Modification of commercial poly-lactide for extrusion coated food packaging applications

Poly-L-lactide (PLLA) is a widely used sustainable and biodegradable alternative to replace synthetic non-degradable plastic materials in the packaging industry. Conversely, its processing properties are not always optimal, e.g. insufficient melt strength at higher temperatures (necessary in extrusion coating processes). This thesis reports on research to improve properties of commercial PLLA grade (3051D from NatureWorks), to satisfy and extend end-use applications, such as food packaging by blending with modified PLLA. Adjustment of the processability by chain branching of commercial poly-L-lactide initiated by peroxide was evaluated. Several well-defined branched structures with four arms (sPLLA) were synthesized using pentaerythritol as a tetra-functional initiator. Finally, several block copolymers consisting of polyethylene glycol and PLLA (i.e. PEGLA) were produced to obtain a well extruded material with improved heat sealing properties. Reactive extrusion of poly-L-lactide was carried out in the presence of 0.1, 0.3 and 0.5 wt% of various peroxides [tert-butyl-peroxybenzoate (TBPB), 2,5-dimethyl-2,5-(tert-butylperoxy)-hexane (Lupersol 101; LOL1) and benzoyl peroxide (BPO)] at 190C. The peroxide-treated PLLAs showed increased complex viscosity and storage modulus at lower frequencies, indicating the formation of branched/cross linked architectures. The material property changes were dependent on the peroxide, and the used peroxide concentration. Gel fraction analysis showed that the peroxides, afforded different gel contents, and especially 0.5 wt% peroxide, produced both an extremely high molar mass, and a cross linked structure, not perhaps well suited for e.g. further use in a blending step. The thermal behavior was somewhat unexpected as the materials prepared with 0.5 wt% peroxide showed the highest ability for crystallization and cold crystallization, despite substantial cross linking. The peroxide-modified PLLA, i.e. PLLA melt extruded with 0.3 wt% of TBPB and LOL1 and 0.5 wt% BPO was added to linear PLLA in ratios of 5, 15 and 30 wt%. All blends showed increased zero shear viscosity, elastic nature (storage modulus) and shear sensitivity. All blends remained amorphous, though the ability of annealing was improved slightly. Extrusion coating on paperboard was conducted with PLLA, and peroxide-modified PLLA blends (90:10). All blends were processable, but only PLLA with 0.3 wt% of LOL1 afforded a smooth high quality surface with improved line speed. Adhesion levels between fiber and plastic, as well as heat seal performance were marginally reduced compared with pure 3051D. The water vapor transmission measurements (WVTR) of the blends containing LOL1 showed acceptable levels, only slightly lower than for comparable PLLA 3051D. A series of four-arm star-shaped poly-L-lactide (sPLLA) with different branch length was synthesized by ring opening polymerization (ROP) of L-lactide using pentaerythritol as initiator and stannous octoate as catalyst. The star-shaped polymers were further blended with its linear resin and studied for their melt flow and thermal properties. Blends containing 30 wt% of sPLLA with low molecular weight (30 wt%; Mwtotal: 2500 g mol-1 and 15000 g mol-1) showed lower zero shear viscosity and significantly increased shear thinning, while at the same time slightly increased crystallization of the blend. However, the amount of crystallization increased significantly with the higher molecular weight sPLLA, therefore the star-shaped structure may play a role as nucleating agent. PLLA-polyethylene glycol–PLLA triblock copolymers (PEGLA) with different PLLA block length were synthesized and their applicability as blends with linear PLLA (3051D NatureWorks) was investigated with the intention of improving heat-seal and adhesion properties of extrusion-coated paperboard. PLLA-PEG-PLLA was obtained by ring opening polymerization (ROP) of L-lactide using PEG (molecular weight 6000 g mol-1) as an initiator, and stannous octoate as catalyst. The structures of the PEGLAs were characterized by proton nuclear magnetic resonance spectroscopy (1H-NMR). The melt flow and thermal properties of all PEGLAs and their blends were evaluated using dynamic rheology, and differential scanning calorimeter (DSC). All blends containing 30 wt% of PEGLAs showed slightly higher zero shear viscosity, higher shear thinning and increased melt elasticity (based on tan delta). Nevertheless, no significant changes in thermal properties were distinguished. High molecular weight PEGLAs were used in extrusion coating line with 3051D without problems.

Improving oral healthcare in Scotland with special reference to sustainability and caries prevention

Brett Duane Improving oral healthcare in Scotland with special reference to sustainability and caries prevention University of Turku, Faculty of Medicine, Institute of Dentistry, Community Dentistry, Finnish Doctoral Program in Oral Sciences (FINDOS-Turku), Turku, Finland Annales Universitatis Turkuensis, Sarja- Ser. D, Medica-Odontologica. Painosalama Oy, Turku, Finland, 2015. Dentistry must provide sustainable, evidence-based, and prevention-focused care. In Scotland oral health prevention is delivered through the Childsmile programme, with an increasing use of high concentration fluoride toothpaste (HCFT). Compared with other countries there is little knowledge of xylitol prevention. The UK government has set strict carbon emission limits with which all national health services (NHS) must comply. The purpose of these studies was firstly to describe the Scottish national oral health prevention programme Childsmile (CS), to determine if the additional maternal use of xylitol (CS+X) was more effective at affecting the early colonisation of mutans streptococci (MS) than this programme alone; secondly to analyse trends in the prescribing and management of HCFT by dentists; and thirdly to analyse data from a dental service in order to improve its sustainability. In all, 182 mother/child pairs were selected on the basis of high maternal MS levels. Motherswere randomly allocated to a CS or CS+X group, with both groups receiving Childsmile. Theintervention group consumed xylitol three times a day, from when the child was 3 months until 24 months. Children were examined at age two to assess MS levels. In order to understand patterns of HCFT prescribing, a retrospective secondary data analysis of routine prescribing data for the years 2006-2012 was performed. To understand the sustainability of dental services, carbon accounting combined a top-down approach and a process analysis approach, followed by the use of Pollard’s decision model (used in other healthcare areas) to analyse and support sustainable service reconfiguration. Of the CS children, 17% were colonised with MS, compared with 5% of the CS+X group. This difference was not statistically significant (P=0.1744). The cost of HCFT prescribing increased fourteen-fold over five years, with 4% of dentists prescribing 70% of the total product. Travel (45%), procurement (36%) and building energy (18%) all contributed to the 1800 tonnes of carbon emissions produced by the service, around 4% of total NHS emissions. Using the analytical model, clinic utilisation rates improved by 56% and patient travel halved significantly reducing carbon emissions. It can be concluded that the Childsmile programme was effective in reducing the risk for MS transmission. HCFT is increasing in Scotland and needs to be managed. Dentistry has similar carbon emissions proportionally as the overall NHS, and the use of an analytic tool can be useful in helping identify these emissions. Key words: Sustainability, carbon emissions, xylitol, mutans streptococci, fluoride toothpaste, caries prevention.

Perfluorattuja yhdisteitä sisältävien jätevesien puhdistus- ja analyysimenetelmät

Perfluoratut alkyyliyhdisteet eli PFAS-yhdisteet ovat synteettisiä orgaanisia yhdisteitä, joissa on fluorattu hiiliketju. Hiilen ja fluorin väliset vahvat sidokset ovat muodostuneet ongelmaksi jätevedenpuhdistamoilla, sillä yhdisteet eivät hajoa puhdistamoilla käytössä olevilla vedenpuhdistusmenetelmillä. Yhdisteitä kertyy luontoon jätevesien mukana. Kandidaatintyössä on vertailtu yhdisteitä sisältävien vesien käsittelymenetelmiä parhaiten soveltuvan menetelmän löytämiseksi. Menetelmien kustannuksia tai soveltuvuutta vedenpuhdistamomittakaavan prosessiksi ei ole arvioitu. Lisäksi työssä on koottu yhdisteitä sisältävien jätevesien analysointiin sopivia analyysimenetelmiä. Soveltuvat puhdistus- ja analyysimenetelmät on esitelty uusien tieteellisten artikkelien pohjalta. Mahdollisia erotusmenetelmiä ovat membraanierotus ja sorptio. Membraaneista soveltuvimpia ovat nanosuodatus- ja käänteisosmoosimembraanit, joilla erottuvat jopa 0,0001 μm:n kokoiset partikkelit. PFAS-yhdisteet voidaan erottaa sorptiolla muun muassa aktiivihiileen. Yhdisteiden rakenne hajoaa nykyaikaisilla hapetusmenetelmillä ja polttamalla lietteen mukana. Hapettaminen permanganaatin avulla ei tuottanut hyvää tulosta, mutta fotokemiallisella hapetuksella ja alhaisen lämpötilan plasmatekniikalla (NTP) yhdisteiden rakenne hajosi lähes kokonaan. Fotokemiallinen hapetus onnistui erityisesti perfluorokarboksyylihapoilla, joiden rakenne hajosi jopa kolmessa tunnissa. Yleisimmin käytetty analyysimenetelmä on nestekromatografin ja massaspektrometrin yhdistelmä (LC-MS/MS) ja matriisivaikutus minimoidaan tyypillisesti kiinteäfaasiuutolla (SPE). Työssä esitellyistä käsittelymenetelmistä parhaiten soveltuva on NTP-menetelmä, koska sillä saatiin tutkimusten mukaan hajotettua yhdisteiden rakenne muita menetelmiä lyhyemmässä ajassa ja se soveltuu parhaiten kaikille PFAS-yhdisteille. NTP-menetelmässä ei tarvita katalyyttiä tai lisäkemikaaleja. Voimakkaana hapettimena toimivat epästabiilit hydroksyyliradikaalit, jotka syntyvät koronapurkauksen kautta. Koronapurkauksessa muodostuu myös otsonia ja lisäksi vapaa happi voi tehostaa hapettumista. Menetelmässä muodostuvien hajoamistuotteiden hallinta vaatii lisätutkimusta. Mahdollinen hallintakeino voisi olla esimerkiksi hapettumisessa vapautuvien fluoridi-ionien saostaminen. Muodostuvien hajoamistuotteiden toksisuutta voitaisiin tarkkailla biosensorilla.