Magnetic hardening mechanisms in Nd-Fe-B nanocrystalline material

Microstructural and magnetic measurements of the evolution by heat treatment of initially amorphous Nd16Fe76B8 alloys prepared by melt spinning are presented. Evidence of magnetic hardening above a threshold temperature induced by magnetic isolation of the Nd2Fe14B grains is provided. A thermodynamic and kinetic explanation of local melting of the intergranular nanostructured Nd¿rich eutectic phase at temperatures below 900 K based on capillary effects is presented. A subsequent Ostwald ripening process moves Nd to wet intimately the hard magnetic grains, becoming, on cooling, a real paramagnetic isolating thin film (~2.5 nm). By using a simple analogy, it is shown that the switching magnetization field in a single¿domain crystal can be drastically affected through the exchange coupling to neighboring grains with different orientation of the easy axis. This effect should be important enough to reinforce the coercive field of polycrystalline hard magnetic materials and explains the observed enhancement from 0.9 to 1.9 T.

Magnetic properties of Fe-Cu-Nb-Si-B nanocrystaliine magnetic alloys

Several ribbons of composition Fe73.5Cu1Nb 3Si16.5B6 and Fe73.5Cu1 Nb3Si13.5B9 were prepared by annealing the as-quenched samples between 525°C and 700°C; which induced nucleation of nanocrystallites of Fe bcc-type composition. Mean grain sizes were obtained from X-ray diffraction. Static magnetic properties were measured with both a Magnet Physik Hysteresis-Graph (up to 200 Oe) and a SHE SQUID magnetometer (up to 50 kOe). Soft magnetic parameters (coercive field and initial permeability) were very sensitive to grain size. The ZFC magnetization at low field showed a broad peak at a temperature TM, thus signalling a certain distribution of nanocrystalline sizes, and TM strongly decreased when the mean grain size decreased. Isothermal magnetization curves at low temperature showed the expected asymptotic behavior of a random magnet material at low and high fields.

Growth and magnetic characterization of Co nanoparticles obtained by femtosecond pulsed laser deposition.

We present a detailed study on the morphology and magnetic properties of Co nanostructures deposited onto oxidized Si substrates by femtosecond pulsed laser deposition. Generally, Co disks of nanometric dimensions are obtained just above the ablation threshold, with a size distribution characterized by an increasingly larger number of disks as their size diminishes, and with a maximum disk size that depends on the laser power density. In Au/Co/Au structures, in-plane magnetic anisotropy is observed in all cases, with no indication of superparamagnetism regardless of the amount of material or the laser power density. Magnetic force microscopy observations show coexistence of single-domain and vortex states for the magnetic domain structure of the disks. Superconducting quantum interference device magnetometry and x-ray magnetic circular dichroism measurements point to saturation magnetization values lower than the bulk, probably due to partial oxidation of the Co resulting from incomplete coverage by the Au capping layer.