Microstructure, mechanical properties and chemical degradation of brazed AISI 316 stainless steel/alumina systems

The main aims of the present study are simultaneously to relate the brazing parameters with: (i) the correspondent interfacial microstructure, (ii) the resultant mechanical properties and (iii) the electrochemical degradation behaviour of AISI 316 stainless steel/alumina brazed joints. Filler metals on such as Ag–26.5Cu–3Ti and Ag–34.5Cu–1.5Ti were used to produce the joints. Three different brazing temperatures (850, 900 and 950 °C), keeping a constant holding time of 20 min, were tested. The objective was to understand the influence of the brazing temperature on the final microstructure and properties of the joints. The mechanical properties of the metal/ceramic (M/C) joints were assessed from bond strength tests carried out using a shear solicitation loading scheme. The fracture surfaces were studied both morphologically and structurally using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction analysis (XRD). The degradation behaviour of the M/C joints was assessed by means of electrochemical techniques. It was found that using a Ag–26.5Cu–3Ti brazing alloy and a brazing temperature of 850 °C, produces the best results in terms of bond strength, 234 ± 18 MPa. The mechanical properties obtained could be explained on the basis of the different compounds identified on the fracture surfaces by XRD. On the other hand, the use of the Ag–34.5Cu–1.5Ti brazing alloy and a brazing temperature of 850 °C produces the best results in terms of corrosion rates (lower corrosion current density), 0.76 ± 0.21 μA cm−2. Nevertheless, the joints produced at 850 °C using a Ag–26.5Cu–3Ti brazing alloy present the best compromise between mechanical properties and degradation behaviour, 234 ± 18 MPa and 1.26 ± 0.58 μA cm−2, respectively. The role of Ti diffusion is fundamental in terms of the final value achieved for the M/C bond strength. On the contrary, the Ag and Cu distribution along the brazed interface seem to play the most relevant role in the metal/ceramic joints electrochemical performance.

Study on the changes of soil chemical characteristics as result of prescribed fire

Every year, particularly during the summer period, the Portuguese forests are devastated by forest fire that destroys their ecosystems. So in order to prevent these forest fires, public and private authorities frequently use methods for the reduction of combustible mass as the prescribed fire and the mechanical vegetation pruning. All of these methods of prevention of forest fires alter the vegetation layer and/or soil [1-2]. This work aimed the study of the variation of some chemical characteristics of soil that suffered prescribed fire. The studied an area was located in the Serra of Cabreira (Figure 1) with 54.6 ha. Twenty sampling points were randomly selected and samples were collected with a shovel before, just after the prescribed fire, and 125 and 196 days after that event. The parameters that were studied were: pH, soil moisture, organic matter and iron, magnesium and potassium total concentration. All the analysis followed International Standard Methodologies. This work allowed to conclude that: a) after the prescribed fire; i) the pH remained practically equal to the the initial value; ii) occurred a slight increase of the average of the organic matter contents and iron total contents; b) at the end of the sampling period compared to the initial values; i) the pH didn´t change significantly; ii) the average of the contents of organic matter decreased; and iii) the average of the total contents of Fe, Mg and K increased.