Evaluation of the Chemical Durability of Iowa Fly Ash Concretes, HR-327, Phase II Progress Report, 1992

The major objective of this research project is to investigate how fly ash influences the chemical durability of portland cement based materials. The testing program is evaluating how Iowa fly ashes influence the sulfate durability of portland cement-fly ash pastes, mortars, and concretes. Also, alkali-reactivity studies are being conducted on mortar bar specimens prepared in accordance with ASTM C 311. Prelimary sulfate test results, based only on mortar bar studies, indicate that only the very high-calcium fly ash (29 percent CaO, by weight) consistently reduced the durability of test specimens exposed to a solution containing 5 percent sodium sulfate. The remaining four fly ashes that were used in the study showed negligible to dramatic increases in sulfate resistance. Concrete specimens were only beginning to respond to the sulfate solutions after about one year of exposure; and hence, considerably more time will be needed to assess their performance. Preliminary results from the alkali-reactivity tests have indicated that the Oreopolis aggregate is not sensitive to alkali attack. However, some of the test results have indicated that the testing procedure may be prone to delayed expansion due to the presence of periclase (MgO) in the Class C fly ashes. Research is being planned to: (1) verify if the periclase is influencing test results; and (2) estimating the magnitude of the potential error.

Evaluation and Testing of a Lightweight Fine Aggregate Concrete Bridge Deck in Buchanan County, Iowa, TR-648, 2016

Internal curing is a relatively new technique being used to promote hydration of Portland cement concretes. The fundamental concept is to provide reservoirs of water within the matrix such that the water does not increase the initial water/cementitious materials ratio to the mixture, but is available to help continue hydration once the system starts to dry out. The reservoirs used in the US are typically in the form of lightweight fine aggregate (LWFA) that is saturated prior to batching. Considerable work has been conducted both in the laboratory and in the field to confirm that this approach is fundamentally sound and yet practical for construction purposes. A number of bridge decks have been successfully constructed around the US, including one in Iowa in 2013. It is reported that inclusion of about 20% to 30% LWFA will not only improve strength development and potential durability, but, more importantly, will significantly reduce shrinking, thus reducing cracking risk. The aim of this work was to investigate the feasibility of such an approach in a bridge deck.

Evaluation of the Chemical Durability of Iowa Fly Ash Concretes, HR-327, Phase I Progress Report, 1991

The following report summarizes research activities conducted on Iowa Department of Transportation Project HR-327, for the period April 1, 1990 through March 31, 1991. The purpose of this research project is to investigate how fly ash influences the chemical durability of portland cement based materials. The goal of this research is to utilize the empirical information obtained from laboratory testing to better estimate the durability of portland cement concrete pavements (with and without fly ash) subjected to chemical attack via the natural environment or the application of deicing salts. This project is being jointly sponsored by the Iowa Department of Transportation and the Iowa Fly Ash Affiliate Research group. The research work is also being cooperatively conducted by Iowa State University and Iowa Department of Transportation research personnel. Researchers at Iowa State University are conducting the paste and mortar studies while Iowa Department of Transportation researchers are conducting the concrete study.