Structural modification of TiO2 nanorod films with an influence on the photovoltaic efficiency of a dye-sensitized solar cell (DSSC).

TiO2 nanorod films have been deposited on ITO substrates by dc reactive magnetron sputtering technique. The structures of these nanorod films were modified by the variation of the oxygen pressure during the sputtering process. Although all these TiO2 nanorod films deposited at different oxygen pressures show an anatase structure, the orientation of the nanorod films varies with the oxygen pressure. Only a very weak (101) diffraction peak can be observed for the TiO2 nanorod film prepared at low oxygen pressure. However, as the oxygen pressure is increased, the (220) diffraction peak appears and the intensity of this diffraction peak is increased with the oxygen pressure. The results of the SEM show that these TiO2 nanorods are perpendicular to the ITO substrate. At low oxygen pressure, these sputtered TiO2 nanorods stick together and have a dense structure. As the oxygen pressure is increased, these sputtered TiO2 nanorods get separated gradually and have a porous structure. The optical transmittance of these TiO2 nanorod films has been measured and then fitted by OJL model. The porosities of the TiO2 nanorod films have been calculated. The TiO2 nanorod film prepared at high oxygen pressure shows a high porosity. The dye-sensitized solar cells (DSSCs) have been assembled using these TiO2 nanorod films prepared at different oxygen pressures as photoelectrode. The optimum performance was achieved for the DSSC using the TiO2 nanorod film with the highest (220) diffraction peak and the highest porosity.

Inventories and concentration profiles of 137Cs in undisturbed soils in the northeast of Buenos Aires Province, Argentina

Inventories and vertical distribution of (137)Cs were determined in La Plata region undisturbed soils, Argentina. A mean inventory value of 891 ± 220 Bq/m(2) was established, which is compatible with the values expected from atmospheric weapon tests fallout. The study was complemented with pH, organic carbon fraction, texture and mineralogical soil analyses. Putting together Southern Hemisphere (137)Cs inventory data, it is possible to correlate these data with the mean annual precipitations. The large differences in (137)Cs concentration profiles were attributed to soil properties, especially the clay content and the pH values. A convection-dispersion model with irreversible retention was used to fit the activity concentration profiles. The obtained effective diffusion coefficient and effective convection velocity parameters values were in the range from 0.2 cm(2)/y to 0.4 cm(2)/y and from 0.23 cm/y to 0.43 cm/y, respectively. These data are in agreement with values reported in literature. In general, with the growth of clay content in the soil, there was an increase in the transfer rate from free to bound state. Finally, the highest transfer rate from free to bound state was obtained for soil pH value equal to 8.