Adhesion and wear behaviour of NCD coatings on Si3N4 by micro-abrasion tests

Nanocrystalline diamond (NCD) coatings offer an excellent alternative for tribological applications, preserving most of the intrinsic mechanical properties of polycrystalline CVD diamond and adding to it an extreme surface smoothness. Silicon nitride (Si3N4) ceramics are reported to guarantee high adhesion levels to CVD microcrystalline diamond coatings, but the NCD adhesion to Si3N4 is not yet well established. Micro-abrasion tests are appropriate for evaluating the abrasive wear resistance of a given surface, but they also provide information on thin film/substrate interfacial resistance, i.e., film adhesion. In this study, a comparison is made between the behaviour of NCD films deposited by hot-filament chemical vapour deposition (HFCVD) and microwave plasma assisted chemical vapour deposition (MPCVD) techniques. Silicon nitride (Si3N4) ceramic discs were selected as substrates. The NCD depositions by HFCVD and MPCVD were carried out using H2–CH4 and H2–CH4–N2 gas mixtures, respectively. An adequate set of growth parameters was chosen for each CVD technique, resulting in NCD films having a final thickness of 5 m. A micro-abrasion tribometer was used, with 3 m diamond grit as the abrasive slurry element. Experiments were carried out at a constant rotational speed (80 r.p.m.) and by varying the applied load in the range of 0.25–0.75 N. The wear rate for MPCVD NCD (3.7±0.8 × 10−5 m3N−1m−1) is compatible with those reported for microcrystalline CVD diamond. The HFCVD films displayed poorer adhesion to the Si3N4 ceramic substrates than the MPCVD ones. However, the HFCVD films show better wear resistance as a result of their higher crystallinity according to the UV Raman data, despite evidencing premature adhesion failure.

Determinação de germânio em alimentos por espectrometria de massa ligada a um plasma acoplada indutivamente (ICP-MS)

Nos dias de hoje existe uma grande preocupação da população em fazer uma alimentação mais saudável, uma alimentação que tenha nos seus alimentos elementos que não prejudiquem a saúde mas sim que a tornem mais forte. Um desses elementos que pode trazer benefício para a saúde é o Germânio, elemento de estudo no presente trabalho. Neste trabalho determinou-se a concentração de Germânio em alguns alimentos. Os alimentos usados foram: espargos, ginseng, cogumelos, rabanete, gengibre, aloé vera e alho. Para se fazer a decomposição das amostras foi usada uma solução de ácido nítrico concentrado (67%) e peróxido de hidrogénio (30%), de seguida as soluções resultantes foram analisadas por espectrometria de massa ligado a um plasma acoplado indutivamente (Inductive Coupled Plasma - Mass Spectrometry (ICP-MS)). Esta técnica permitiu estudar os três isótopos mais abundantes de germânio (Ge70, Ge72 e Ge74). Como principais resultados deste trabalho pode-se referir que o alimento que apresenta uma maior concentração de Germânio é o ginseng (243,0 ng/g), seguindo-se o alho (152,6 ng/g). Com concentrações bastante próximas ficaram os espargos, gengibre e cogumelos com um valor aproximado de 75 ng/g. As concentrações mais baixas formam encontradas no aloé vera e rabanete, com valores de 38,16 e 21,85ng/g respectivamente. Com estes resultados podemos concluir que para ter uma alimentação rica neste elemento deve-se ingerir ginseng e alho pois dos alimentos estudados são os mais ricos em Germânio.

Self-mated tribological systems based on multilayer micro/nanocrystalline CVD diamond coatings

The tribological response of multilayer micro/nanocrystalline diamond coatings grown by the hot filament CVD technique is investigated. These multigrade systems were tailored to comprise a starting microcrystalline diamond (MCD) layer with high adhesion to a silicon nitride (Si3N4) ceramic substrate, and a top nanocrystalline diamond (NCD) layer with reduced surface roughness. Tribological tests were carried out with a reciprocating sliding configuration without lubrication. Such composite coatings exhibit a superior critical load before delamination (130–200 N), when compared to the mono- (60–100 N) and bilayer coatings (110 N), considering ∼10 µm thick films. Regarding the friction behaviour, a short-lived initial high friction coefficient was followed by low friction regimes (friction coefficients between 0.02 and 0.09) as a result of the polished surfaces tailored by the tribological solicitation. Very mild to mild wear regimes (wear coefficient values between 4.1×10−8 and 7.7×10−7 mm3 N−1 m−1) governed the wear performance of the self-mated multilayer coatings when subjected to high-load short-term tests (60–200 N; 2 h; 86 m) and medium-load endurance tests (60 N; 16 h; 691 m).

Wear resistance of TiAlSiN thin coatings

In the last decades TiAlN coatings deposited by PVD techniques have been extensively investigated but, nowadays, their potential development for tribological applications is relatively low. However, new coatings are emerging based on them, trying to improve wear behavior. TiAlSiN thin coatings are now investigated, analyzing if Si introduction increases the wear resistance of PVD films. Attending to the application, several wear test configurations has been recently used by some researchers. In this work, TiAlSiN thin coatings were produced by PVD Unbalanced Magnetron Sputtering technique and they were conveniently characterized using Scanning Electron Microscopy (SEM) provided with Energy Dispersive Spectroscopy (EDS), Atomic Force Microscopy (AFM), Electron Probe Micro-Analyzer (EPMA), Micro Hardness (MH) and Scratch Test Analysis. Properties as morphology, thickness, roughness, chemical composition and structure, hardness and film adhesion to the substrate were investigated. Concerning to wear characterization, two very different ways were chosen: micro-abrasion with ball-on-flat configuration and industrial non-standardized tests based on samples inserted in a feed channel of a selected plastic injection mould working with 30% (wt.) glass fiber reinforced polypropylene. TiAlSiN coatings with a small amount of about 5% (wt.) Si showed a similar wear behavior when compared with TiAlN reported performances, denoting that Si addition does not improve the wear performance of the TiAlN coatings in these wear test conditions.

Influence of the abrasive particles size in the micro-abrasion wear tests of TiAlSiN thin coatings

Ball rotating micro-abrasion tribometers are commonly used to carry out wear tests on thin hard coatings. In these tests, different kinds of abrasives were used, as alumina (Al2O3), silicon carbide (SiC) or diamond. In each kind of abrasive, several particle sizes can be used. Some studies were developed in order to evaluate the influence of the abrasive particle shape in the micro-abrasion process. Nevertheless, the particle size was not well correlated with the material removed amount and wear mechanisms. In this work, slurry of SiC abrasive in distilled water was used, with three different particles size. Initial surface topography was accessed by atomic force microscopy (AFM). Coating hardness measurements were performed with a micro-hardness tester. In order to evaluate the wear behaviour, a TiAlSiN thin hard film was used. The micro-abrasion tests were carried out with some different durations. The abrasive effect of the SiC particles was observed by scanning electron microscopy (SEM) both in the films (hard material) as in the substrate (soft material), after coating perforation. Wear grooves and removed material rate were compared and discussed.

Micro-abrasion wear behaviour of TiAlCrSiN nanostructured coatings

The injection process of glass fibres reinforced plastics promotes the moulds surface degradation by erosion. In order to improve its wear resistance, several kinds of PVD thin hard coatings were used. It is well-known that nanostructures present a better compromise between hardness and toughness. Indeed, when the coating is constituted by a large number of ultra-thin different layers, cracks and interface troubles tend to decrease. However, it is not clear that these nanostructures present a better wear behaviour in erosion processes. In order to study its wear behaviour, a sputtered PVD nanostructured TiAlCrSiN coating was used. The substrate and film surfaces topography were analyzed by profilometry and atomic force microscopy techniques. Film adhesion to the substrate was evaluated by scratch tests. The surface hardness was measured with a Vickers micro-hardness tester. The wear resistance was evaluated by micro-abrasion with a rotating ball tribometer tests. Slurry of SiC particles in distilled water was used in order to provoke the surface abrasion. Different duration tests were performed in order to analyze the wear evolution. After these tests, the wear mechanisms developed were analyzed by scanning electron microscopy. Wear craters were measured and the wear rate was calculated and discussed. With the same purpose, coated inserts were mounted in an injection mould working with a 30% glass fibres reinforced polypropylene. After 45 000 cycles no relevant wear was registered.

Comparação dos Perfis Lipídicos de Plasma de uma População da Região Norte

Os ácidos gordos desempenham um papel fisiológico importante como componentes indispensáveis na estrutura celular, bem como fontes de energia. Nas últimas décadas, tem havido um aumento notável do interesse público nos ácidos gordos polinsaturados ómegas 3 e 6 e no seu impacto sobre a saúde humana, especialmente em doenças metabólicas e cardiovasculares. Estes ácidos gordos específicos podem prevenir e/ou tratar várias patologias metabólicas, atuando nomeadamente como compostos anti-inflamatórios. A menopausa é um fator de risco para doença cardiovascular, a diminuição de estrogénio, que ocorre neste estado fisiológico, provoca disfunção endotelial e stresse oxidativo. Consequentemente há uma redução dos níveis de ácidos gordos polinsaturados ómegas 3, o que contribui para o aparecimento de aterosclerose e doença cardiovascular. Neste contexto, o objetivo deste estudo foi avaliar e caracterizar o perfil lipídico de ácidos gordos de uma amostra de mulheres pós-menopausa e com este, estudar as associações entre o perfil lipídico determinado e parâmetros metabólicos de risco (parâmetros clínicos e bioquímicos). Inicialmente, os ácidos gordos foram extraídos da matriz plasmática através da derivatização destes e a sua composição percentual no plasma foi determinada com recurso a cromatografia gasosa com deteção de ionização de chama. De seguida, através do software IBM SPSS Statistics 21, foram estabelecidas associações entre os parâmetros clínicos e bioquímicos e o perfil lipídico determinado. A população em estudo foi divida em dois grupos consoante o período de entrada na menopausa (há menos de 7 anos e há 7 anos ou mais). Não há conhecimento de estudos semelhantes ao apresentado, que relacionem todo o perfil de ácidos gordos com parâmetros metabólicos de risco considerando o estado menopausal. Os resultados obtidos mostram que o perfil lipídico influencia vários marcadores metabólicos / endócrinos com relevância clínica que devem ser explorados em futuros ensaios clínicos. Para as mulheres na menopausa há menos de 7 anos foram estabelecidas as seguintes relações: i) entre os ácidos gordos saturados e insaturados cis e os níveis de ALP; ii) entre os ácidos gordos mono e polinsaturados cis e os níveis de GGT, IL10 e estradiol; iii) entre os ácidos gordos polinsaturados trans e o IMC e os níveis de IL6; iv) entre os ómegas 3 e os níveis de IL10 e ácido úrico; v) entre os ómegas 6 e os níveis de estradiol, ALP e GGT; vi) entre os ómegas 9 e os níveis de estradiol e GGT; vi) entre os ácidos gordos de curta cadeia e os níveis de colesterol total, LDL, triglicerídeos e IL10; vii) entre os ácidos gordos saturados de cadeia longa e o ΣÁcido láurico, mirístico, palmítico e esteárico e os níveis de triglicerídeos, ALP e GGT; viii) os níveis de IL10 podem ser simultaneamente associados com os ácidos gordos de curta cadeia e os ómegas 3. Para as mulheres na menopausa há 7 anos ou mais foram estabelecidas relações: i) entre os ómegas 3 e o IMC e os níveis de triglicerídeos; ii) entre os ácidos gordos monoinsaturados cis e os ómegas 9 com os níveis de ALT. Relações independentes do estado menopausal também foram estabelecidas, nomeadamente: i) entre os ácidos gordos polinsaturados cis e ómegas 6 e os níveis de ALT, triglicerídeos e AST; ii) entre os níveis de ácidos gordos monoinsaturados cis e ómegas 9 e os níveis de AST e triglicerídeos. O perfil lipídico de ácidos gordos pode ser considerado um biomarcador para a condição de saúde da mulher na menopausa.