Influence of the abrasive particles size in the micro-abrasion wear tests of TiAlSiN thin coatings

Ball rotating micro-abrasion tribometers are commonly used to carry out wear tests on thin hard coatings. In these tests, different kinds of abrasives were used, as alumina (Al2O3), silicon carbide (SiC) or diamond. In each kind of abrasive, several particle sizes can be used. Some studies were developed in order to evaluate the influence of the abrasive particle shape in the micro-abrasion process. Nevertheless, the particle size was not well correlated with the material removed amount and wear mechanisms. In this work, slurry of SiC abrasive in distilled water was used, with three different particles size. Initial surface topography was accessed by atomic force microscopy (AFM). Coating hardness measurements were performed with a micro-hardness tester. In order to evaluate the wear behaviour, a TiAlSiN thin hard film was used. The micro-abrasion tests were carried out with some different durations. The abrasive effect of the SiC particles was observed by scanning electron microscopy (SEM) both in the films (hard material) as in the substrate (soft material), after coating perforation. Wear grooves and removed material rate were compared and discussed.

Caracterização mecânica e análise da resistência à corrosão em diferentes solos, de aços inoxidáveis duplex

O aço inoxidável é um material de alta durabilidade e resistência, utilizado nos mais diversos setores comerciais. O conhecimento das suas características e propriedades é essencial para uma escolha mais seletiva e vantajosa. Pretende‐se com este trabalho, estudar as propriedades mecânicas, a resistência ao desgaste e o comportamento, em ambientes mais agressivos de três tipos de aços inoxidáveis duplex, produzidos pela OUTOKUMPU e comercialmente conhecidos pelas designações LDX 2101, SAF 2507 e o SAF 2205. Para tal efeito foram realizados ensaios de Dureza Vickers, antes e após dobragem; ensaios de tracção em duas diferentes situações: seguindo a norma NP EN 10002‐ 1:2006 e após a realização de alguns ciclos de carga e descarga; ensaio de Impacto à temperatura ambiente e após arrefecimento criogénico; ensaio de resistência à corrosão. Também foi feito o estudo de resistência ao desgaste com base na técnica de micro‐abrasão por esfera rotativa e o estudo metalográfico. Foi também objetivo deste trabalho, relacionar o uso dos referidos aços duplex e as consequências que esse uso tem para o meio ambiente, bem como o seu comportamento quando exposto a condições extremas. Para tal, foram colocadas amostras dos referidos aços, em dois tipos de solos com condições de humidade e acidez diferentes analisando o seu estado após imersão em solo com condições controladas durante 272 dias.

Cutting forces and wear analysis of Si3N4 diamond coated tools in high speed machining

Si3N4 tools were coated with a thin diamond film using a Hot-Filament Chemical Vapour Deposition (HFCVD) reactor, in order to machining a grey cast iron. Wear behaviour of these tools in high speed machining was the main subject of this work. Turning tests were performed with a combination of cutting speeds of 500, 700 and 900 m min−1, and feed rates of 0.1, 0.25 and 0.4 mm rot−1, remaining constant the depth of cut of 1 mm. In order to evaluate the tool behaviour during the turning tests, cutting forces were analyzed being verified a significant increase with feed rate. Diamond film removal occurred for the most severe set of cutting parameters. It was also observed the adhesion of iron and manganese from the workpiece to the tool. Tests were performed on a CNC lathe provided with a 3-axis dynamometer. Results were collected and registered by homemade software. Tool wear analysis was achieved by a Scanning Electron Microscope (SEM) provided with an X-ray Energy Dispersive Spectroscopy (EDS) system. Surface analysis was performed by a profilometer.

Friction and wear in thrust ball bearings lubricated with biodegradable greases

Thrust ball bearings lubricated with several different types of grease, including three biodegradable low-toxicity greases, were tested in a modified four-ball machine in order to evaluate the bearing friction torque. At the end of each test, grease samples were obtained and analysed through ferrography, allowing the quantification and evaluation of the bearing wear. In order to compare the grease performance in terms of friction and wear, a correlation between the grease characteristics (base oil, bleed oil, thickener structure, and rheological parameters) and the experimental results was established.