Influence of Heat Treatment on Strength Properties of Finger-jointed Components

The purpose for the thesis was to study the thermo treatment of finger-jointed wood. The thesis concentrated on examining the tensile and bending strength of finger-jointed and thermo treated wood. The aim was to find out how different treatment temperature levels and adhesives influence the strength of wood that has been finger-jointed before heat treatment. Secondary objectives were to examine the influence of the treatment time at one temperature, determine differences in the strength between the joints in heartwood and sapwood, examine the visual appearance of the finger joints after the treatment and establish possibilities to reach a characteristic strength level corresponding to C14. Only minor differences in strength properties were measured between the finger-jointed wood treatments II and III. A greater difference was shown between these two treatment temperatures I, which lead to reduced strength. The average strength of joints glued with adhesive 2 was higher after treatments II and III compared to those glued with the adhesive 1. At the treatment temperature I, the adhesive 1 strength properties were at the same level compared to the adhesive 2 or better. There were not any significant differences.

Sormijatketun rakennesahatavaran lujuuteen vaikuttavat tekijät puun jatkojalostuksessa

Diplomityö tehtiin Stora Enson Kiteen sahalla, tuotantokäytössä olevaa sormijatkoslinjaa tutkien. Tutkimuksen tavoitteena oli selvittää raaka-aineen keskikosteuden, kosteusgradientin, mitallistamishöyläyksen ja liitettävien aihioiden pituuden vaikutus jatketun tuotteen laatuun. Koekappaleita valmistettiin viisi höylättyä ja viisi sahapintaista luokkaa. Luokat valmistettiin eripituisista aihioista, puolen metrin jaolla. Koekappaleiden taivutuslujuus mitattiin nelipistetaivutuksella, standardin EN 408 mukaan. Taivutuskokeen jälkeen kappaleista mitattiin keskikosteus ja sahattiin koepalat kosteusgradientin mittaamiseksi. Koekappaleita valmistettiin yhteensä 37.8 m3. Tutkimuksissa selvisi, että kappaleiden keskikosteuden ja taivutuslujuuden välillä vallitsee heikko positiivinen riippuvuus. Kosteusgradientin ja taivutuslujuuden välillä riippuvuus on selkeämpi, kosteusgradientin kasvaessa myös taivutuslujuus lisääntyy. Tämä selittyy kappaleiden tiheyden vaihtelulla. Tiheämpiin kappaleisiin jää kuivauksessa suurempi kosteusgradientti. Aihioiden mitallistaminen pienentää taivutuslujuuden hajontaa ja vähentää raaka-aineen mittaheittojen aiheuttamia häiriöitä tuotannossa. Aihionpituus vaikuttaa murtumatyyppien jakaumiin ja aihioiden kierouteen. Sopivin aihionpituus on tässä tapauksessa 0.8-1.0 m. Puolet kappaleista murtui liitoksen ulkopuolelta, useimmiten oksan kohdalta. Paras tapa parantaa kappaleiden lujuutta on lujuuslajitella raaka-aine.

Puukuitulujitteiset muovikomposiitit puunjalostusteollisuudessa

Puukuitulujitteisten muovikomposiittien käyttömäärät ovat maailmanlaajuisesti kasvaneet jatkuvasti viimeisen 15 vuoden aikana.Kasvun on ennustettu jatkuvan voimakkaana myös tulevaisuudessa. Diplomityön tavoitteena oli selvittää puukuitulujitteisten muovikomposiittimateriaalien soveltuvuus erääseen, mahdollisesti rakennusteollisuuden käyttöön tulevaan, tuotteeseen. Tutkittaviksi materiaaliyhdistelmiksi valittiin sekä kerta- että kestomuovin ja puu- jauhon seos. Puujauho oli koivupuista sahaus- ja hiontajätettä. Molemmissa tapauksissa puun osuus komposiitissa oli 30 p-%. Koekappaleiden valmistuksessakäytettiin koivupuisia muotteja, joihin materiaali annosteltiin. Kertamuovin japuujauhon seos kovettui huoneenlämmössä. Kestomuovin ja puujauhon seoksen sulatukseen käytettiin lämmitettävillä puristinlevyillä varustettua aihiopuristinta. Koekappaleille määritettiin taivutuslujuudet taivutuskokeen avulla. Koekappaleiden taivutuslujuuksia verrattiin mm. lattialastulevyn ja koivuliimalevyn arvoihin. Liimalevyn taivutuslujuus muihin verrattuna oli huomattavasti suurempi. Komposiittimateriaalista valmistettujen koekappaleiden taivutuslujuus oli lähellä lattia-lastulevyn tasoa, osittain jonkin verran parempikin. Diplomityössä saatujen tulosten perusteella voidaan todeta puukuitulujitteisilla muovikomposiiteilla olevan kehityspotentiaalia myös tutkimuskohteen tyyppisissä ratkaisuissa. Jatkotutkimusta tulisi kohdistaa ennen kaikkea kestomuovipohjaisen komposiittimateriaalinsuuntaan.

Viilujen lujuuslajittelun kehittäminen

Työn lähtökohtana on viilujen lujuuslajittelun kehittäminen. Lujuuslajittelun on tarkoitus perustua viilujen paino- ja tiheyseroihin, joilla on vaikutusta viilujen lujuusominaisuuksiin. Viilujen paino- ja tiheyserojen selvittäminen on tarkoi-tus toteuttaa punnituksen avulla ja siihen kuuluva laitteisto oli jo alustavasti suunniteltu. Teoriaosan avulla tutustuttiin viilujen ja vanerin valmistukseen liittyviin pro-sesseihin, puun tiheyteen ja lujuuteen liittyviin tekijöihin ja eri tekijöiden vaikutuksiin viilujen ja vanereiden lujuusominaisuuksissa. Työn kokeellinen osa voidaan jakaa selkeästi kahteen tutkimusalueeseen. Ensimmäisessä oli tarkoitus selvittää viiluissa esiintyvien paino- ja tiheyserojen vaihteluita ja niiden vaikutuksia viilujen lujuusominaisuuksiin ja sitä kautta myös valmiiden levyrakenteiden ominaisuuksiin. Viilutasolla tutkittiin tiheyden vaikutusta poikittaisveto- ja taivutuslujuuteen ja vaneritasolla tiheyden vaikutusta taivutuslujuu-teen. Raaka-aineina tutkimuksissa ja lujuuskokeissa käytettiin koivu-, kuusi- ja poppeliviiluja. Työn toinen osa keskittyi viilujen punnituksen testaamiseen ja kehittämiseen. Tutkittavien puulajien kohdalla viiluista löytyi huomattavia paino- ja tiheyseroja, joiden vaikutukset näkyivät erityisesti viilujen ja vanerien taivutuslujuuksien arvoissa. Punnituksen tulokset osoittivat, että riittävän tuotekehityksen myötä viilujen punnitukseen perustuva lajittelu olisi mahdollista toteuttaa tutkitun menetelmän avulla. Vanerirakenteissa havaittujen taivutuslujuuserojen perusteella lujuuslajittelulle olisi käyttöä ja siitä olisi hyötyä levyrakenteiden suunnittelussa.

Ekologisen kuorilevyn valmistaminen puunjalostusteollisuuden sivutuotteista

Puunjalostusteollisuudessa syntyy huomattavia määriä sivutuotteita, joiden hyödyntäminen on vielä vajavaista. Sahajauhon ja puukuoren pääasiallinen käyttö rajoittuu energiantuotantoon eli polttamiseen voimalaitoksissa. Selostettavassa tutkimustyössä, joka on tehty Lappeenrannan teknillisen yliopiston puunjalostustekniikan levylaboratoriossa, on pyritty selvittämään kotimaisten kuusi-, mänty- ja koivukuorten käyttömahdollisuuksia raaka-aineina lastulevyn tapaan ns. ekologisen kuorilevyn valmistamisessa, mutta ilman liimaa. Tutkimusmateriaalina käytettiin puunjalostusteollisuudesta hankittua tuoretta kuusen ja männyn rumpukuorintajätettä sekä koivun roottorikuorintajätettä, joista kukin raaka-aine pienennettiin kahteen eri partikkelikokoon käyttäen oksasilppuria ja vasaramyllyä. Raaka-ainemäärät mitattiin ja kaadettiin viiran päällä olevaan puusta valmistettuun muottiin ja muotin poisnostamisen jälkeen levyaihio puristettiin 1-välikuumapuristimessa sykleittäin. Valmistetut kuorilevyt olivat 1 -kerroksisia. Koelevyistä tutkittiin kosteuspitoisuus, tilavuuspaino, taivutuslujuus ja Brinell -kovuus.Saadut tulokset osoittavat, että kuusen, männyn ja koivun kuoresta voidaan valmistaa kuorilevyä ilman liima-ainetta, sillä puukuoren sisältämät omat liimaavuutta parantavat uuteaineet antavat riittävän vaikutuksen kuorilevyn rakenteen stabiloimiseksi. Tällaisen kuorilevyn taivutuslujuus on kuitenkin huomattavasti heikompi kuin puulastulevyllä. Kaikki jauhetusta raaka-aineesta sekä pelkästään silputusta koivuraaka-aineesta valmistetut kuorilevyt täyttävät taivutuslujuuden osalta kuitenkin huokoiselle, A-lujuusluokan standardi-kuitulevylle asetetut vaatimukset. Tarkasteltaessa eri raaka-aineista valmistettujen levyjen ominaisuuksia, voidaan todeta, että tilavuuspainoltaan suurinta sekä kovuudeltaan ja taivutuslujuudeltaan parasta levyä saadaan valmistettua jauhetusta koivukuoresta. Jokaisen valmistetun kuorilevyn kovuusarvo ylittää Suomen johtavan lastulevyn valmistajan lastulevyn kovuusarvon lukuun ottamatta pelkästään silputuista kuusi- ja mäntykuorista valmistettuja levyjä.Vaikka tulokset ovat suuntaa-antavia, osoittavat ne selvästi millaisia mahdollisuuksia tarjoaa puun kuoren tai sahajauhon käyttäminen lastulevyn tapaan valmistettavien levyjen raaka-aineena. Koko tutkimuskenttä on tässä käsiteltävänä olevalla alueella varsin laaja, ja tässä tutkimuksessa selvitetyt asiat ovat siitä vain pieni osa antaen kuitenkin suunnan useille tärkeille jatkossa selvitettäville asioille. Näistä mainittakoon mm. ekologisen levyn jatkojalostus ja tuotesuunnittelu, levyn valmistuksen taloudellisuus ja tuotteiden markkinointi, kuorilevyn valmistusprosessin kehittäminen sekä eri raaka-aineyhdistelmien kokeilu kuorilevyn raaka-aineena.

Puupohjaisten kuitukomposiittien materiaalitekniset mahdollisuudet veneteollisuudessa

Tämän diplomityön tavoitteena oli selvittää puupohjaisten kuitukomposiittimateriaalien soveltuvuutta veneteollisuuden valmistusmateriaaliksi. Huviveneiden rakennusta säätelee huvivenedirektiivi ja lukuisat standardit. Standardien mukaan uusien materiaalien käyttö veneenrakennuksessa on mahdollista, mikäli materiaalin ominaisuudet todetaan muun muassa laboratoriotesteissä soveltuviksi kyseiseen käyttötarkoitukseen. Tutkimusta varten valmistettiin kuusi erilaista kuitukomposiittimateriaalia. Tutkimuksessa käytettiin myös neljän kaupallisen puumuovikomposiittivalmistajan materiaalia. Vertailumateriaaleiksi valittiin puuraaka-aineista mänty, saarni ja mahonki sekä muoviraakaaineista ABS – muovi. Tarkisteltaville materiaaleille määriteltiin standardien mukaisin testein taivutuslujuus, vetolujuus, Charpy – iskulujuus, Brinell – kovuus, veden absorptio sekä paksuusturpoama. Saatuja arvoja vertailtiin vertailumateriaalien kirjallisuudessa mainittuihin arvoihin. Puupohjaisten kuitukomposiittien ominaisuudet jäivät vertailumateriaalien vastaavista lukuun ottamatta Brinell – kovuutta. Taivutus- ja vetolujuuden osalta eräiden kaupallisten puumuovikomposiittivalmistajien ilmoittamat lujuusarvot olivat lähellä veneenrakennuksessa käytettyjen materiaalien vastaavia. Suurimpana yksittäisenä haasteena puukuitupohjaisilla kuitukomposiiteilla havaittiin Charpy – iskulujuus. Myös veden absorption saattaminen alhaiseksi havaittiin tärkeäksi veneilysovelluksissa. Ominaisuuksien kehittäminen on kuitenkin käytettävissä olevan tutkimustiedon perusteella mahdollista. Diplomityössä saatujen tulosten perusteella on puupohjaisilla kuitukomposiiteilla potentiaalia veneteollisuudessa. Jatkotutkimusta tulisikin kohdistaa materiaalin ominaisuuksien kehittämiseen.

A novel procedure for establishing clinching parameters for high strength steel sheet

The building industry has a particular interest in using clinching as a joining method for frame constructions of light-frame housing. Normally many clinch joints are required in joining of frames.In order to maximise the strength of the complete assembly, each clinch joint must be as sound as possible. Experimental testing is the main means of optimising a particular clinch joint. This includes shear strength testing and visual observation of joint cross-sections. The manufacturers of clinching equipment normally perform such experimental trials. Finite element analysis can also be used to optimise the tool geometry and the process parameter, X, which represents the thickness of the base of the joint. However, such procedures require dedicated software, a skilled operator, and test specimens in order to verify the finite element model. In addition, when using current technology several hours' computing time may be necessary. The objective of the study was to develop a simple calculation procedure for rapidly establishing an optimum value for the parameter X for a given tool combination. It should be possible to use the procedure on a daily basis, without stringent demands on the skill of the operator or the equipment. It is also desirable that the procedure would significantly decrease thenumber of shear strength tests required for verification. The experimental workinvolved tests in order to obtain an understanding of the behaviour of the sheets during clinching. The most notable observation concerned the stage of the process in which the upper sheet was initially bent, after which the deformation mechanism changed to shearing and elongation. The amount of deformation was measured relative to the original location of the upper sheet, and characterised as the C-measure. By understanding in detail the behaviour of the upper sheet, it waspossible to estimate a bending line function for the surface of the upper sheet. A procedure was developed, which makes it possible to estimate the process parameter X for each tool combination with a fixed die. The procedure is based on equating the volume of material on the punch side with the volume of the die. Detailed information concerning the behaviour of material on the punch side is required, assuming that the volume of die does not change during the process. The procedure was applied to shear strength testing of a sample material. The sample material was continuously hot-dip zinc-coated high-strength constructional steel,with a nominal thickness of 1.0 mm. The minimum Rp0.2 proof stress was 637 N/mm2. Such material has not yet been used extensively in light-frame housing, and little has been published on clinching of the material. The performance of the material is therefore of particular interest. Companies that use clinching on a daily basis stand to gain the greatest benefit from the procedure. By understanding the behaviour of sheets in different cases, it is possible to use data at an early stage for adjusting and optimising the process. In particular, the functionality of common tools can be increased since it is possible to characterise the complete range of existing tools. The study increases and broadens the amount ofbasic information concerning the clinching process. New approaches and points of view are presented and used for generating new knowledge.

Narrow Gap flux-cored arc welding of high strength shipbuilding steels

This thesis is part of the Arctic Materials Technologies Development –project. The research of the thesis was done in cooperation with Arctech Helsinki Shipyard, Lappeenranta University of Technology and Kemppi Oy. Focus of the thesis was to study narrow gap flux-cored arc welding of two high strength steels with three different groove angles of 20°, 10° and 5°. Welding of the 25 mm thick E500 TMCP and 10 mm thick EH36 steels was mechanized and Kemppi WisePenetration and WiseFusion processes were tested with E500 TMCP steel. EH36 steel test pieces were welded without Wise processes. Shielding gases chosen were carbon dioxide and a mixture of argon and carbon dioxide. Welds were tested with non-destructive and destructive testing methods. Radiographic, visual, magnetic particle and liquid penetrant testing proved that welds were free from imperfections. After non-destructive testing, welds were tested with various destructive testing methods. Impact strength, bending, tensile strength and hardess tests proved that mechanized welding and Wise processes produced quality welds with narrower gap. More inconsistent results were achieved with test pieces welded without Wise processes. Impact test results of E500 TMCP exceeded the 50 J limit on weld, set by Russian Maritime Register of Shipping. EH36 impact test results were much closer to the limiting values of 34 J on weld and 47 on HAZ. Hardness values of all test specimens were below the limiting values. Bend testing and tensile testing results fulfilled the the Register requirements. No cracking or failing occurred on bend test specimens and tensile test results exceeded the Register limits of 610 MPa for E500 TMCP and 490 MPa for EH36.

Effects of Fabrication Processes on the Behavior of S960 Ultra High Strength Steel (UHSS)

Strenx® 960 MC is a direct quenched type of Ultra High Strength Steel (UHSS) with low carbon content. Although this material combines high strength and good ductility, it is highly sensitive towards fabrication processes. The presence of stress concentration due to structural discontinuity or notch will highlight the role of these fabrication effects on the deformation capacity of the material. Due to this, a series of tensile tests are done on both pure base material (BM) and when it has been subjected to Heat Input (HI) and Cold Forming (CF). The surface of the material was dressed by laser beam with a certain speed to study the effect of HI while the CF is done by bending the specimen to a certain angle prior to tensile test. The generated results illustrate the impact of these processes on the deformation capacity of the material, specially, when the material has HI experience due to welding or similar processes. In order to compare the results with those of numerical simulation, LS-DYNA explicit commercial package has been utilized. The generated results show an acceptable agreement between experimental and numerical simulation outcomes.

Effect of loading type on the fatigue strength of symmetric and asymmetric welded joints made of ultra high strength steel

In this study, finite element analyses and experimental tests are carried out in order to investigate the effect of loading type and symmetry on the fatigue strength of three different non-load carrying welded joints. The current codes and recommendations do not give explicit instructions how to consider degree of bending in loading and the effect of symmetry in the fatigue assessment of welded joints. The fatigue assessment is done by using effective notch stress method and linear elastic fracture mechanics. Transverse attachment and cover plate joints are analyzed by using 2D plane strain element models in FEMAP/NxNastran and Franc2D software and longitudinal gusset case is analyzed by using solid element models in Abaqus and Abaqus/XFEM software. By means of the evaluated effective notch stress range and stress intensity factor range, the nominal fatigue strength is assessed. Experimental tests consist of the fatigue tests of transverse attachment joints with total amount of 12 specimens. In the tests, the effect of both loading type and symmetry on the fatigue strength is studied. Finite element analyses showed that the fatigue strength of asymmetric joint is higher in tensile loading and the fatigue strength of symmetric joint is higher in bending loading in terms of nominal and hot spot stress methods. Linear elastic fracture mechanics indicated that bending reduces stress intensity factors when the crack size is relatively large since the normal stress decreases at the crack tip due to the stress gradient. Under tensile loading, experimental tests corresponded with finite element analyzes. Still, the fatigue tested joints subjected to bending showed the bending increased the fatigue strength of non-load carrying welded joints and the fatigue test results did not fully agree with the fatigue assessment. According to the results, it can be concluded that in tensile loading, the symmetry of joint distinctly affects on the fatigue strength. The fatigue life assessment of bending loaded joints is challenging since it depends on whether the crack initiation or propagation is predominant.

Release of soil phosphorus during runoff as affected by ionic strength and temperature

Selostus: Ympäristöolosuhteiden vaikutus maan fosforin liukenemiseen pintavalunnan aikana

Statistical variation of weld profiles and their expected influence on fatigue strength

The general objective of this study was to conduct astatistical analysis on the variation of the weld profiles and their influence on the fatigue strength of the joint. Weld quality with respect to its fatigue strength is of importance which is the main concept behind this thesis. The intention of this study was to establish the influence of weld geometric parameters on the weld quality and fatigue strength. The effect of local geometrical variations of non-load carrying cruciform fillet welded joint under tensile loading wasstudied in this thesis work. Linear Elastic Fracture Mechanics was used to calculate fatigue strength of the cruciform fillet welded joints in as-welded condition and under cyclic tensile loading, for a range of weld geometries. With extreme value statistical analysis and LEFM, an attempt was made to relate the variation of the cruciform weld profiles such as weld angle and weld toe radius to respective FAT classes.

The influence ofvariable amplitude loading on the fatigue strength of rhs corners

Rectangular hollow section (RHS) members are components widely used in engineering applications because of their good-looking, good properties in engineering areas and inexpensive cost comparing to members with other sections. The increasing use of RHS in load bearing structures makes it necessary to analyze the fatigue behavior of the RHS members. In this thesis, concentration will be given to the fatigue behavior of the RHS members under variable amplitude pure torsional loading. For the RHS members, failure will normally occur in the corner region if the welded regions are under full penetration. This is because of the complicated stress components' distributions at the RHScorners, where all of three fracture mechanics modes will happen. Mode I is mainly caused by the residual stresses that caused by the manufacturing process. Modes II and III are caused by the applied torsional loading. Stress based Findleymodel is also used to analyze the stress components. Constant amplitude fatigue tests have been done as well as variable amplitude fatigue tests. The specimens under variable amplitude loading gave longer fatigue lives than those under constant amplitude loading. Results from tests show an S-N curvewith slope around 5.

Constant and variable amplitude fatigue strength of high strength steel welds treated with ultrasonic impact treatment

Hitsattujen rakenteiden väsymiskestävyyttä pystytään parantamaan jälkikäsittelymenetelmillä, joistayksi, ultraäänikäsittely muokkaa hitsin geometriaa ja aiheuttaa puristusjäännösjännitystilan. Tässä tutkimuksessa verrataan kokeellisesti kuormaa kantamattoman hitsatun ja ui -käsitellyn rivan väsymislujuutta toisiinsa. Tutkimusohjelmaan kuuluu kahta teräslajia ja sekä vakio - että vaihtuva - amplitudista kuormitusta. Ultraäänikäsittelyllä saavutetaan väsymiskestoiän parantuminen vakio - ja vaihtuva - amplitudisella kuormituksella. Perusaineen lujuudella ei ole merkittää vaikutusta väsymislujuuteen kun liitos on hitsatussa tilassa. Tällöin väsymiskestävyyden määrää hitsin rajaviivan jännityskeskittymä. Ultraäänikäsitellyn hitsatunliitoksen väsymiskestävyys on suurempi korkeamman lujuuden omaavilla teräksillä. Tästä syystä korkealujuuksisten terästen käyttö ultraäänikäsiteltynä väsyttävästi kuormitetuissa kevytrakenteissa on perusteltua.

Mangaaniseosteisen duplex-teräksen hitsattavuus

Diplomityön tavoitteena oli selvittää mangaaniseosteisen LDX2101 duplex-teräksen ja LDX2101 hitsauslisäaineiden hitsausparametrit puikkohitsaus-, MAG-täytelankahitsaus- ja plasmahitsausprosessilla. Toisena tavoitteena oli selvittää lämmöntuonnin vaikutuksia hit-sausliitosten mekaanisiin ominaisuuksiin, iskusitkeyteen (-40 °C) ja ferriitti- / austeniittipitoi-suuksien jakaantumiseen. Tutkittavat hitsit olivat päittäishitsejä ja koelevyjen aineenpaksuus oli 6 mm. Koetulosten perusteella tehtiin hitsausohjeet kyseisille hitsausprosesseille. Työn kirjallisessa osassa on selvitetty yleisesti duplex-terästen käyttökohteita, mekaanisia ja kemiallisia ominaisuuksia sekä duplex-terästen korroosio-ominaisuuksia. Lisäksi on käsitelty eri hitsausprosesseja ja duplex-terästen hitsattavuutta, jossa selvitetään mm. terästen jähmet-tymistä, erkaumia ja faaseja, lämmöntuonnin vaikutuksia ja hitsausliitosten korroosionkestä-vyyttä. Teoriaosassa on kerrottu myös hitsausliitosten tarkastuksesta ja hitsiluokista. Työn kokeellisessa osassa esitellään kokeiden suoritus sekä ainetta rikkova ja ainetta rikko-maton tarkastus. Liitoksille suoritettava koestusohjelma noudatti pääosin menetelmäkoestan-dardin SFS-EN 15614-1 ohjetta. Hitseille tehtiin ainetta rikkomaton tarkastus, joka käsittää silmämääräisen tarkastuksen, pintatarkastuksen ja röntgentarkastuksen. Rikkovaa aineen-koetusta tehtiin sisältäen kovuusmittaukset, vetokokeet, taivutuskokeet jaiskusitkeyskokeet. Lisäksi valmistettiin metallografiset hieet, joita tutkimalla selvitettiin hitsausliitoksen metal-lurgiaa ja määriteltiin ferriitti- ja austeniittipitoisuudet. Kokeiden perusteella on laadittu hit-sausohjeet kullekin hitsausprosessille. Lisäksi kokeellisessa osassa on esitelty tulokset syö-pymäkokeesta, jossa selvitettiin eri materiaalien syöpymiskestävyyttä valkolipeäliuoksessa. Tutkimustuloksien perusteella LDX2102 duplex-materiaali onhyvin hitsattavaa laajalla hit-sausparametrialueella. Mekaaniset ominaisuudet, kuten lujuus- ja iskusitkeysarvot täyttävät materiaalistandardin SFS-EN10028-7 niille asettamat vaatimukset. Taivutussitkeys ja murto-venymät jäivät kuitenkin osalla koekappaleista vaatimustasoa alhaisemmiksi. Austeniitti- ja ferriittipitoisuudet vastaavat materiaalistandardin vaatimuksia.