Microstructure, mechanical properties and chemical degradation of brazed AISI 316 stainless steel/alumina systems

The main aims of the present study are simultaneously to relate the brazing parameters with: (i) the correspondent interfacial microstructure, (ii) the resultant mechanical properties and (iii) the electrochemical degradation behaviour of AISI 316 stainless steel/alumina brazed joints. Filler metals on such as Ag–26.5Cu–3Ti and Ag–34.5Cu–1.5Ti were used to produce the joints. Three different brazing temperatures (850, 900 and 950 °C), keeping a constant holding time of 20 min, were tested. The objective was to understand the influence of the brazing temperature on the final microstructure and properties of the joints. The mechanical properties of the metal/ceramic (M/C) joints were assessed from bond strength tests carried out using a shear solicitation loading scheme. The fracture surfaces were studied both morphologically and structurally using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction analysis (XRD). The degradation behaviour of the M/C joints was assessed by means of electrochemical techniques. It was found that using a Ag–26.5Cu–3Ti brazing alloy and a brazing temperature of 850 °C, produces the best results in terms of bond strength, 234 ± 18 MPa. The mechanical properties obtained could be explained on the basis of the different compounds identified on the fracture surfaces by XRD. On the other hand, the use of the Ag–34.5Cu–1.5Ti brazing alloy and a brazing temperature of 850 °C produces the best results in terms of corrosion rates (lower corrosion current density), 0.76 ± 0.21 μA cm−2. Nevertheless, the joints produced at 850 °C using a Ag–26.5Cu–3Ti brazing alloy present the best compromise between mechanical properties and degradation behaviour, 234 ± 18 MPa and 1.26 ± 0.58 μA cm−2, respectively. The role of Ti diffusion is fundamental in terms of the final value achieved for the M/C bond strength. On the contrary, the Ag and Cu distribution along the brazed interface seem to play the most relevant role in the metal/ceramic joints electrochemical performance.

Estudo de esmalte estufa aquoso definitivo

Mestrado em Engenharia Química

Biomimetic sensors of molecularly-imprinted polymers for chlorpromazine determination

A new man-tailored biomimetic sensor for Chlorpromazine host-guest interactions and potentiometric transduction is presented. The artificial host was imprinted within methacrylic acid, 2-vinyl pyridine and 2-acrylamido-2-methyl-1-propanesulfonic acid based polymers. Molecularly imprinted particles were dispersed in 2-nitrophenyloctyl ether and entrapped in a poly(vinyl chloride) matrix. Slopes and detection limits ranged 51–67 mV/decade and 0.46–3.9 μg/mL, respectively, in steady state conditions. Sensors were independent fromthe pHof test solutionswithin 2.0–5.5.Good selectivitywas observed towards oxytetracycline, doxytetracycline, ciprofloxacin, enrofloxacin, nalidixic acid, sulfadiazine, trimethoprim, glycine, hydroxylamine, cysteine and creatinine. Analytical features in flowing media were evaluated on a double-channel manifold, with a carrier solution of 5.0×10−2 mol/L phosphate buffer. Near-Nernstian response was observed over the concentration range 1.0×10−4 to 1.0×10−2 mol/L. Average slopes were about 48 mV/decade. The sensors were successfully applied to field monitoring of CPZ in fish samples, offering the advantages of simplicity, accuracy, automation feasibility and applicability to complex samples.

Desenvolvimento de uma ferramenta para cálculo de estruturas em material compósito

Os desafios à engenharia moderna são cada vez maiores, pretendendo-se quase sempre obter estruturas mais leves, com propriedades mecânicas atrativas e muitas vezes com geometrias complexas. Com tais requisitos, um dos materiais que tem vindo a ter uma crescente aplicação é o material compósito. Contudo, no que toca ao cálculo estrutural destes materiais, tudo se torna mais complexo, já que são materiais que geralmente são formados por empilhamento de várias camadas de material heterogéneo, podendo estas encontrarem-se dispostas segundo diferentes orientações. Assim, a utilização de um software que permita a previsão das propriedades mecânicas de uma estrutura em material compósito através da micromecânica, a aplicação da Teoria Clássica dos Laminados e de um critério de rotura, como por exemplo o de Tsai-Hill, é fundamental para agilizar o processo de estudo da estrutura a fabricar. Para dar uma resposta a tal necessidade foi desenvolvida uma aplicação, em MATLAB® GUI, denominada CAFE – Composite Analysis For Engineers, com ambiente gráfico apelativo, que permite determinar todas as variáveis importantes no estudo de estruturas em material compósito. Esta aplicação visa suportar e agilizar a aprendizagem desta área do conhecimento, permitindo também o acesso ao código de cálculo por parte do utilizador, de modo a conhecerem-se as equações utilizadas e, eventualmente, ser alvo de futuros desenvolvimentos. O programa desenvolvido foi alvo de validação, recorrendo-se para tal, a uma comparação dos resultados obtidos entre o respetivo programa e por um outro programa de grande fiabilidade. Assim sendo, concluiu-se que o software CAFE apresenta resultados válidos, encontrando-se apto a ser utilizado.