Nephrotoxicity of CCA-treated wood: a comparative study with As2O5 and CrO3 on mice

The purpose of this work was to assess the acute toxicity on male mice to a chromated copper arsenate (CCA) solution, a widespread wood preservative used in building industry until 2002. Animals were subcutaneously injected with CCA (7.2 mg/kg arsenic and 10.2 mg/kg chromium per body weight), CrO3 (10.2 mg/kg), As2O5 (7.2 mg/kg) and NaCl (0.9%) per se, during 48 h and 96 h, for histopathology, histochemistry, chromium and arsenic analysis. The results showed some histopathological changes within renal tubules lumen of CCA exposed animals (during 48 h, and 96 h), and CrO3 (for the period of 96 h). Furthermore, the renal levels of arsenic and chromium in treated animals were statistically more evident than controls. Although, the same contents of pentavalent arsenic and hexavalent chromium were injected into treated animals with CCA and with the prepared solutions of As2O5 and CrO3, a different distribution of the pattern of these compounds was observed in kidneys.

Toxicity of chromated copper arsenate: a study in mice

Chromated copper arsenate (CCA) was widespread used as a chemical wood preservative with application in the construction of playground equipment, fences, jetties, and naval. Environmental protection agency (EPA) had limited the use of CCA-treated wood on 2002, due to probable implications on both human and environmental health. Although this fact, several industries pursue the use of this product within their manufactories. In addition, the durability of this wood for 60 years, makes these treated products an hazard to the public health. In the present work, studies were explored exposing mice to CCA, during 14, 24, 48, and 96 h for the assessment of acute toxicity of CCA. Kidney and liver were removed, prepared for histology and for metalloid, and copper content evaluation by high resolution inductively coupled plasma mass spectroscopy. The histological results evidenced apparently normal structures for control animals and group exposed to As2O5. On the contrary, the renal sections of the animals treated with CCA revealed epithelium cells desquamation, hyaline, and granular casts in renal tubules lumen. Furthermore, high levels of arsenic were detected in the kidney of animals treated with CCA over 14 and 48 h, being significantly greater than controls. Although this approach underlines the potential hazard of CCA on some vital organs, further testing may be required to establish the impacts on other functions.

Mechanical properties of chemically modified portuguese pinewood

To turn wood into a construction material with enhanced properties, many methods of chemical modification have been developed in the last few decades. In this work, mechanical properties of pine wood were chemically modified, compared and evaluated. Maritime pine wood (Pinus pinaster) was modified with four chemical processes: 1,3-dimethylol-4,5- dihydroxyethyleneurea, N-methylol melamine formaldehyde, tetra-alkoxysilane and wax. The following mechanical properties were assessed experimentally: Modulus of elasticity measured statically, stiffness stabilization efficiency in different climates (30 and 87% of relative humidity), modulus of rupture, work maximum load, impact bending strength, compression, tensile and shear strength at indoor conditions (65% of relative humidity). In both types of active principle of modification, cell wall or lumen fill, no significant changes on the bending stiffness (modulus of elasticity) were found. In the remaining properties analysed significant changes in the modified wood-material took place compared to unmodified wood control: - Cell wall modification was the most effective method to achieve high stiffness stabilization efficiency (up to 60%) and also increased compression strength (up to 230%). However, modulus of rupture, tensile, shear and the impact bending strength were reduced by both resins, but in a varying extent, where the N-methylol melamine formaldehyde endured less reduction than 1,3-dimethylol-4,5-dihydroxyethyleneurea resin. In the latter, reduction up to 60% can take place. - In the lumen fill modification: tetra-alkoxysilane has no effect in the mechanical properties. Although, a slight increase in shear strength parallel to the grain was found. Wax specimens have shown a slight increase in bending strength, compression, tensile and shear strength as well as in the absorption energy capacity.