MASS CONSERVATION ENHANCEMENT OF FREE BOUNDARY FLOWS IN COMPOSITES MANUFACTURING

Undesirable void formation during the injection phase of the liquid composite molding process can be understood as a consequence of the non-uniformity of the flow front progression, caused by the dual porosity of the fiber perform. Therefore the best examination of the void formation physics can be provided by a mesolevel analysis, where the characteristic dimension is given by the fiber tow diameter. In mesolevel analysis, liquid impregnation along two different scales; inside fiber tows and within the spaces between them; must be considered and the coupling between these flow regimes must be addressed. In such case, it is extremely important to account correctly for the surface tension effects, which can be modeled as capillary pressure applied at the flow front. When continues Galerkin method is used, exploiting elements with velocity components and pressure as nodal variables, strong numerical implementation of such boundary conditions leads to ill-posing of the problem, in terms of the weak classical as well as stabilized formulation. As a consequence, there is an error in mass conservation accumulated especially along the free flow front. This article presents a numerical procedure, which was formulated and implemented in the existing Free Boundary Program in order to significantly reduce this error.

Mass Conservation Enhancement of Free Boundary Mesolevel Flows during LCM Processes of Composites Manufacturing

Undesirable void formation during the injection phase of the liquid composite moulding process can be understood as a consequence of the non-uniformity of the flow front progression, caused by the dual porosity of the fibre perform. Therefore the best examination of the void formation physics can be provided by a mesolevel analysis, where the characteristic dimension is given by the fibre tow diameter. In mesolevel analysis, liquid impregnation along two different scales; inside fibre tows and within the open spaces between them; must be considered and the coupling between these flow regimes must be addressed. In such case, it is extremely important to account correctly for the surface tension effects, which can be modelled as capillary pressure applied at the flow front. Numerical implementation of such boundary conditions leads to ill-posing of the problem, in terms of the weak classical as well as stabilized formulation. As a consequence, there is an error in mass conservation accumulated especially along the free flow front. This contribution presents a numerical procedure, which was formulated and implemented in the existing Free Boundary Program in order to significantly reduce this error.

Production of aluminium based composites reinforced with embedded NiTi by friction stir welding

Dissertação para a obtenção do grau de Mestre em Engenharia Mecânica

Electrochemical supercapacitors of conductive polymers and their composites

Dissertação Para Obtenção Do Grau De Mestre Em Bioorgânica

Cellulose-based composites as functional conductive materials for printed electronics

In this work, cellulose-based electro and ionic conductive composites were developed for application in cellulose based printed electronics. Electroconductive inks were successfully formulated for screen-printing using carbon fibers (CFs) and multi-walled carbon nanotubes (MWCNTs) as conductive functional material and cellulose derivatives working as binder. The formulated inks were used to fabricate conductive flexible and disposable electrodes on paper-based substrates. Interesting results were obtained after 10 printing passes and drying at RT of the ink with 10 % wt. of pristine CFs and 3% wt. of carboxymethyl cellulose (CMC), exhibiting a resistivity of 1.03 Ωcm and a resolution of 400 μm. Also, a resistivity of 0.57 Ωcm was obtained for only one printing pass using an ink based on 0.5 % wt. MWCNTs and 3 % wt. CMC. It was also demonstrated that ionic conductive cellulose matrix hydrogel can be used in electrolyte-gated transistors (EGTs). The electrolytes revealed a double layer capacitance of 12.10 μFcm-2 and ionic conductivity of 3.56x10-7 Scm-1. EGTs with a planar configuration, using sputtered GIZO as semiconducting layer, reached an ON/OFF ratio of 3.47x105, a VON of 0.2 V and a charge carrier mobility of 2.32 cm2V-1s-1.

Preliminary study on the production of functionally graded materials by friction stir processing

Dissertação apresentada na Faculdade de Ciências e Tecnologia da Universidade Nova de Lisboa para obtenção do grau de Mestre em Engenharia Mecânica

Liquid crystal mobility and PDLC memory effects

Dissertation presented at Faculdade de Ciências e Tecnologia of Universidade Nova de Lisboa to obtain the Degree of Master in Chemical and Biochemical Engineering

Development and implementation of strategies for the incorporation of reinforcing elements in aluminium alloys by solid state processing

Dissertação para obtenção do Grau de Mestre em Engenharia Mecânica

Selective synthesis under microwave irradiation of new monomers for potential applications in PDLC films

Dissertation to obtain the degree of master in Bioorganic

Effect of surfactant on PDLC films with and without permanent memory effect

Dissertação para obtenção do Grau de Mestre em Engenharia Química e Bioquímica

Physical and chemical assessment of lime–metakaolin mortars: Influence of binder:aggregate ratio

Cement & Concrete Composites 45 (2014) 264–271

Cellulose nanorods in liquid crystalline elastomers for improved actuators

Nanotechnology plays a central role in ‘tailoring’ materials’ properties and thus improving its performances for a wide range of applications. Coupling nature nano-objects with nanotechnology results in materials with enhanced functionalities. The main objective of this master thesis was the synthesis of nanocrystalline cellulose (NCCs) and its further incorporation in a cellulosic matrix, in order to produce a stimuli-responsive material to moisture. The induced behaviour (bending/unbending) of the samples was deeply investigated, in order to determine relationships between structure/properties. Using microcrystalline cellulose as a starting material, acid hydrolysis was performed and the NCC was obtained. Anisotropic aqueous solutions of HPC and NCC were prepared and films with thicknesses ranging from 22μm to 61μm were achieved, by using a shear casting technique. Microscopic and spectroscopic techniques as well as mechanical and rheological essays were used to characterize the transparent and flexible films produced. Upon the application of a stimulus (moisture), the bending/unbending response times were measured. The use of NCC allowed obtaining films with response times in the order of 6 seconds for the bending and 5 seconds for the unbending, improving the results previously reported. These promising results open new horizons for building up improved soft steam engines.

Analysis of temporal and spatial variations of forest. A case of study in notheastern Armenia

The forest has a crucial ecological role and the continuous forest loss can cause colossal effects on the environment. As Armenia is one of the low forest covered countries in the world, this problem is more critical. Continuous forest disturbances mainly caused by illegal logging started from the early 1990s had a huge damage on the forest ecosystem by decreasing the forest productivity and making more areas vulnerable to erosion. Another aspect of the Armenian forest is the lack of continuous monitoring and absence of accurate estimation of the level of cuts in some years. In order to have insight about the forest and the disturbances in the long period of time we used Landsat TM/ETM + images. Google Earth Engine JavaScript API was used, which is an online tool enabling the access and analysis of a great amount of satellite imagery. To overcome the data availability problem caused by the gap in the Landsat series in 1988- 1998, extensive cloud cover in the study area and the missing scan lines, we used pixel based compositing for the temporal window of leaf on vegetation (June-late September). Subsequently, pixel based linear regression analyses were performed. Vegetation indices derived from the 10 biannual composites for the years 1984-2014 were used for trend analysis. In order to derive the disturbances only in forests, forest cover layer was aggregated and the original composites were masked. It has been found, that around 23% of forests were disturbed during the study period.

Influência da humidade no comportamento mecânico de compósitos de madeira-plástico

As crescentes questões ambientais têm vindo a impor, entre outras, a necessidade da reciclagem dos desperdícios produzidos por diversos setores (agricultura, indústria e serviços). Nesta ótica têm vindo a surgir um conjunto alargado de produtos compósitos que incluem os compósitos de madeira-plástico (Wood Plastic Composites). Estes compósitos têm vindo a competir com os produtos de madeira em diversos nichos de mercado, sendo o maior deles os revestimentos de piso em ambiente exterior, vulgarmente designados de deckings. Estes compósitos são comercializados salientando as suas vantagens relativamente à madeira maciça, como seja maior durabilidade biológica e menor variabilidade de propriedades mecânicas e físicas. No final do ano 2013 e início de 2014, foram reportadas uma série de anomalias na aplicação de réguas de compósitos madeira-plástico, nomeadamente a diminuição do desempenho físico e mecânico destes materiais, quando sujeitos a períodos prolongados de humidificação. Embora, para a maioria dos casos reportados, estas anomalias se devam a condições deficientes de aplicação, a possibilidade de alteração de características à flexão, quando sujeitos a condições de uma aplicação exterior, ainda não se encontra bem estudada. Na presente dissertação são avaliados e apresentados os efeitos no comportamento à flexão de três tipos diferentes de réguas de compósito madeira-plástico, quando sujeitos a condições de humidade permanente ou cíclica. Para este efeito, foram conduzidos um conjunto de ensaios, nomeadamente, de flexão para determinação da pré-carga, de resistência à humidade e de variação dimensional e de módulo de elasticidade devido à imersão em água e a ambiente húmido. Posteriormente, os resultados obtidos foram sujeitos a uma verificação aos Estados Limite de Serviço. Os resultados revelaram reduzidas variações dimensionais (inchamento) e perdas significativas de módulo de elasticidade, apenas devido à exposição a elevados níveis de humidade, mostrando-se o caso de exposição prolongada a água líquida o mais gravoso. Relativamente aos Estados Limite de Serviço, sobretudo a longo prazo, os resultados mostraram-se bastante gravosos, nomeadamente para o material de menor qualidade.

Production and characterization of electrospun composite fibers: confinement of thermosensitive microgels

Materials engineering focuses on the assembly of materials´ properties to design new products with the best performance. By using sub-micrometer size materials in the production of composites, it is possible to obtain objects with properties that none of their compounds show individually. Once three-dimensional materials can be easily customized to obtain desired properties, much interest has been paid to nanostructured poly-mers in order to build biocompatible devices. Over the past years, the thermosensitive microgels have become more common in the framework of bio-materials with potential applicability in therapy and/or diagnostics. In addition, high aspect ratio biopolymers fibers have been produced using the cost-effective method called electrospinning. Taking advantage of both microgels and electrospun fibers, surfaces with enhanced functionalities can be obtained and, therefore employed in a wide range of applications. This dissertation reports on the confinement of stimuli-responsive microgels through the colloidal electro-spinning process. The process mainly depends on the composition, properties and patterning of the precur-sor materials within the polymer jet. Microgels as well as the electrospun non-woven mats were investigated to correlate the starting materials with the final morphology of the composite fibers. PNIPAAm and PNIPAAm/Chitosan thermosensitive microgels with different compositions were obtained via surfactant free emulsion polymerization (SFEP) and characterized in terms of chemical structure, morphology, thermal sta-bility, swelling properties and thermosensitivity. Finally, the colloidal electrospinning method was carried out from spinning solutions composed of the stable microgel dispersions (up to a concentration of about 35 wt. % microgels) and a polymer solution of PEO/water/ethanol mixture acting as fiber template solution. The confinement of microgels was confirmed by Scanning Electron Microscopy (SEM). The electrospinning process was statistically analysed providing the optimum set of parameters aimed to minimize the fiber diameter, which give rise to electrospun nanofibers of PNIPAAm microgels/PEO with a mean fiber diameter of 63 ± 25 nm.