Spectroscopic ellipsometry study of the In1-x Gax Asy P1-y / InP Heterojunctions grown by metalorganic chemical-vapor deposition

The dielectric functions of InP, In0.53Ga0.47As, and In0.75Ga0.25As0.5P0.5 epitaxial layers have been measured using a polarization modulation spectroscopic ellipsometer in the 1.5 to 5.3 eV region. The oxide removal procedure has been carefully checked by comparing spectroscopic ellipsometry and x ray photoelectron spectroscopy measurements. These reference data have been used to investigate the structural nature of metalorganic chemical vapor deposition grown In0.53Ga0.47As/InP and In0.75Ga0.25As0.5P0.5/InP heterojunctions, currently used for photodiodes and laser diodes. The sharpness of the interfaces has been systematically compared for the two types of heterojunctions: In1 xGaxAsy/InP and InP/In1 xGaxAsyP1 y. The sharpest interface is obtained for InP growth on In0.75Ga0.25As0.5P0.5 where the interface region is estimated to be (10±10) Å thick. The importance of performing in situ SE measurements is emphasized.

Optimization of KOH etching process to obtain textured substrates suitable for heterojunction solar cells fabricated by HWCVD

In this work, we have studied the texturization process of (100) c-Si wafers using a low concentration potassium hydroxide solution in order to obtain good quality textured wafers. The optimization of the etching conditions have led to random but uniform pyramidal structures with good optical properties. Then, symmetric heterojunctions were deposited by Hot-Wire CVD onto these substrates and the Quasi-Steady-State PhotoConductance technique was used to measure passivation quality. Little degradation in the effective lifetime and implicit open circuit voltage of these devices (< 20 mV) was observed in all cases. It is especially remarkable that for big uniform pyramids, the open-circuit voltage is comparable to the values obtained on flat substrates.