Structural modification of TiO2 nanorod films with an influence on the photovoltaic efficiency of a dye-sensitized solar cell (DSSC).

TiO2 nanorod films have been deposited on ITO substrates by dc reactive magnetron sputtering technique. The structures of these nanorod films were modified by the variation of the oxygen pressure during the sputtering process. Although all these TiO2 nanorod films deposited at different oxygen pressures show an anatase structure, the orientation of the nanorod films varies with the oxygen pressure. Only a very weak (101) diffraction peak can be observed for the TiO2 nanorod film prepared at low oxygen pressure. However, as the oxygen pressure is increased, the (220) diffraction peak appears and the intensity of this diffraction peak is increased with the oxygen pressure. The results of the SEM show that these TiO2 nanorods are perpendicular to the ITO substrate. At low oxygen pressure, these sputtered TiO2 nanorods stick together and have a dense structure. As the oxygen pressure is increased, these sputtered TiO2 nanorods get separated gradually and have a porous structure. The optical transmittance of these TiO2 nanorod films has been measured and then fitted by OJL model. The porosities of the TiO2 nanorod films have been calculated. The TiO2 nanorod film prepared at high oxygen pressure shows a high porosity. The dye-sensitized solar cells (DSSCs) have been assembled using these TiO2 nanorod films prepared at different oxygen pressures as photoelectrode. The optimum performance was achieved for the DSSC using the TiO2 nanorod film with the highest (220) diffraction peak and the highest porosity.

Permeable Reactive Barriers using nanoparticles to remediate nitrate pollution

Nitrat e (NO3 - ) i s per vasi ve i n t he bi ospher e[ 1, 2]. Cont emporar y agri cult ural pr acti ces are a mong t he maj or ant hr opogeni c sources of r eacti ve nitrogen speci es, wher e nitrat ei s t he most abundant of t hese [ 2]. Excessi ve a mount s of r eacti ve nitrogen i n soil s and gr oundwat er ar e creati ng si gnifi cant t hr eat s t o hu man healt h and saf et y [ 3] as well as a host of undesirabl e environment al i mpact s [ 2]; it i s curr ently consi der ed t he second most r el evant environment al i ssue, aft er car bon di oxide e mi ssi ons. Nowadays, a mong t he most r el evant and pr omi si ng appr oaches t o r educe nitrat e concentrati on i n wat er, na mel y gr oundwat er, ar e denitrifi cati on- based pr ocesses [ 4]. Per meabl e r eacti ve barri ers ( PRB) have been pr oven eff ecti ve i n r educi ng vari ous cont ami nant s i n copi ous a mount s, parti cul arl y i n shall ow gr oundwat er [ 5]. However t he possi bl e added eff ecti veness of usi ng nanoparti cl es i n t hese structur es t o obt ai n nitrogen gas from nitrat es requires f urt her i nvesti gati on.