Morphological and structural characterization of CrO2/Cr2O3 films grown by laser-CVD

This work reports on the synthesis of chromium (III, IV) oxides films by KrF laser-assisted CVD. Films were deposited onto sapphire substrates at room temperature by the photodissociation of Cr(CO)(6) in dynamic atmospheres containing oxygen and argon. A study of the processing parameters has shown that partial pressure ratio Of O-2 to Cr(CO)(6) and laser fluence are the prominent parameters that have to be accurately controlled in order to co-deposit both the crystalline oxide phases. Films consistent with such a two-phase system were synthesised for a laser fluence of 75 mJ cm(-2) and a partial pressure ratio of about 1. (c) 2005 Elsevier B.V. All rights reserved.

Influence of the Sodium/Proton replacement on the structural, morphological and photocatalytic properties of titanate nanotubes

Titanate nanotubes (TNT) with different sodium contents have been synthesised using a hydrothermal approach and a swift and highly controllable post-washing processes. The influence of the sodium/proton replacement on the structural and morphological characteristics of the prepared materials was analysed. Different optical behaviour was observed depending on the Na+/H+ samples’ content. A band gap energy of 3.27±0.03 eV was estimated for the material with higher sodium content while a value of 2.81±0.02 eV was inferred for the most protonated material, which therefore exhibits an absorption edge in the near visible region. The point of zero charge of the materials was determined and the influence of the sodium content on the adsorption of both cationic and anionic organic dyes was studied. The photocatalytic performance of the TNT samples was evaluated in the rhodamine 6G degradation process. Best photodegradation results were obtained when using the most protonated material as catalyst, although this material has shown the lowest R6G adsorption capability.

The insular shelves of the Faial-Pico Ridge (Azores archipelago): a morphological record of its evolution

Shelves surrounding reefless volcanic ocean islands are formed by surf erosion of their slopes during changing sea levels. Posterosional lava flows, if abundant, can cross the coastal cliffs and fill partially or completely the accommodation space left by erosion. In this study, multibeam bathymetry, high-resolution seismic reflection profiles, and sediment samples are used to characterize the morphology of the insular shelves adjacent to Pico Island. The data show offshore fresh lava flow morphologies, as well as an irregular basement beneath shelf sedimentary bodies and reduced shelf width adjacent to older volcanic edifices in Pico. These observations suggest that these shelves have been significantly filled by volcanic progradation and can thus be classified as rejuvenated. Despite the general volcanic infilling of the shelves around Pico, most of their edges are below the depth of the Last Glacial Maximum, revealing that at least parts of the island have subsided after the shelves formed by surf erosion. Prograding lava deltas reached the shelf edge in some areas triggering small slope failures, locally decreasing the shelf width and depth of their edges. These areas can represent a significant risk for the local population; hence, their identification can be useful for hazard assessment and contribute to wiser land use planning. Shelf and subaerial geomorphology, magnetic anomalies and crustal structure data of the two islands were also interpreted to reconstruct the long-term combined onshore and offshore evolution of the Faial-Pico ridge. The subaerial emergence of this ridge is apparently older than previously thought, i.e., before approximate to 850 ka.