Ranking of HMA Moisture Sensitivity Tests in Iowa, RB00-012, 2012

Several agencies specify AASHTO T283 as the primary test for field acceptance of moisture susceptibility in hot mix asphalt. When used in this application, logistical difficulties challenge its practicality, while repeatability is routinely scrutinized by contractors. An alternative test is needed which can effectively demonstrate the ability to screen mixtures based on expected performance. The ideal replacement can be validated with field performance, is repeatable, and allows for prompt reporting of results. Dynamic modulus, flow number, AASHTO T283, Hamburg wheel tracking device (HWTD), and the moisture induced sensitivity test (MIST) were performed on plant produced surface mixes in Iowa. Follow-up distress surveys were used to rank the mixes by their performance. The rankings indicate both the quantity of swelling from MIST conditioning and submersed flow number matched the performance ranking of all but one mixture. Hamburg testing parameters also appear effective, namely the stripping inflection point and the ratio between stripping slope and the creep slope. Dynamic modulus testing was ineffective, followed by AASHTO T283 and ratios produced from flow number results of conditioned samples.

Modification of Ca-Montmorillonite by Low-Temperature Heat Treatment, HR-106, 1964

Objectives of this investigation were to measure the effects of moderate heat treatments (below the dehydroxylation temperature) on physical and chemical properties of a calcium-montmorillonite clay. Previous workers have noted the reduction in cation exchange capacity and swelling property after heating in the range 200 to 400°C, and have suggested several possible explanations, such as hysteresis effect, increased inter-layer attractions due to removal of inter-layer water, or changes in the disposition of inter-layer or layer surface ions. The liquid limits of Ca-montmorillonite were steadily decreased with increased temperature of treatment, levelling at about 450°C. The plastic limit decreased slightly up to 350°C, above which samples could no longer be rolled into threads. The gradual change is in contrast with sudden major changes noted for weight loss (maximum rates of change at l00°C and 500°C), glycol retention surface area (520°C), and d001 diffraction peak intensity (17.7 A spacing) and breadth after glycolation (530°C). Other properties showing more gradual reductions with heat treatment were amount of exchangeable calcium (without water soaking), cation exchange capacity by NH4AC method, and d001 intensity (21 A spacing) after storing at 100% r.h. one month and re-wetting with water. Previous water soaking allowed much greater release of fixed Ca++ up to 450°C. Similar results were obtained with cation exchange capacities when samples were treated with N CaCl2 solution. The 21.0 A peak intensity curve showed close similarity to the liquid limit and plastic index curves in the low temperature range, and an explanation is suggested.