A Study of the Relative Durability and Drying Shrinkage of Concrete using Various Retarders, R-234, 1971

A number of concrete admixtures are presently used in various concretes principally for water reduction, retardation, or air entrainment. Whereas the use of these admixtures in concrete placement is well documented, there is limited information showing their effects on durability and drying shrinkage. Since the durability and the shrinkage of concrete can have a pronounce effect on a structures longevity, wear characteristics, and reaction to loading, it is desirable to know the relative effects of different admixtures prior to concrete placement. The purpose of this study is to provide information which could be used to establish durability and shrinkage criterion for evaluating the admixtures currently in use and those whose use may be proposed.

Drying Shrinkage in P.C. Concrete, MLR-89-5, 1990

Crack formation has been a problem on some recently constructed bridges in Iowa. Drying shrinkage has been considered a contributing factor in that cracking. The study was undertaken to evaluate some of those material properties that contribute to the magnitude of drying shrinkage. Cement content, cement composition, fly ash and retarding admixture were the factors studied. Concrete prisms were cast for seven mixes and, after curing, were exposed to 100 deg F heat at ambient humidity for 280 days. The following were observed from the testing: (1) Higher C3A content cement concrete produced larger shrinkage; (2) Use of fly ash increased shrinkage; (3) Use of retarder increased shrinkage; and (4) Lowering the cement content reduced the shrinkage.

Oils and Tars from Iowa Shales, HR-32, 1962

The inadequate supply of suitable road surfacing material in the southern part of Iowa raises the question of the possibility of utilizing certain shales abundant in this area. These carbonaceous shales commonly overlie the coal beds and may also be found as impurities in the coal seams. They constitute the "slate" which with minor amounts of coal makes up the "gob" piles at the mines. These shales frequently contain enough carbonaceous material to burn. Those which do not usually require only a relatively small amount of coal mixed with them to support combustion. As a result, the "gob" piles frequently burn. The residual shale material is frequently used locally as a road surfacing material. However, since there is no control over the burning, there is no assurance that the product is the most suitable which might be produced or that it is even uniform in its properties. To determine if a controlled burning would produce a suitable road building product economically a research project "Use of Shales as Highway Materials" (ISHC Project HR-21, IEES Project 299-S) was set up in the Iowa Engineering Experiment Station with funds provided by the Iowa State Highway Commission, This project was supervised by Charles Frush, formerly Assistant Professor of Mining Engineering at Iowa State University. The various shales were subjected to controlled burning, and the solid residues were tested for their suitability for highway use.

Concrete Pavement Mixture Design and Analysis (MDA): Factors Influencing Drying Shrinkage, TPF-5(205), 2014

This literature review focuses on factors influencing drying shrinkage of concrete. Although the factors are normally interrelated, they can be categorized into three groups: paste quantity, paste quality, and other factors.