Microstructure and magnetic properties of Ni50 Mn37 Sn13 Heusler alloy ribbons

The Heusler alloy Ni50 Mn37 Sn13 was successfully produced as ribbon flakes of thickness around 7-10 μm melt spinning. Fracture cross section micrographs in the ribbon show the formation of a microcrystalline columnarlike microstructure, with their longer axes perpendicular to the ribbon plane. Phase transition temperatures of the martensite-austenite transformation were found to be MS =218 K, Mf =207 K, AS =224 K, and Af =232 K; the thermal hysteresis of the transformation is 15 K. Ferromagnetic L 21 bcc austenite phase shows a Curie point of 313 K, with cell parameter a=0.5971 (5) nm at 298 K, transforming into a modulated 7M orthorhombic martensite with a=0.6121 (7) nm, b=0.6058 (8) nm, and c=0.5660 (2) nm, at 150 K

Magnetic properties and martensitic transition in annealed Ni50Mn30Al20

We have studied the effect of heat treatment on the magnetic properties and on the martensitic transition of the Ni50Mn30Al20 alloy. A mixed L21+B2 state is obtained in the as-prepared sample, while no L21 order is retained in the sample quenched from high temperature. For the two heat treatments, the samples order antiferromagnetically, but there is evidence of coexisting ferromagnetic interactions. A martensitic transition occurs below the magnetic one for quenched samples. However, the martensitic transition is inhibited in the as-prepared sample.

Growth and magnetic properties of multiferroic LaxBi1-xMnO3 thin films

A comparative study of LaxBi1-xMnO3 thin films grown on SrTiO3 substrates is reported. It is shown that these films grow epitaxially in a narrow pressure-temperature range. A detailed structural and compositional characterization of the films is performed within the growth window. The structure and the magnetization of this system are investigated. We find a clear correlation between the magnetization and the unit-cell volume that we ascribe to Bi deficiency and the resultant introduction of a mixed valence on the Mn ions. On these grounds, we show that the reduced magnetization of LaxBi1-xMnO3 thin films compared to the bulk can be explained quantitatively by a simple model, taking into account the deviation from nominal composition and the Goodenough-Kanamori-Anderson rules of magnetic interactions.

Structure and magnetic properties of Sm/Fe multilayers versus substrate temperature

Three Sm(2 Å)/Fe(3 Å) multilayers have been made using two electron beams in a high vacuum chamber onto very thin Kapton foils at different substrate temperatures, (Ts=40°C, 150°C and 230°C), with the same total thickness of 3000 Å. We have found that the substrate temperature strongly affects structure and magnetic properties of the samples. For a substrate temperature of 150°C the sample behaves as a three dimensional random magnet.

Magnetic properties of Fe-Cu-Nb-Si-B nanocrystaliine magnetic alloys

Several ribbons of composition Fe73.5Cu1Nb 3Si16.5B6 and Fe73.5Cu1 Nb3Si13.5B9 were prepared by annealing the as-quenched samples between 525°C and 700°C; which induced nucleation of nanocrystallites of Fe bcc-type composition. Mean grain sizes were obtained from X-ray diffraction. Static magnetic properties were measured with both a Magnet Physik Hysteresis-Graph (up to 200 Oe) and a SHE SQUID magnetometer (up to 50 kOe). Soft magnetic parameters (coercive field and initial permeability) were very sensitive to grain size. The ZFC magnetization at low field showed a broad peak at a temperature TM, thus signalling a certain distribution of nanocrystalline sizes, and TM strongly decreased when the mean grain size decreased. Isothermal magnetization curves at low temperature showed the expected asymptotic behavior of a random magnet material at low and high fields.

Magnetic properties and giant magnetoresistance in melt-spun CoCu alloys

Magnetic, structural, and transport properties of as quenched and annealed Co10Cu90 samples have been investigated using x¿ray diffraction and a SQUID magnetometer. The largest value of MR change was observed for the as¿quenched sample annealed at 450°C for 30 min. The magnetic and transport properties closely correlate with the microstructure, mainly with Co magnetic particle size and its distribution. For thermal annealing the as quenched samples below 600°C, the Co particle diameters increase from 4.0 to 6.0 nm with a magnetoresistance (MR) drop from 33.0% to 5.0% at 10 K. Comparison with the theory indicates that the interfacial electron spin¿dependent scattering mechanism correlates with GMR for Co particle diameters up to about 6.0 nm.

Magnetic properties of amorphous Fe-Si compositionally modulated thin films

The present paper reports on a magnetometric study of Fe‐Si compositionally modulated thin films. The low‐temperature dependence of the magnetization exhibit Bloch's T3/2 dependence with a minor T5/2 correction term. The spin‐wave stiffness constant deduced from the temperature coefficient depends on the characteristic modulation length and its values are much lower that in glassy alloys.

Magnetic properties and domain-wall motion in single-crystal BaFe10.2Sn0.74Co0.66O19

The magnetic properties of BaFe12O19 and BaFe10.2Sn0.74Co0.66O19 single crystals have been investigated in the temperature range (1.8 to 320 K) with a varying field from -5 to +5 T applied parallel and perpendicular to the c axis. Low-temperature magnetic relaxation, which is ascribed to the domain-wall motion, was performed between 1.8 and 15 K. The relaxation of magnetization exhibits a linear dependence on logarithmic time. The magnetic viscosity extracted from the relaxation data, decreases linearly as temperature goes down, which may correspond to the thermal depinning of domain walls. Below 2.5 K, the viscosity begins to deviate from the linear dependence on temperature, tending to be temperature independent. The near temperature independence of viscosity suggests the existence of quantum tunneling of antiferromagnetic domain wall in this temperature range.

Morphological and Magnetic Properties of Superparamagnetic Carbon-Coated Fe Nanoparticles Produced by Arc Discharge.

Spherical carbon coated iron particles of nanometric diameter in the 510 nm range have been produced by arc discharge at near-atmospheric pressure conditions (using 58·10 4 Pa of He). The particles exhibit a crystalline dense iron core with an average diameter 7.4 ± 2.0 nm surrounded by a sealed carbon shell, shown by transmission electron microscopy (TEM), selected-area diffrac- tion (SAED), energy-dispersive X-ray analysis (STEM-EDX) and electron energy loss spectroscopy (EELS). The SAED, EDX and EELS results indicate a lack of traces of core oxidized phases showing an efficient protection role of the carbon shell. The magnetic properties of the nanoparticles have been investigated in the 5300 K temperature range using a superconducting quantum interference device (SQUID). The results reveal a superparamagnetic behaviour with an average monodomain diameter of 7.6 nm of the nanoparticles. The zero field cooled and field cooled (ZFC-FC)magnetization curves show a blocking temperature (TB)at room temperature very suitable for biomedical applications (drug delivery, magnetic resonance imaging MRI, hyperthermia).