CuxSnSx+1 (x = 2, 3) thin films grown by sulfurization of metallic precursors deposited by dc magnetron sputtering

We report the results of the growth of Cu-Sn-S ternary chalcogenide compounds by sulfurization of dc magnetron sputtered metallic precursors. Tetragonal Cu2SnS3 forms for a maximum sulfurization temperature of 350 ºC. Cubic Cu2SnS3 is obtained at sulfurization temperatures above 400 ºC. These results are supported by XRD analysis and Raman spectroscopy measurements. The latter analysis shows peaks at 336 cm-1, 351 cm-1 for tetragonal Cu2SnS3, and 303 cm-1, 355 cm-1 for cubic Cu2SnS3. Optical analysis shows that this phase change lowers the band gap from 1.35 eV to 0.98 eV. At higher sulfurization temperatures increased loss of Sn is expected in the sulphide form. As a consequence, higher Cu content ternary compounds like Cu3SnS4 grow. In these conditions, XRD and Raman analysis only detected orthorhombic (Pmn21) phase (petrukite). This compound has Raman peaks at 318 cm-1, 348 cm-1 and 295 cm-1. For a sulfurization temperature of 450 ºC the samples present a multi-phase structure mainly composed by cubic Cu2SnS3 and orthorhombic (Pmn21) Cu3SnS4. For higher temperatures, the samples are single phase and constituted by orthorhombic (Pmn21) Cu3SnS4. Transmittance and reflectance measurements were used to estimate a band gap of 1.60 eV. For comparison we also include the results for Cu2ZnSnS4 obtained using similar growth conditions.

Detection of ZnS phases in CZTS thin-films by EXAFS

Copper zinc tin sulfide (CZTS) is a promising Earthabundant thin-film solar cell material; it has an appropriate band gap of ~1.45 eV and a high absorption coefficient. The most efficient CZTS cells tend to be slightly Zn-rich and Cu-poor. However, growing Zn-rich CZTS films can sometimes result in phase decomposition of CZTS into ZnS and Cu2SnS3, which is generally deleterious to solar cell performance. Cubic ZnS is difficult to detect by XRD, due to a similar diffraction pattern. We hypothesize that synchrotron-based extended X-ray absorption fine structure (EXAFS), which is sensitive to local chemical environment, may be able to determine the quantity of ZnS phase in CZTS films by detecting differences in the second-nearest neighbor shell of the Zn atoms. Films of varying stoichiometries, from Zn-rich to Cu-rich (Zn-poor) were examined using the EXAFS technique. Differences in the spectra as a function of Cu/Zn ratio are detected. Linear combination analysis suggests increasing ZnS signal as the CZTS films become more Zn-rich. We demonstrate that the sensitive technique of EXAFS could be used to quantify the amount of ZnS present and provide a guide to crystal growth of highly phase pure films.

Properties of tantalum oxynitride thin films produced by magnetron sputtering: the influence of processing parameters

The main purpose of this work is to present and to interpret the change of structure and physical properties of tantalum oxynitride (TaNxOy) thin films, produced by dc reactive magnetron sputtering, by varying the processing parameters. A set of TaNxOy films was prepared by varying the reactive gases flow rate, using a N2/O2 gas mixture with a concentration ratio of 17:3. The different films, obtained by this process, exhibited significant differences. The obtained composition and the interpretation of X-ray diffraction results, shows that, depending on the partial pressure of the reactive gases, the films are: essentially dark grey metallic, when the atomic ratio (N + O)/Ta < 0.1, evidencing a tetragonal β-Ta structure; grey-brownish, when 0.1 < (N + O)/Ta < 1, exhibiting a face-centred cubic (fcc) TaN-like structure; and transparent oxide-type, when (N + O)/Ta > 1, evidencing the existence of Ta2O5, but with an amorphous structure. These transparent films exhibit refractive indexes, in the visible region, always higher than 2.0. The wear resistance of the films is relatively good. The best behaviour was obtained for the films with (N + O)/Ta ≈ 0.5 and (N + O)/Ta ≈ 1.3.

Dimensionamento de lajes aligeiradas betonadas "in situ"

A conjuntura económica da construção não se encontra numa fase de prosperidade, existindo a necessidade de criar soluções construtivas que permitam a redução de custos dos materiais a nível de obra. As lajes de betão armado, devido à sua grande área de implantação, possuem uma parcela importante no orçamento final de qualquer obra de edifícios correntes. Sabendo das possibilidades de aligeiramento de lajes, torna-se necessária a realização de um estudo pormenorizado e comparativo entre soluções de aligeiramento. O desenvolvimento deste relatório reflete todo o trabalho efetuado durante a realização de um estágio curricular desenvolvido na empresa FercaNorte – Estruturas, Lajes e Cofragens, Lda. e foca-se num dimensionamento e estudo comparativo de soluções de lajes fungiformes aligeiradas, aplicadas a dois casos de estudo e também num dimensionamento e estudo comparativo de soluções de lajes aligeiradas unidirecionais mas apenas aplicadas a um caso de estudo. No primeiro caso de estudo, laje fungiforme com um vão de 6 metros nas duas direções, são dimensionadas e comparadas quatro soluções: laje fungiforme maciça; laje fungiforme aligeirada com blocos elipsoides perdidos dispostos de forma ortogonal e envolvidos totalmente por betão; laje fungiforme aligeirada com blocos elipsoides perdidos dispostos em formato de favo de mel e envolvidos totalmente por betão; e laje fungiforme nervurada com moldes recuperáveis. No segundo caso de estudo, laje fungiforme com um vão de 7,04 metros nas duas direções, são dimensionadas e comparadas cinco soluções: laje fungiforme maciça, laje fungiforme aligeirada com blocos cúbicos perdidos dispostos de forma ortogonal e envolvidos totalmente por betão; laje fungiforme aligeirada, com blocos elipsoides perdidos dispostos de forma ortogonal e envolvidos totalmente por betão; laje fungiforme aligeirada com blocos elipsoides perdidos dispostos em formato de favo de mel e envolvidos totalmente por betão; e laje fungiforme nervurada com moldes recuperáveis. No terceiro caso de estudo, laje unidirecional com um vão de 8 metros apoiada em vigas com vão de 5 metros, são dimensionadas e comparadas três soluções: laje maciça; laje aligeirada com perfis tubulares com secção transversal reta oval; e laje nervurada com moldes recuperáveis. No final é apresentada uma estimativa orçamental para cada solução analisada nos três casos de estudo abordados.