Mechanical and elemental characterization of solder joints and welds using a gold-palladium alloy

Purpose. This study was conducted to determine whether newer infrared or laser welding technologies created joints superior to traditional furnace or torch soldering methods of joining metals. It was designed to assess the mechanical resistance, the characteristics of the fractured surfaces, and the elemental diffusion of joints obtained by four different techniques: (1) preceramic soldering with a propane-oxygen torch, (2) postceramic soldering with a porcelain furnace, (3) preceramic and (4) postceramic soldering with an infrared heat source, and (5) laser welding. Material and methods. Mechanical resistance was determined by measuring the ultimate tensile strength of the joint and by determining their resistance to fatigue loading. Elemental diffusion to and from the joint was assessed with microprobe tracings. Scanning electron microscopy micrographs of the fractured surface were also obtained and evaluated. Results. Under monotonic tensile stress, three groups emerged: The laser welds were the strongest, the preceramic joints ranged second, and the postceramic joints were the weakest. Under fatigue stress, the order was as follows: first, the preceramic joints, and second, a group that comprised both postceramic joints and the laser welds. Inspection of the fractographs revealed several fracture modes but no consistent pattern emerged. Microprobe analyses demonstrated minor diffusion processes in the preceramic joints, whereas significant diffusion was observed in the postceramic joints. Clinical Implications. The mechanical resistance data conflicted as to the strength that could be expected of laser welded joints. On the basis of fatigue resistance of the joints, neither infrared solder joints nor laser welds were stronger than torch or furnace soldered joints.

In vivo electrochemical corrosion study of a CoCrMo biomedical alloy in human synovial fluids.

The present study was initiated with the aim to assess the in vivo electrochemical corrosion behaviour of CoCrMo biomedical alloys in human synovial fluids in an attempt to identify possible patient or pathology specific effects. For this, electrochemical measurements (open circuit potential OCP, polarization resistance Rp, potentiodynamic polarization curves, electrochemical impedance spectroscopy EIS) were carried out on fluids extracted from patients with different articular pathologies and prosthesis revisions. Those electrochemical measurements could be carried out with outstanding precision and signal stability. The results show that the corrosion behaviour of CoCrMo alloy in synovial fluids not only depends on material reactivity but also on the specific reactions of synovial fluid components, most likely involving reactive oxygen species. In some patients the latter were found to determine the whole cathodic and anodic electrochemical response. Depending on patients, corrosion rates varied significantly between 50 and 750mgdm(-2)year(-1).