Abrasion of Aggregates as Affected by Grading, 1970

Many specifications for coarse aggregates, that are to be used in highway construction, limit the percentage of wear when tested by AASHO T-96 "Resistance to Abrasion of Coarse Aggregate by use of the Los Angeles Machine". This test consists of placing a 5000 gram sample of the aggregate in a "hollow steel cylinder, closed at both ends, having an inside diameter of 28 inches and an inside length of 20 inches. The cylinder - - - shall be mounted in such a manner that it may be rotated with the axis in a horizontal position. - A removable steel shelf, projecting radially 3-1/2 inches into the cylinder and extending its full length, shall be mounted along one element of the interior surface of the cylinder."

A Laboratory Evaluation of Tungsten Carbide Inserts for Snowplow Blades, MLR-95-6, 1996

Tungsten carbide used in snowplow blades was studied from three manufacturers. The carbides were measured for common industry properties including specific gravity and hardness. In addition, an abrasion resistance was performed. There was no significant difference found in abrasion resistance between the Kenametal and the Valk carbides. The Bucyrus carbides showed improved abrasion resistance, but were outside industry specifications for specific gravity.

Performance Evaluation of Concrete Pavement Granular Subbase - Pavement Surface Condition Evaluation, TR-554, 2008

This research project covered a wide range of activities that allowed researchers to understand the relationship between stability, pavement distress, and recycled portland cement concrete (RPCC) subbase aggregate materials. Detailed laboratory and field tests, including pavement distress surveys, were conducted at 26 sites in Iowa. Findings show that specific gravities of RPCC are lower than those of crushed limestone. RPCC aggregate material varies from poorly or well-graded sand to gravel. A modified Micro-Deval test procedure showed that abrasion losses of virgin aggregate materials were within the maximum Micro-Deval abrasion loss of 30% recommended by ASTM D6028-06. Micro-Deval abrasion loss of RPCC aggregate materials, however, was much higher than that of virgin materials and exceeded 30% loss. Modulus of elasticity of RPCC subbase materials is high but variable. RPCC subbase layers normally have low permeability. The pavement surfaces for both virgin and RPCC subbase across Iowa were evaluated to fulfill the objectives of this study related to field evaluation. Visual distress surveys were conducted to gather the detailed current pavement condition information including the type, extent, and severity of the pavement distresses. The historical pavement condition information for the surveyed field sections was extracted from the Iowa DOT's Pavement Management Information System (PMIS). The current surface condition of existing field pavements with RPCC subbase was compared with the virgin aggregate subbase sections using two different approaches. The changes in pavement condition indices (PCI and IRI) with time for both types of pavements (subbases) were compared.

Examination of Curing Criteria for Cold In-Place Recycling, TR-553, 2008

Cold In-Place Recycling (CIR) has been used widely in rehabilitating the rural highways because it improves a long-term pavement performance. A CIR layer is normally covered by a hot mix asphalt (HMA) overlay in order to protect it from water ingress and traffic abrasion and obtain the required pavement structure and texture. Curing is the term currently used for the period of time that a CIR layer should remain exposed to drying conditions before an HMA overlay is placed. The industry standard for curing time is 10 days to 14 days or a maximum moisture content of 1.5 percent, which appear to be very conservative. When the exposed CIR layer is required to carry traffic for many weeks before the wearing surface is placed, it increases the risk of a premature failure in both CIR layer and overlay. This study was performed to explore technically sound ways to identify minimum in-place CIR properties necessary to permit placement of the HMA overlay. To represent the curing process of CIR pavement in the field construction, three different laboratory curing procedures were examined: 1) uncovered, 2) semi-covered and 3) covered specimens. The indirect tensile strength of specimens in all three curing conditions did not increase during an early stage of curing but increased during a later stage of curing usually when the moisture content falls below 1.5%. Dynamic modulus and flow number increased as curing time increased and moisture contents decreased. For the same curing time, CIR-foam specimens exhibited the higher tensile strength and less moisture content than CIR-emulsion. The laboratory test results concluded that the method of curing temperature and length of the curing period significantly affect the properties of the CIR mixtures. The moisture loss index was developed to predict the moisture condition in the field and, in the future, this index be calibrated with the measurements of temperature and moisture of a CIR layer in the field.