Evaluation of Additives for Extruded Asphalt Curbs, MLR-85-06, 1985

This study investigates the properties imparted to extruded asphalt curb mixes by five different additives. The AC used in these mixes was also tested with various amounts of the additives. All of the additives stiffened the AC as indicated by a reduction of penetration and increased viscosity. Only the powdered asphalts, gilsonite and Witcurb improved the Marshall stability and the indirect tensil strength enough to justify their use in curb mixes.

Self-Consolidating Concrete—Applications for Slip-Form Paving: Phase II, May 2011

The goal of the project was to develop a new type of self-consolidating concrete (SCC) for slip-form paving to simplify construction an make smoother pavements. Developing the new SCC involved two phases: a feasibility study (Phase I sponsored by TPF-5[098] and concrete admixtures industry) and an in-depth mix proportioning and performance study and field applications (Phase II). The phase I study demonstrated that the new type of SCC needs to possess not only excellent self-consolidating ability before a pavement slab is extruded, but also sufficient “green” strength (the strength of the concrete in a plastic state) after the extrusion. To meet these performance criteria, the new type of SCC mixtures should not be as fluid as conventional SCC but just flowable enough to be self-consolidating. That is, this new type of SCC should be semi-flowable self-consolidating concrete (SFSCC). In the phase II study, effects of different materials and admixtures on rheology, especially the thixotropy, and green strength of fresh SFSCC have been further investigated. The results indicate that SFSCC can be designed to (1) be workable enough for machine placement, (2) be self-consolidating without segregation, (3) hold its shape after extrusion from a paver, and (4) have performance properties (strength and durability) comparable with current pavement concrete. Due to the combined flowability (for self-consolidation) and shape-holding ability (for slip-forming) requirements, SFSCC demands higher cementitious content than conventional pavement concrete. Generally, high cementitious content is associated with high drying shrinkage potential of the concrete. However, well-proportioned and well-constructed SFSCC in a bike path constructed at Ames, IA, has not shown any shrinkage cracks after approximately 3 years of field service. On the other hand, another SFSCC pavement with different mix proportions and construction conditions showed random cracking. The results from the field SFSCC performance monitoring implied that not only the mix proportioning method but also the construction practice is important for producing durable SFSCC pavements. A carbon footprint, energy consumption, and cost analysis conducted in this study have suggested that SFSCC is economically comparable to conventional pavement concrete in fixed-form paving construction, with the benefit of faster, quieter, and easier construction.

RFID Tags for Detecting Concrete Degradation in Bridge Decks, RB08-011, 2013

Steel reinforcing bar (rebar) corrosion due to chlorine ingress is the primary degradation mechanism for bridge decks. In areas where rock salt is used as a de-icing agent, salt water seeps into the concrete through cracks, causing corrosion of the rebar and potentially leading to catastrophic failure if not repaired. This project explores the use of radio frequency identification (RFID) tags as low-cost corrosion sensors. RFID tags, when embedded in concrete, will fail due to corrosion in the same manner as rebar after prolonged exposure to salt water. In addition, the presence of salt water interferes with the ability to detect the tags, providing a secondary mechanism by which this method can work. During this project, a fieldable RFID equipment setup was constructed and tested. In addition to a number of laboratory experiments to validate the underlying principles, RFID tags were embedded and tested in several actual bridge decks. Two major challenges were addressed in this project: issues associated with tags not functioning due to being in close proximity to rebar and issues associated with portland concrete coming in direct contact with the tags causing a detuning effect and preventing the tags from operating properly. Both issues were investigated thoroughly. The first issue was determined to be a problem only if the tags are placed in close proximity to rebar. The second issue was resolved by encapsulating the tag. Two materials, polyurethane spray foam and extruded polystyrene, were identified as providing good performance after testing, both in the lab and in the field.