Assessment of the potential of tin sulphide thin films prepared by sulphurization of metallic precursors as cell absorbers

In this work, SnxSy thin films have been grown on soda-lime glass substrates by sulphurization of metallic precursors in a nitrogen plus sulphur vapour atmosphere. Different sulphurization temperatures were tested, ranging from 300 °C to 520 °C. The resulting phases were structurally investigated by X-Ray Diffraction and Raman spectroscopy. Composition was studied using Energy Dispersive Spectroscopy being then correlated with the sulphurization temperature. Optical measurements were performed to obtain transmittance and reflectance spectra, from which the energy band gaps, were estimated. The values obtained were 1.17 eV for the indirect transition and for the direct transition the values varied from 1.26 eV to 1.57 eV. Electrical characterization using Hot Point Probe showed that all samples were p-type semiconductors. Solar cells were built using the structure: SLG/Mo/SnxSy/CdS/ZnO:Ga and the best result for solar cell efficiency was 0.17%.

Minimização de odores em contentores de resíduos sólidos

Mestrado em Engenharia Química

Influence of the pre-treatments on the properties of biodegradable films from bovine hair

The replacement of conventional synthetic films and coatings by biodegradable alternatives reduces the use of non-renewable resources and waste disposal problems. Considering that Portugal is a major producer of leather, and consequently a large producer of related wastes, in this research, bovine hair was tested for the production of biodegradable films directly by thermo-compression, allowing waste valorisation and reduction of environmental pollution. The aim of this study was to determine the influence of the different pre-treatments performed by two processes (removal by mechanical action and removal by chemical process), applied to bovine hair, in order to obtain a biodegradable film with appropriate properties. Mechanical properties for these films were evaluated, namely strain at break, stress at break and Young modulus. Additionally colour, solubility and swelling in water were also studied. The mechanical removal hair only produced films with Na2S treatment. Chemical removed hair (immunization) depends of the pre-treatment and the degreasing with petroleum ether or sodium sulphide pre-treatment leads better mechanical properties. The results obtained indicated that the pre-treatments have an important role in the final properties of biodegradable films.

Desenvolvimento de processo de depilação de pele caprina sem destruição do pêlo e avaliação do seu impacto ambiental

O meio ambiente é uma grande preocupação mundial existindo cada vez mais imposições legais no sentido de o proteger. Torna-se assim necessário que as indústrias adoptem e desenvolvam processos alternativos mais limpos. A indústria de curtumes transforma a pele animal em couro, material resistente à putrefacção e com estabilidade térmica suficiente para ser manufacturado nas indústrias do calçado, estofos, vestuário e marroquinaria. A transformação referida é efectuada através duma série de processos entre os quais o caleiro, processo que visa depilar a pele e promover o relaxamento da estrutura fibrilar, tem um papel importante. O processo de caleiro produz um efluente bastante poluente. Tendo em conta esse facto, este trabalho teve como objectivo desenvolver processos de depilação de pele caprina sem destruição do pêlo, com vista à redução da quantidade de sulfureto e sulfidrato de sódio utilizada e da carga poluente do efluente. Além disso, o processo permite a recuperação do pêlo e este pode ser reaproveitado como fertilizante orgânico, hidrolisado de queratina, compostagem, etc. Todo o trabalho foi realizado tomando por base um processo de caleiro padrão utilizado industrialmente, alterando-o de forma a obter um processo de caleiro óptimo de depilação sem destruição do pêlo com e sem utilização de enzimas. Numa primeira fase, desenvolveu-se um processo de depilação sem destruição do pêlo normalmente utilizado para a pele de bovino que foi adaptado com resultados positivos, designado de processo sem enzimas. Numa segunda fase, desenvolveu-se um processo enzimático em que se utilizou uma protease (Erhavit DMC), uma lipase (Defat 50) e uma amilase (Mayzme SD-L); este processo deu bons resultados tal como o anterior. A redução da quantidade de sulfureto de sódio foi de 33% e 53% para o processo sem enzimas e processo com enzimas, respectivamente, em relação ao processo padrão. O efeito dos processos na carga poluente, à escala piloto, comprova uma redução de 37% nos SST, 37% nos SDT, 60% na CQO, 9% no S2- e 73% no Azoto para o processo sem enzimas e uma redução de 93% nos SST, 63% nos SDT, 69% na CQO, 69% no S2- e 83% no Azoto para o processo com enzimas, quando comparados com o processo padrão. . Uma análise de custos, com incidência apenas nos agentes químicos utilizados, permitiu concluir a existência de uma redução de custos anuais de 30% para o processo com enzimas e de 13% para o processo sem enzimas, quando comparados com o processo padrão. Como conclusão, os processos desenvolvidos apresentam um grande potencial para serem explorados industrialmente.

Construction and evaluation of cysteine selective electrodes for FIA analysis of pharmaceuticals

A flow injection analysis (FIA) system comprising a cysteine selective electrode as detection system was developed for determination of this amino acid in pharmaceuticals. Several electrodes were constructed for this purpose, having PVC membranes with different ionic exchangers and mediator solvents. Better working characteristics were attained with membranes comprising o-nitrophenyl octyl ether as mediator solvent and a tetraphenylborate based ionic-sensor. Injection of 500 µL standard solutions into an ionic strength adjuster carrier (3x10-3 M) of barium chloride flowing at 2.4mL min-1, showed linearity ranges from 5.0x10-5 to 5.0x10-3 M, with slopes of 76.4±0.6mV decade-1 and R2>0.9935. Slope decreased significantly under the requirement of a pH adjustment, selected at 4.5. Interference of several compounds (sodium, potassium, magnesium, barium, glucose, fructose, and sucrose) was estimated by potentiometric selectivity coefficients and considered negligible. Analysis of real samples were performed and considered accurate, with a relative error to an independent method of +2.7%.

Molecularly-imprinted materials for potentiometric transduction: application to the antibiotic enrofloxacin

Enrofloxacin (ENR) is an antimicrobial used both in humans and in food producing species. Its control is required in farmed species and their surroundings in order to reduce the prevalence of antibiotic resistant bacteria. Thus, a new biomimetic sensor enrofloxacin is presented. An artificial host was imprinted in specific polymers. These were dispersed in 2-nitrophenyloctyl ether and entrapped in a poly(vinyl chloride) matrix. The potentiometric sensors exhibited a near-Nernstian response. Slopes expressing mVΔlog([ENR]/M) varied within 48–63. The detection limits ranged from 0.28 to 1.01 µg mL 1. Sensors were independent from the pH of test solutions within 4–7. Good selectivity was observed toward potassium, calcium, barium, magnesium, glycine, ascorbic acid, creatinine, norfloxacin, ciprofloxacin, and tetracycline. In flowing media, the biomimetic sensors presented good reproducibility (RSD of ±0.7%), fast response, good sensitivity (47 mV/Dlog([ENR]/ M), wide linear range (1.0×10-5–1.0×10-3 M), low detection limit (0.9 µg mL-1), and a stable baseline for a 5×10-2 M acetate buffer (pH 4.7) carrier. The sensors were used to analyze fish samples. The method offered the advantages of simplicity, accuracy, and automation feasibility. The sensing membrane may contribute to the development of small devices allowing in vivo measurements of enrofloxacin or parent-drugs.

CuxSnSx+1 (x = 2, 3) thin films grown by sulfurization of metallic precursors deposited by dc magnetron sputtering

We report the results of the growth of Cu-Sn-S ternary chalcogenide compounds by sulfurization of dc magnetron sputtered metallic precursors. Tetragonal Cu2SnS3 forms for a maximum sulfurization temperature of 350 ºC. Cubic Cu2SnS3 is obtained at sulfurization temperatures above 400 ºC. These results are supported by XRD analysis and Raman spectroscopy measurements. The latter analysis shows peaks at 336 cm-1, 351 cm-1 for tetragonal Cu2SnS3, and 303 cm-1, 355 cm-1 for cubic Cu2SnS3. Optical analysis shows that this phase change lowers the band gap from 1.35 eV to 0.98 eV. At higher sulfurization temperatures increased loss of Sn is expected in the sulphide form. As a consequence, higher Cu content ternary compounds like Cu3SnS4 grow. In these conditions, XRD and Raman analysis only detected orthorhombic (Pmn21) phase (petrukite). This compound has Raman peaks at 318 cm-1, 348 cm-1 and 295 cm-1. For a sulfurization temperature of 450 ºC the samples present a multi-phase structure mainly composed by cubic Cu2SnS3 and orthorhombic (Pmn21) Cu3SnS4. For higher temperatures, the samples are single phase and constituted by orthorhombic (Pmn21) Cu3SnS4. Transmittance and reflectance measurements were used to estimate a band gap of 1.60 eV. For comparison we also include the results for Cu2ZnSnS4 obtained using similar growth conditions.

Molecularly-Imprinted Materials for Potentiometric Transduction: Application to the Antibiotic Enrofloxacin

Enrofloxacin (ENR) is an antimicrobial used both in humans and in food producing species. Its control is required in farmed species and their surroundings in order to reduce the prevalence of antibiotic resistant bacteria. Thus, a new biomimetic sensor enrofloxacin is presented. An artificial host was imprinted in specific polymers. These were dispersed in 2-nitrophenyloctyl ether and entrapped in a poly(vinyl chloride) matrix. The potentiometric sensors exhibited a near-Nernstian response. Slopes expressing mV/Δlog([ENR]/M) varied within 48–63. The detection limits ranged from 0.28 to 1.01 µg mL−1. Sensors were independent from the pH of test solutions within 4–7. Good selectivity was observed toward potassium, calcium, barium, magnesium, glycine, ascorbic acid, creatinine, norfloxacin, ciprofloxacin, and tetracycline. In flowing media, the biomimetic sensors presented good reproducibility (RSD of ± 0.7%), fast response, good sensitivity (47 mV/Δlog([ENR]/M), wide linear range (1.0 × 10−5–1.0 × 10−3 M), low detection limit (0.9 µg mL−1), and a stable baseline for a 5 × 10−2 M acetate buffer (pH 4.7) carrier. The sensors were used to analyze fish samples. The method offered the advantages of simplicity, accuracy, and automation feasibility. The sensing membrane may contribute to the development of small devices allowing in vivo measurements of enrofloxacin or parent-drugs.

Minimização do impacto ambiental do processo de curtume de pele de bovino

O presente trabalho teve como objectivo a minimização do impacto ambiental do processo de curtume da pele de bovino. A indústria de curtumes transforma a pele, material putrescível, em couro, material nobre, termicamente estável e imputrescível. A transformação da pele em couro origina uma carga poluente apreciável quer quanto a efluentes líquidos quer quanto a resíduos sólidos. O fluxo produtivo da indústria de curtumes pode dividir-se em quatro sectores: ribeira, curtume, tinturaria e acabamento, sendo que os três primeiros geram efluentes líquidos com elevada carga poluente. Neste trabalho, foram avaliadas as fases do processo que geram efluentes líquidos: molho, caleiro, curtume e tinturaria. Na avaliação do processo do molho testou-se uma protease e uma lipase contra um molhante e um desengordurante tradicional, agentes químicos normalmente utilizados no molho mas menos biodegradáveis que as enzimas testadas. Salienta-se o bom resultado obtido quanto à eficiência do molho Na avaliação do processo de caleiro testaram-se várias alternativas no sentido da redução da quantidade de sulfureto de sódio utilizada e da minimização da carga poluente. Entre as alternativas, depilação por oxidação, depilação enzimática com e sem destruição do pêlo, elegeu-se a depilação enzimática sem destruição do pêlo que conduziu a resultados com menor impacto ambiental, nomeadamente a redução da % da quantidade de sulfureto de sódio, sendo a redução da carga poluente de 4,19 % de sulfureto, 32.80% de sólidos suspensos totais (SST),27.09% de sólidos totais (ST) e de 76.90% da carência química de oxigénio (CQO) no efluente de caleiro. No processo do curtume da pele é utilizado crómio como agente de curtume em cerca de 80% das peles tratadas, sendo este metal problemático em termos ambientais. No sentido de reduzir a quantidade de crómio utilizada no processo foi realizado um planeamento factorial onde as variáveis a estudar foram a concentração de crómio e a temperatura, tendo este como objectivo observar qual a quantidade mínima de crómio necessária para termos um produto final nas condições desejadas e gerando um menor impacto ambiental. Concluiu-se desenvolvendo um processo que mostra ser possível reduzir a quantidade de sal de crómio de 7% para 5%, além de ter um impacto ambiental claramente menos agressivo nos efluentes de curtume gerado. Este processo quando comparado com o processo tradicional permite a redução de 27% na CQO, 79% nos SST, 11% nos ST e 38% no teor de crómio Na avaliação do processo de tinturaria foi estudado um processo compacto contra o processo tradicional, tendo-se concluído pelo menor impacto ambiental do processo estudado, nomeadamente ao nível da redução do consumo de água e da carga poluente gerada. A comparação dos dois processos, no que respeita à carga poluente gerada, permitiu concluir por uma redução de 39% da CQO, 50% dos SST, e 12% dos ST quando aplicado o processo compacto Por fim foi feita uma avaliação do impacto ambiental do efluente global gerado pelos processos considerados com menor impacto ambiental contra o processo tradicional, normalmente aplicado na indústria. A aplicação do conjunto dos processos desenvolvidos, quando comparada com a aplicação do conjunto dos processos tradicionais, mostra uma redução de 1% no sulfureto, 40% na CQO, 60 % nos SST, 42 % no crómio e 11% nos ST, mostrando claramente que é possível reduzir a carga poluente da indústria de curtumes atuando no processo. Este trabalho mostrou a importância de atuar no processo para minimizar os custos de tratamento e mesmo de investimento dos efluentes da indústria de curtumes. Importa salientar que os processos desenvolvidos necessitam de validação a uma escala semi-industrial.