CuxSnSx+1 (x = 2, 3) thin films grown by sulfurization of metallic precursors deposited by dc magnetron sputtering

We report the results of the growth of Cu-Sn-S ternary chalcogenide compounds by sulfurization of dc magnetron sputtered metallic precursors. Tetragonal Cu2SnS3 forms for a maximum sulfurization temperature of 350 ºC. Cubic Cu2SnS3 is obtained at sulfurization temperatures above 400 ºC. These results are supported by XRD analysis and Raman spectroscopy measurements. The latter analysis shows peaks at 336 cm-1, 351 cm-1 for tetragonal Cu2SnS3, and 303 cm-1, 355 cm-1 for cubic Cu2SnS3. Optical analysis shows that this phase change lowers the band gap from 1.35 eV to 0.98 eV. At higher sulfurization temperatures increased loss of Sn is expected in the sulphide form. As a consequence, higher Cu content ternary compounds like Cu3SnS4 grow. In these conditions, XRD and Raman analysis only detected orthorhombic (Pmn21) phase (petrukite). This compound has Raman peaks at 318 cm-1, 348 cm-1 and 295 cm-1. For a sulfurization temperature of 450 ºC the samples present a multi-phase structure mainly composed by cubic Cu2SnS3 and orthorhombic (Pmn21) Cu3SnS4. For higher temperatures, the samples are single phase and constituted by orthorhombic (Pmn21) Cu3SnS4. Transmittance and reflectance measurements were used to estimate a band gap of 1.60 eV. For comparison we also include the results for Cu2ZnSnS4 obtained using similar growth conditions.

Influence of selenization pressure on the growth of Cu2ZnSnSe4 films from stacked metallic layers

Cu2ZnSnSe4 (CZTSe) is a p-type semiconductor with a high absorption coefficient, 104 to 105 cm-1, and is being seen as a possible replacement for Cu(In,Ga)Se2 in thin film solar cells. Yet, there are some fundamental properties of CZTSe that are not well known, one of them is its band gap. In order to resolve its correct value it is necessary to improve the growth conditions to ensure that single phase crystalline thin films are obtained. One of the problems encountered when growing CZTSe is the loss of Sn through evaporation of SnSe. Stoichiometric films are then difficult to obtain and usually there are other phases present. One possible way to overcome this problem is to increase the pressure of growth of CZTSe. This can be done by introducing an atmosphere of an inert gas like Ar or N2. In this work we report the results of morphological, structural and optical studies of the properties of CZTSe thin films grown by selenization of DC magnetron sputtered metallic layers under different Ar pressures. The films are analysed by SEM/EDS, Raman scattering and XRD.