Disorder-induced critical phenomena in magnetically glassy Cu-Al-Mn alloys

Measurements of magnetic hysteresis loops in Cu-Al-Mn alloys of different Mn content at low temperatures are presented. The loops are smooth and continuous above a certain temperature, but exhibit a magnetization discontinuity below that temperature. Scaling analysis suggest that this system displays a disorder-induced phase transition line. Measurements allow one to determine the critical exponents ß=0.03±0.01 and ß¿=0.4±0.1, which coincide with those reported recently in a different system, thus supporting the existence of universality for disorder-induced critical points.

Kerr measurements on single-domain SrRuO3 thin films

We report on the magneto-optical measurements of an epitaxial SrRuO3 film grown on SrTiO3 (0 0 1), which previously was determined to be single domain orientated by x-ray diffraction and Raman spectroscopy techniques. Our experiments reveal a large Kerr rotation, which reaches a maximum value of about 0.5° at low temperature. By measuring magnetic hysteresis loops at different temperatures, we determined the temperature dependence of the Kerr rotation in the polar configuration. Values of the anisotropic magnetoresistance ~ 20% have been measured. These values are remarkably higher than those of other metallic oxides such as manganites. This striking difference can be attributed to the strong spin-orbit interaction of the Ru 4d ion in the SrRuO3 compound.

Exchange bias between magnetoelectric YMnO3 and ferromagnetic SrRuO3 epitaxial films

Orthorhombic YMnO3 (YMO) epitaxial thin films were deposited on SrTiO3 (STO) single-crystal substrates. We show that the out-of-plane texture of the YMO films can be tailored using STO substrates having (001), (110), or (111) orientations. We report on the magnetic properties of the YMO(010) films grown on STO(001) substrates. The dependence of the susceptibility on the temperature indicates that the films are antiferromagnetic below the Néel temperature (around 35 K). Orthorhombic YMO(010) films were also deposited on an epitaxial buffer layer of ferromagnetic and metallic SrRuO3 (SRO). The magnetic hysteresis loops of SRO show exchange bias at temperatures below the Néel temperature of YMO. These results confirm that the YMO films are antiferromagnetic and demonstrate that magnetoelectric YMO can be integrated in functional epitaxial architectures.

Hysteresis in a system driven by either generalized force or displacement variables: martensitic phase transition in single-crystalline Cu-Zn-Al

We report on experiments aimed at comparing the hysteretic response of a Cu-Zn-Al single crystal undergoing a martensitic transition under strain-driven and stress-driven conditions. Strain-driven experiments were performed using a conventional tensile machine while a special device was designed to perform stress-driven experiments. Significant differences in the hysteresis loops were found. The strain-driven curves show reentrant behavior yield point which is not observed in the stress-driven case. The dissipated energy in the stress-driven curves is larger than in the strain-driven ones. Results from recently proposed models qualitatively agree with experiments.

Hysteresis and return-point memory in deterministic cellular automata

We have investigated hysteresis and the return-point memory (RPM) property in deterministic cellular automata with avalanche dynamics. The RPM property reflects a partial ordering of metastable states, preserved by the dynamics. Recently, Sethna et al. [Phys. Rev. Lett. 70, 3347 (1993)] proved this behavior for a homogeneously driven system with static disorder. This Letter shows that the partial ordering and the RPM can be displayed as well by systems driven heterogeneously, as a result of its own evolution dynamics. In particular, we prove the RPM property for a deterministic 2D sandpile automaton driven at a central site.

Dielectric anomaly and magnetic response of epitaxial orthorhombic YMnO3 thin films

The structure, magnetic response, and dielectric response of the grown epitaxial thin films of the orthorhombic phase of YMnO3 oxide on Nb:SrTiO3 (001) substrates have been measured. We have found that a substrate-induced strain produces an in-plane compression of the YMnO3 unit cell. The magnetization versus temperature curves display a significant zero-field cooling (ZFC)-field cooling hysteresis below the Nel temperature (TN 45 K). The dielectric constant increases gradually (up to 26%) below the TN and mimics the ZFC magnetization curve. We argue that these effects could be a manifestation of magnetoelectric coupling in YMnO3 thin films and that the magnetic structure of YMnO3 can be controlled by substrate selection and/or growth conditions.

SrRuO3/SrTiO3/SrRuO3 heterostructures for magnetic tunnel junctions

We report on the growth and characterization of SrRuO3 single layers and SrRuO3/SrTiO3/SrRuO3 heterostructures grown on SrTiO3(100) substrates. The thickness dependence of the coercivity was determined for these single layers. Heterostructures with barrier thickness tb=1, 2.5, and 4 nm were fabricated, with electrodes having thickness ranging from 10 to 100 nm. The hysteresis loops of heterostructures with tb=2.5¿nm, 4 nm reveal uncoupled magnetic switching of the electrodes. Therefore, these heterostructures can be used for the fabrication of magnetic tunneling junctions.

Influence of the dipolar interactions in the magnetization reversal asymmetry of hard-soft magnetic ribbons

Partial crystallization of the metallic glass Co66Si16B12Fe4Mo2 was performed by annealing at temperatures between 500 and 540°C for 10-20 min, resulting in crystallite volume fractions of (0.7-5)×10¿3 and sizes of 50-100 nm. This two-phase alloy presents a remarkable feature: a hysteresis loop shift that can be tailored by simply premagnetizing the sample in the adequate magnetic field. Shifts as large as five times the coercive field have been obtained which make them interesting for application as magnetic cores in dc pulse transformers. The asymetrical magnetic reversal is explained in terms of the magnetic dipolar field interaction and the observed hysteresis loops have been satisfactorily simulated by a modification of Stoner-Wohlfarth¿s model of coherent rotations.

Erasing the glassy state in magnetic fine particles

BaFe10.4Co0.8Ti0.8O19 magnetic fine particles exhibit most of the features attributed to glassy behavior, e.g., irreversibility in the hysteresis loops and in the zero-field-cooling and field-cooling curves extends up to very high fields, and aging and magnetic training phenomena occur. However, the multivalley energy structure of the glassy state can be strongly modified by a field-cooling process at a moderate field. Slow relaxation experiments demonstrate that the intrinsic energy barriers of the individual particles dominate the behavior of the system at high cooling fields, while the energy states corresponding to collective glassy behavior play the dominant role at low cooling fields.

Topological magnetic irreversibility in superconducting Pb samples of various shapes

The magnetic-field dependence of the magnetization of cylinders, disks, and spheres of pure type-I superconducting lead was investigated by means of isothermal measurements of first magnetization curves and hysteresis cycles. Depending on the geometry of the sample and the direction and intensity of the applied magnetic field, the intermediate state exhibits different irreversible features that become particularly highlighted in minor hysteresis cycles. The irreversibility is noticeably observed in cylinders and disks only when the magnetic field is parallel to the axis of revolution and is very subtle in spheres. When the magnetic field decreases from the normal state, the irreversibility appears at a temperature-dependent value whose distance to the thermodynamic critical field depends on the sample geometry. The irreversible features in the disks are altered when they are submitted to an annealing process. These results agree well with very recent high-resolution magneto-optical experiments in similar materials that were interpreted in terms of transitions between different topological structures for the flux configuration in the intermediate state. A discussion of the relative role of geometrical barriers for flux entry and exit and pinning effects as responsible for the magnetic irreversibility is given.

Magnetic properties of Fe-Cu-Nb-Si-B nanocrystaliine magnetic alloys

Several ribbons of composition Fe73.5Cu1Nb 3Si16.5B6 and Fe73.5Cu1 Nb3Si13.5B9 were prepared by annealing the as-quenched samples between 525°C and 700°C; which induced nucleation of nanocrystallites of Fe bcc-type composition. Mean grain sizes were obtained from X-ray diffraction. Static magnetic properties were measured with both a Magnet Physik Hysteresis-Graph (up to 200 Oe) and a SHE SQUID magnetometer (up to 50 kOe). Soft magnetic parameters (coercive field and initial permeability) were very sensitive to grain size. The ZFC magnetization at low field showed a broad peak at a temperature TM, thus signalling a certain distribution of nanocrystalline sizes, and TM strongly decreased when the mean grain size decreased. Isothermal magnetization curves at low temperature showed the expected asymptotic behavior of a random magnet material at low and high fields.

Steps in the hysteresis of a high spin molecule

We report the first observation of steps in the hysteresis loop of a high¿spin molecular magnet. We propose that the steps, which occur every 0.46 T, are due to thermally assisted resonant tunneling between different quantum spin states. Magnetic relaxation increases dramatically when the field is in the neighborhood of a step. A simple model accounts for the observations and predicts a value for the anisotropy barrier consistent with that inferred from the superparamagnetic blocking temperature

Effect of a transverse magnetic field on resonant magnetization tunneling in high-spin molecules

The recent observation of steps at regular intervals of magnetic field in the hysteresis loops of oriented crystals of the spin-10 molecular magnet Mn12O12(CH3COO)16(H2O)4 has been attributed to resonant tunneling between spin states. Here, we investigate the effect on the relaxation rate of applying the magnetic field at an angle with respect to the easy axis of magnetization. We find that the position of the resonances is independent of the transverse component of the field, and is determined solely by the longitudinal component. On the other hand, a transverse field significantly increases the relaxation rate, both on and off resonance. We discuss classical and quantum mechanical interpretations of this effect