Comportamento à fadiga de juntas soldadas de aços tipo 460M com fios fluxados

Trabalho Final de Mestrado para obtenção do grau de Mestre em Engenharia Mecânica

The effect of metal transfer stability (spattering) on fume generation, morphology and composition in short-circuit MAG welding

The main objective of this work was to evaluate the hypothesis that the greater transfer stability leads also to less volume of fumes. Using an Ar + 25%CO2 blend as shielding gas and maintaining constant the average current, wire feed speed and welding speed, bead-on-plate welds were carried out with plain carbon steel solid wire. The welding voltage was scanned to progressively vary the transfer stability. Using two conditions of low stability and one with high stability, fume generation was evaluated by means of the AWS F1.2:2006 standard. The influence of these conditions on fume morphology and composition was also verified. A condition with greater transfer stability does not generate less fume quantity, despite the fact that this condition produces fewer spatters. Other factors such as short-circuit current, arcing time, droplet diameters and arc length are the likely governing factors, but in an interrelated way. Metal transfer stability does not influence either the composition or the size/morphology of fume particulates. (c) 2014 Elsevier B.V. All rights reserved.

Effect of explosive mixture on quality of explosive welds of copper to aluminium

The aim of this research is to investigate the influence of explosive ratio and type of sensitizer on the quality of explosive welds between copper and aluminium alloy plates. The welds were performed on a partially overlapping joint configuration using an emulsion explosive (EE) with two different sensitizers, hollow glass microspheres (HGMS) and expanded polystyrene spheres (EPS). Welds with an improved surface were achieved by using the HGMS sensitizer. A higher wave amplitude was registered in welds produced with the EPS sensitizer. In turn, the dimension of the molten pockets was influenced by the explosive ratio, increasing in size with increases in the values of this parameter. The intermetallic content of these zones varied according to the sensitizer type. Unlike the CuAl2 phase, the Cu-richer phases CuAl and Cu9Al4 were only identified in welds performed using the EPS sensitizer. An increase in hardness was observed at the interface of all welds, which resulted from both the presence of intermetallic phases and the plastic deformation of the materials promoted by the impact. This effect was most evident on the aluminium alloy side. All the welds had a greater strength than copper, i.e. the weakest material of the joint. (C) 2016 Elsevier Ltd. All rights reserved.