Microstructure, mechanical properties and chemical degradation of brazed AISI 316 stainless steel/alumina systems

The main aims of the present study are simultaneously to relate the brazing parameters with: (i) the correspondent interfacial microstructure, (ii) the resultant mechanical properties and (iii) the electrochemical degradation behaviour of AISI 316 stainless steel/alumina brazed joints. Filler metals on such as Ag–26.5Cu–3Ti and Ag–34.5Cu–1.5Ti were used to produce the joints. Three different brazing temperatures (850, 900 and 950 °C), keeping a constant holding time of 20 min, were tested. The objective was to understand the influence of the brazing temperature on the final microstructure and properties of the joints. The mechanical properties of the metal/ceramic (M/C) joints were assessed from bond strength tests carried out using a shear solicitation loading scheme. The fracture surfaces were studied both morphologically and structurally using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction analysis (XRD). The degradation behaviour of the M/C joints was assessed by means of electrochemical techniques. It was found that using a Ag–26.5Cu–3Ti brazing alloy and a brazing temperature of 850 °C, produces the best results in terms of bond strength, 234 ± 18 MPa. The mechanical properties obtained could be explained on the basis of the different compounds identified on the fracture surfaces by XRD. On the other hand, the use of the Ag–34.5Cu–1.5Ti brazing alloy and a brazing temperature of 850 °C produces the best results in terms of corrosion rates (lower corrosion current density), 0.76 ± 0.21 μA cm−2. Nevertheless, the joints produced at 850 °C using a Ag–26.5Cu–3Ti brazing alloy present the best compromise between mechanical properties and degradation behaviour, 234 ± 18 MPa and 1.26 ± 0.58 μA cm−2, respectively. The role of Ti diffusion is fundamental in terms of the final value achieved for the M/C bond strength. On the contrary, the Ag and Cu distribution along the brazed interface seem to play the most relevant role in the metal/ceramic joints electrochemical performance.

Complex evolution of a multi-particle system

This paper studies a discrete dynamical system of interacting particles that evolve by interacting among them. The computational model is an abstraction of the natural world, and real systems can range from the huge cosmological scale down to the scale of biological cell, or even molecules. Different conditions for the system evolution are tested. The emerging patterns are analysed by means of fractal dimension and entropy measures. It is observed that the population of particles evolves towards geometrical objects with a fractal nature. Moreover, the time signature of the entropy can be interpreted at the light of complex dynamical systems.

Dimensionamento de ligações aço-betão segundo a prEN1992-4:2013

O presente relatório documenta o estágio desenvolvido na empresa SE2P – Sociedade de Engenharia, Projeto e Planeamento Lda. no âmbito da unidade curricular de DIPRE (Dissertação/Projeto/ Estágio) do Mestrado em Engenharia Civil – Ramo de Estruturas do Instituto Superior de Engenharia do Porto. A frequência no estágio curricular teve como objetivo principal o desenvolvimento de uma ferramenta de cálculo que permitisse o dimensionamento de ligações aço-betão segundo a prEN1992-4:2013. O desenvolvimento desta ferramenta resulta da necessidade do dimensionamento de soluções leves, económicas e esteticamente agradáveis tendo em conta a uniformização da legislação existente em toda a União Europeia. Atualmente, os projetistas têm utilizado programas de cálculo automático desenvolvidos por fabricantes de sistemas de ancoragens, como é o caso do Profis Anchor da Hilti. Esses programas de cálculo têm como base de dados as Diretrizes de Aprovação Técnica Europeia, a ETAG001- anexo C para dimensionamento de ancoragens mecânicas em betão e o relatório técnico EOTA TR029 para o dimensionamento de ancoragens químicas, apresentando até métodos de cálculo simplificados para uma rápida resposta ao cliente. A publicação da prEN1992-4:2013 é um marco importante, pois há já algum tempo que a construção metálica e mista está regulamentada apresentando algumas falhas no que diz respeito às ligações aço-betão. Esta norma é o culminar de anos de pesquisas, estudos e testes efetuados aos diferentes tipos de ligação tendo em conta além dos modos de rotura possíveis, os princípios de transferência de esforços.