Self-mated tribological systems based on multilayer micro/nanocrystalline CVD diamond coatings

The tribological response of multilayer micro/nanocrystalline diamond coatings grown by the hot filament CVD technique is investigated. These multigrade systems were tailored to comprise a starting microcrystalline diamond (MCD) layer with high adhesion to a silicon nitride (Si3N4) ceramic substrate, and a top nanocrystalline diamond (NCD) layer with reduced surface roughness. Tribological tests were carried out with a reciprocating sliding configuration without lubrication. Such composite coatings exhibit a superior critical load before delamination (130–200 N), when compared to the mono- (60–100 N) and bilayer coatings (110 N), considering ∼10 µm thick films. Regarding the friction behaviour, a short-lived initial high friction coefficient was followed by low friction regimes (friction coefficients between 0.02 and 0.09) as a result of the polished surfaces tailored by the tribological solicitation. Very mild to mild wear regimes (wear coefficient values between 4.1×10−8 and 7.7×10−7 mm3 N−1 m−1) governed the wear performance of the self-mated multilayer coatings when subjected to high-load short-term tests (60–200 N; 2 h; 86 m) and medium-load endurance tests (60 N; 16 h; 691 m).

Produção de biodiesel por catálise heterogénea

Mestrado em Engenharia Química. Ramo optimização energética na indústria química.

Preparação de adsorventes mesoporosos para a adsorção de poluentes em águas

Mestrado Engenharia Química. Ramo Tecnologias de Protecção Ambiental

Adhesion and wear behaviour of NCD coatings on Si3N4 by micro-abrasion tests

Nanocrystalline diamond (NCD) coatings offer an excellent alternative for tribological applications, preserving most of the intrinsic mechanical properties of polycrystalline CVD diamond and adding to it an extreme surface smoothness. Silicon nitride (Si3N4) ceramics are reported to guarantee high adhesion levels to CVD microcrystalline diamond coatings, but the NCD adhesion to Si3N4 is not yet well established. Micro-abrasion tests are appropriate for evaluating the abrasive wear resistance of a given surface, but they also provide information on thin film/substrate interfacial resistance, i.e., film adhesion. In this study, a comparison is made between the behaviour of NCD films deposited by hot-filament chemical vapour deposition (HFCVD) and microwave plasma assisted chemical vapour deposition (MPCVD) techniques. Silicon nitride (Si3N4) ceramic discs were selected as substrates. The NCD depositions by HFCVD and MPCVD were carried out using H2–CH4 and H2–CH4–N2 gas mixtures, respectively. An adequate set of growth parameters was chosen for each CVD technique, resulting in NCD films having a final thickness of 5 m. A micro-abrasion tribometer was used, with 3 m diamond grit as the abrasive slurry element. Experiments were carried out at a constant rotational speed (80 r.p.m.) and by varying the applied load in the range of 0.25–0.75 N. The wear rate for MPCVD NCD (3.7±0.8 × 10−5 m3N−1m−1) is compatible with those reported for microcrystalline CVD diamond. The HFCVD films displayed poorer adhesion to the Si3N4 ceramic substrates than the MPCVD ones. However, the HFCVD films show better wear resistance as a result of their higher crystallinity according to the UV Raman data, despite evidencing premature adhesion failure.

Produção de biodiesel a partir de pastas de gordura e resíduo de glicerol

O principal objectivo deste trabalho consistiu na produção de biodiesel a partir de resíduos fornecidos pela Empresa SOCIPOLE, S.A. Esta, forneceu, pastas de gordura (depósito formado nos óleos usados), só aproveitadas pela empresa para a produção de sabões, e resíduo de glicerol proveniente da produção de biodiesel. Com as pastas de gordura, foi feito um estudo onde se variaram alguns parâmetros, tais como: o tipo de reactor, catalisador, temperatura, agitação, tempo de reacção, razão molar gordura:metanol e condições de secagem. O estudo mais pormenorizado foi efectuado com o NaOH, como catalisador. Foram feitos vários ensaios para os tempos de reacção de 30minutos, 1hora e 2horas, a 65ºC e razão molar gordura:metanol 1:6, tendo-se obtido respectivamente 86,7; 88,1 e 87,5% para o teor de ésteres. No caso da resina catiónica forte como catalisador, aparentemente não houve reacção ao fim de 12h, enquanto no ensaio que utilizou o ácido sulfúrico, o teor de ésteres foi de 82,6%, ao fim de 12h com razão molar gordura:metanol igual a 1:11. Quanto à produção de biodiesel a partir do resíduo de ácidos gordos resultante da purificação do resíduo de glicerol, foi feito um estudo preliminar usando diferentes catalisadores, uma resina catiónica forte, ácido sulfúrico e zircónia sulfatada. Este resíduo continha cerca de 60% de ácidos gordos e aproximadamente 39% de ésteres metílicos. Dos três catalisadores usados, o que permitiu obter maior teor de ésteres foi a zircónia sulfatada, tendo-se obtido 82,9% trabalhando a 60ºC durante 18horas com agitação de 230rpm e razão molar ácidos gordos:metanol de 1:12 . O ensaio em que se obteve menor percentagem de ésteres (56,4%) foi com resina catiónica. Com as duas matérias-primas obteve-se sempre um teor de ésteres, no produto final, abaixo dos 96,5% estabelecidos pela Norma Europeia EN 14103. Estes resultados reflectem provavelmente a composição complexa das matérias-primas. As pastas de gordura podem conter compostos não esterificáveis, solúveis no biodiesel, ou mais dificilmente esterificáveis nas condições operacionais usadas. Já o resíduo de ácidos gordos apresenta uma cor escura o que indica a existência de compostos corados, talvez polímeros. Portanto, para se tirar conclusões fundamentadas é necessário fazer análises mais completas das pastas de gordura e do resíduo de ácidos gordos, assim como ao biodiesel produzido de forma a identificar as possíveis contaminações existentes nos produtos com esta proveniência.