Growth and Raman scattering characterization of Cu2ZnSnS4 thin films

In the present work we report the results of the growth, morphological and structural characterization of Cu2ZnSnS4 (CZTS) thin films prepared by sulfurization of DC magnetron sputtered Cu/Zn/Sn precursor layers. The adjustment of the thicknesses and the properties of the precursors were used to control the final composition of the films. Its properties were studied by SEM/EDS, XRD and Raman scattering. The influence of the sulfurization temperature on the morphology, composition and structure of the films has been studied. With the presented method we have been able to prepare CZTS thin films with the kesterite structure.

Growth pressure dependence of Cu2ZnSnSe4 properties

In this work, we show a set of growth conditions, for the two step process, with which the growth of CZTSe is successful and reproducible. The properties of the best CTZSe thin films grown by this method were examined by SEM/EDS, XRD, Raman scattering, AFM/EFM, transmittance and reflectance measurements, photoluminescence (PL) measurements and hot point probe. A broad emission band was observed in the photoluminescence spectrum of the CZTSe thin film. The band gap energy was estimated to be around 1.05 eV at room temperature, using the transmittance and reflectance data, and CZTSe samples show p-type conductivity with the hot point probe. The different characterization techniques show that we could grow single phase CZTSe thin films with our optimized process conditions.

Effect of selenization conditions on the growth and properties of Cu2ZnSn(S,Se)4 thin films

The opto-electronic properties of copper zinc tin sulfide can be tuned to achieve better cell efficiencies by controlled incorporation of selenium. In this paper we report the growth of Cu2ZnSn(S,Se)4 (CZTSSe) using a hybrid process involving the sequential evaporation of Zn and sputtering of the sulfide precursors of Cu and Sn, followed by a selenization step. Two approaches for selenization were followed, one using a tubular furnace and the other using a rapid thermal processor. The effects of annealing conditions on the morphological and structural properties of the films were investigated. Scanning electron microscopy and energy dispersive spectroscopy were employed to investigate the morphology and composition of the films. Structural analyses were done using X-ray diffraction (XRD) and Raman spectroscopy. Structural analyses revealed the formation of CZTSSe. This study shows that regardless of the selenization method a temperature above 450 °C is required for conversion of precursors to a compact CZTSSe layer. XRD and Raman analysis suggests that the films selenized in the tubular furnace are selenium rich whereas the samples selenized in the rapid thermal processor have higher sulfur content.