The suitability of steam exploded vitis vinifera and alkaline lignin for the manufacture of fiberboard

The main objective of this study was to explore the suitability of Vitis vinifera as a raw material and alkaline lignin as a natural binder for fiberboard manufacturing. In the first step, Vitis vinifera was steam- exploded through a thermo-mechanical vapor process in a batch reactor, and the obtained pulp was dried, ground, and pressed to produce the boards. The effects of pretreatment factors and pressing conditions on the chemical composition of the fibers and the physico-mechanical properties of binderless fiberboards were evaluated, and the conditions that optimize these properties were found. A response surface method based on a central composite design and multiple-response optimization was used. The variables studied and their respective variation ranges were: pretreatment temperature (Tr: 190-210ºC), pretreatment time (tr: 5-10 min), pressing temperature (Tp: 190-210ºC), pressing pressure (Pp: 8-16MPa), and pressing time (tp: 3-7min). The results of the optimization step show that binderless fiberboards have good water resistance and weaker mechanical properties. In the second step, fiberboards based on alkaline lignin and Vitis vinifera pulp produced at the optimal conditions determined for binderless fiberboards were prepared and their physico-mechanical properties were tested. Our results show that the addition of about 15% alkaline lignin leads to the production of fiberboards that fully meet the requirements of the relevant standard specifications

The effect of lignin as a natural adhesive on the physico-mechanical properties of Vitis vinifera fiberboards

Lignin was used as a natural adhesive to manufacture Vitis vinifera fiberboards. The fiberboards were produced at laboratory scale by adding powdered lignin to material that had previously been steam-exploded under optimized pretreatment and pressing conditions. The kraft lignin used was washed several times with an acidic solution to eliminate any contaminants and low molecular weight compounds. This research studied the effects of amounts of lignin ranging from 5% to 20% on the properties of Vitis vinifera fiberboards. The fiberboard properties evaluated were density, water resistance in terms of thickness swelling, water absorption, and the mechanical properties in terms of modulus of rupture, modulus of elasticity, and internal bond. Results showed that fiberboards made from Vitis vinifera without lignin addition had weaker mechanical properties. However, the fiberboards obtained using acid-washed kraft lignin as a natural adhesive had good mechanical and water resistance properties that fully satisfied the relevant standard specifications