Failure mechanism under tensile loads in CFRP 0-90º cross-ply laminates containing voids

The failure mechanism of a voided CFRP 0-90° cross-ply laminate under tensile loads applied in one direction was studied in this Final Degree Project. For this purpose, voided coupons were manufactured for being tested and a FEA was done. In both investigations, voids were placed in 90º and 0º direction, in order to understand the void location influence. On the one hand, the behaviour of the voided laminates was investigated through a FEM in order to preview the stress distribution within the material. On the other hand, voided specimens where manufactured by applying blowing agent in between the inner layers. These specimens were tested by a quasi-static step wise tensile test where data showing its real behaviour was collected. Specimens were X-rayed after each step of the test in order to investigate the failure mechanism of the composite. Data from the test was studied so that relations such as strength of the laminates, crack density per stress, void length per first crack at the void and void area per first crack at the specimen could be characterized

Estudio del contenido polinico de la atmosfera de Barcelona segun un nuevo metodo de filtracion

Descripción de una nueva técnica de captación de polen atmosférico y su aplicación en el estudio del contenido polínico de la atmósfera de Barcelona durante el año 1981. Esta nueva técnica de captación se basa en la filtración, a través de filtros especiales de éster de celulosa, tipo Millipore, de volúmenes de aire perfectamente medidos por contadores de gas. El mecanismo de filtración es un McLEOD adaptado convenientemente. El muestreo se ha realizado en tres puntos y los resultados de los análisis polínicos de la ciudad de Barcelona son expresados mediante gráficas que indican las fluctuaciones cualitativas y cuantitativas, semanales y mensuales. Aquellas formas polínicas que se consideran de especial interés, son presentadas en gráficas aparte y discutidas individualmente.

La tendencia mineralógica de las eolianitas del Pleistoceno de Mallorca, mediante la aplicación del metodo de Chung

El objetivo de este trabajo es conocer la evolución diagenética de los minerales carbonatados de las eolianitas del Pleistoceno de Mallorca. Se ha puesto de relieve un control de la composición original y un control climático en la tendencia mineralógica de las eolianitas. Para la determinación cuantitativa se ha utilizado el método de Chung.

Creatividad publicitaria :análisis de los modelos que evalluan la creatividad en los productos publicitarios

Realizar una recopilacion organizada de los conocimientos pertenecientes al tema de valoracion de la creatividad en los productos publicitarios, con la finalidad de hacer un analisis de los metodos utilizados por los investigadores. Esto permite tambien, la construccion de un marco teorico, que servira como fundamento para el desarrollo de un metodo propio en la segunda parte de este estudio, ademas de identificar las futuras lineas de investigacion aplicables al estudio de la creatividad.

Engineering the thermal emission of macroporous silicon

Todos los cuerpos emiten luz espontaneamente al ser calentados. El espectro de radiacion es una funcion de la temperatura y el material. Sin embargo, la mayoria de los materiales irradia, en general, en una banda espectral amplia. Algunas matereiales, por el contrario, son capaces de concentrar la radiacion termica en una banda espectral mucho mas estrecha. Estos materiales se conocen como emisores selectivos y su uso tiene un profundo impacto en la eficiencia de sistemas sistemas tales como iluminacion y conversion de energia termofotovoltaica. De los emisores selectivos se espera que sean capaces de operar a altas temperaturas y que emitan en una banda espectral muy concisa. Uno de los metodos mas prometedores para controlar y disenar el espectro de emision termico es la utilizacion de cristales fotonicos. Los cristales fotonicos son estructuras periodicas artificiales capaces de controlar y confinar la luz de formas sin precedentes. Sin embargo, la produccion de dichas estructuras con grandes superficies y capaces de soportar altas temperaturas sigue siendo una dificil tarea. Este trabajo esta dedicada al estudio de las propiedades de emision termica de estructuras 3D de silicio macroporoso en el rango espectral mid-IR (2-30 m). En particular, este trabajo se enfoca en reducir la elevada emisividad del silicio cristalino. Las muestras estudiadas en este trabajo tienen una periodicidad de 4 m, lo que limitan los resultados obtenidos a la banda del infrarrojo medio, aunque estructuras mucho mas pequenas son tecnologicamente realizables con el metodo de fabricacion utilizado. Hemos demostrado que el silicio macroporoso 3D puede inhibir completamente la emision termica en su superficie. Mas aun, esta banda se puede ajustar en un amplio margen mediante pequenos cambios durante la formacion de los macroporos. Tambien hemos demostrado que tanto el ancho como la frecuencia de la banda de inhibicion se puede doblar mediante la aplicacion de tecnicas de postprocesado adecuadas. Finalmente hemos mostrado que es posible crear bandas de baja emisividad arbitrariamente anchas mediante estructuras macroporosas aperiodicas.

Los modelos causales asociados a estructuras de covarianza: una via para la unificación de los dos métodos de la Psicologia cientifica

A través de este articulo he pretendido exponer una introducción a los Modelos Causales desde las perspectivas histórica, metodológica y estadístico-matemtitica. Asimismo, he planteado las posibilidades que tienen estos modelos, asociados a estructuras de covariancia, como via que puede contribuir a superar la dicotomia metodo experimental/mktodo correlacional. Para la exposición de 10s procesos de especificación, identificación, estimación, prueba de ajuste e interpretación de parámetros de un modelo causal he tomado como referencia el modelo LISREL. Sin embargo, en la sistematización de estos procesos no he intentado presentar solamente la simple descripción del modelo, insistiendo, para ello, en la necesidad de integrar este modelo en el contexto del método cientifico.

Functional diversity of macrophyte communities within and between Pyrenean lakes

Submersed vegetation is a common feature in about 70% Pyrene an high mountain (>1500 m a.s.l.) lakes. Isoetids and soft-water elodeids are common elements of this underw ater flora and can form distinct vegetation units (i.e. patches of vegetation dominated by different species) within complex mosaics of vegetation in shallow waters (<7 m). Since is oetids exert a strong influence on sediment biogeochemistry due to high radial oxygen loss, we examined the small scale characteristics of the lake environment (water and sediment) associated to vegetation patches in order to ascertain potential functional differences among them. To do so, we characterised the species composition and biomass of the main vegetation units from 11 lakes, defined plant communities based on biomass data, and then related each community with sediment properties (redox and dissolved nutrient concentration in the pore water) and water nutrient concentration within plant canopy. We also characterised lake water and sediment in areas without vegetation as a reference. A total of twenty-one vegetation units were identified, ranging from one to five per lake. A cluster analysis on biomass species composition suggested seven different macrophyte communities that were named after the most dominant species:Nitella sp.,Potamogeton praelongus, Myriophyllum alterniflorum, Sparganium angustifolium , Isoetes echinospora,Isoetes lacustris and Carex rostrata . Coupling between macrophyte communities and their immediate environment (overlying water and sediment) was manifested mainly as variation in sediment redox conditions and the dominant form of inorganic nitrogen in pore-water. These effects depended on the specific compositi on of the community, and on the allocation between above- and belowground biomass, and could be predicted with a model relating the average and standard deviation of sediment redox potential from 0 down to -20 cm, across macrophyte communities. Differences in pore-water total dissolved phosphorus were related to the trophic state of the lakes. There was no correlation between sediment and water column dissolved nutrients. However, nitrate concentrations tended to be lower in the water overlaying isoetid communities, in apparent contradiction to the patterns of dissolved nitrates in the pore-water. These tendencies were robust even when comparing the water over laying communities within the same lake, thus pointing towards a potential effect of isoetids in reducing dissolved nitrogen in the lakes.

Estudio de la adherencia entre armaduras de materiales compuestos de matriz polimérica (FRP) y hormigón

En este artículo se presentan los resultados del estudio del comportamiento adherente de barras de materiales compuestos de matriz polímero (FRP), con fibras de vidrio (GFRP) y con fibras de carbono (CFRP), como armadura de hormigón. Se realizan un total de 91 ensayos según las normas ACI 440.3R-04 y CSA S806-02. Los parámetros considerados en los ensayos son la resistencia del hormigón,e l acabado superficial,e l tipo de fibra y el diámetro de la barra. Los resultados dan una estimación de la capacidad de adherencia para diferentes tipos de hormigón y armaduras. La diferencia en las propiedades y en el comportamiento adherente se traduce en una respuesta adherencia-deslizamiento distinta