrottu myös hitsausliitosten tarkastuksesta ja hitsiluokista. Työn kokeellisessa osassa esitellään kokeiden suoritus sekä ainetta rikkova ja ainetta rikko-maton tarkastus. Liitoksille suoritettava koestusohjelma noudatti pääosin menetelmäkoestan-dardin SFS-EN 15614-1 ohjetta. Hitseille tehtiin ainetta rikkomaton tarkastus, joka käsittää silmämääräisen tarkastuksen, pintatarkastuksen ja röntgentarkastuksen. Rikkovaa aineen-koetusta tehtiin sisältäen kovuusmittaukset, vetokokeet, taivutuskokeet jaiskusitkeyskokeet. Lisäksi valmistettiin metallografiset hieet, joita tutkimalla selvitettiin hitsausliitoksen metal-lurgiaa ja määriteltiin ferriitti- ja austeniittipitoisuudet. Kokeiden perusteella on laadittu hit-sausohjeet kullekin hitsausprosessille. Lisäksi kokeellisessa osassa on esitelty tulokset syö-pymäkokeesta, jossa selvitettiin eri materiaalien syöpymiskestävyyttä valkolipeäliuoksessa. Tutkimustuloksien perusteella LDX2102 duplex-materiaali onhyvin hitsattavaa laajalla hit-sausparametrialueella. Mekaaniset ominaisuudet, kuten lujuus- ja iskusitkeysarvot täyttävät materiaalistandardin SFS-EN10028-7 niille asettamat vaatimukset. Taivutussitkeys ja murto-venymät jäivät kuitenkin osalla koekappaleista vaatimustasoa alhaisemmiksi. Austeniitti- ja ferriittipitoisuudet vastaavat materiaalistandardin vaatimuksia.

Influence of Heat Treatment on Strength Properties of Finger-jointed Components

The purpose for the thesis was to study the thermo treatment of finger-jointed wood. The thesis concentrated on examining the tensile and bending strength of finger-jointed and thermo treated wood. The aim was to find out how different treatment temperature levels and adhesives influence the strength of wood that has been finger-jointed before heat treatment. Secondary objectives were to examine the influence of the treatment time at one temperature, determine differences in the strength between the joints in heartwood and sapwood, examine the visual appearance of the finger joints after the treatment and establish possibilities to reach a characteristic strength level corresponding to C14. Only minor differences in strength properties were measured between the finger-jointed wood treatments II and III. A greater difference was shown between these two treatment temperatures I, which lead to reduced strength. The average strength of joints glued with adhesive 2 was higher after treatments II and III compared to those glued with the adhesive 1. At the treatment temperature I, the adhesive 1 strength properties were at the same level compared to the adhesive 2 or better. There were not any significant differences.

Ultimate capacity of stainless steel rectangular hollow section X- joints at low temperatures

Growing demand for stainless steel construction materials has increased the popularity of substitutive materials for austenitic stainless steels. The lean duplex grades have taken their place in building of structures exposed to corrosive environments. Since the duplex grades are relatively new materials, the current codes and norms do not fully cover the newest duplex grades. The joints tested in this thesis were designed and studied according to Eurocode 3, even though all the materials are not yet accepted to the standards. The main objective in this thesis was to determine the differences of the used materials in behaviour under loading at low temperatures. Tests in which the deformation and strength properties of the joints were determined were done at the temperature of -46°C, which is the requirement of temperature for structures designed according to Norsok standards. Results show that replacing the austenitic grade with the lean duplex grade is acceptable.

Effects of Fabrication Processes on the Behavior of S960 Ultra High Strength Steel (UHSS)

Strenx® 960 MC is a direct quenched type of Ultra High Strength Steel (UHSS) with low carbon content. Although this material combines high strength and good ductility, it is highly sensitive towards fabrication processes. The presence of stress concentration due to structural discontinuity or notch will highlight the role of these fabrication effects on the deformation capacity of the material. Due to this, a series of tensile tests are done on both pure base material (BM) and when it has been subjected to Heat Input (HI) and Cold Forming (CF). The surface of the material was dressed by laser beam with a certain speed to study the effect of HI while the CF is done by bending the specimen to a certain angle prior to tensile test. The generated results illustrate the impact of these processes on the deformation capacity of the material, specially, when the material has HI experience due to welding or similar processes. In order to compare the results with those of numerical simulation, LS-DYNA explicit commercial package has been utilized. The generated results show an acceptable agreement between experimental and numerical simulation outcomes.

Effect of loading type on the fatigue strength of symmetric and asymmetric welded joints made of ultra high strength steel

In this study, finite element analyses and experimental tests are carried out in order to investigate the effect of loading type and symmetry on the fatigue strength of three different non-load carrying welded joints. The current codes and recommendations do not give explicit instructions how to consider degree of bending in loading and the effect of symmetry in the fatigue assessment of welded joints. The fatigue assessment is done by using effective notch stress method and linear elastic fracture mechanics. Transverse attachment and cover plate joints are analyzed by using 2D plane strain element models in FEMAP/NxNastran and Franc2D software and longitudinal gusset case is analyzed by using solid element models in Abaqus and Abaqus/XFEM software. By means of the evaluated effective notch stress range and stress intensity factor range, the nominal fatigue strength is assessed. Experimental tests consist of the fatigue tests of transverse attachment joints with total amount of 12 specimens. In the tests, the effect of both loading type and symmetry on the fatigue strength is studied. Finite element analyses showed that the fatigue strength of asymmetric joint is higher in tensile loading and the fatigue strength of symmetric joint is higher in bending loading in terms of nominal and hot spot stress methods. Linear elastic fracture mechanics indicated that bending reduces stress intensity factors when the crack size is relatively large since the normal stress decreases at the crack tip due to the stress gradient. Under tensile loading, experimental tests corresponded with finite element analyzes. Still, the fatigue tested joints subjected to bending showed the bending increased the fatigue strength of non-load carrying welded joints and the fatigue test results did not fully agree with the fatigue assessment. According to the results, it can be concluded that in tensile loading, the symmetry of joint distinctly affects on the fatigue strength. The fatigue life assessment of bending loaded joints is challenging since it depends on whether the crack initiation or propagation is predominant.